A 45 wt% Pb-55 wt% Mg alloy is rapidly quenched to room temperature from an elevated temperature in such a way that the high- temperature microstructure is preserved. This microstructure is found to consist of the a phase and M82PB, having respective mass fractions of 0.65 and 0.35. Determine the approximate temperature from which the alloy was quenched. Use Animated Figure. °C

A 45 wt% Pb-55 wt% Mg alloy is rapidly quenched to room temperature from an elevated temperature in such a way that the high- temperature microstructure is preserved. This microstructure is found to consist of the a phase and M82PB, having respective mass fractions of 0.65 and 0.35. Determine the approximate temperature from which the alloy was quenched. Use Animated Figure. °C

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A 80%Ag-20%Cu alloy is slowly heated from room temperature (25°C).Determine (1) At what temperature does the first liquid phase form and what is this liquid’s composition?(2) At what temperature does all solid melt and what is the last remaining solid’s composition?
An alloy of 30 wt % Pb and 70 wt % Sn is slowly cooled from 250°C to 27°C: d) What is the amount and composition of each phase that is present at 183°C - ∆T ? e) What are the amounts of each phase present at room temperature? f) Draw the microstructure 183°C + ∆T and 183°C - ∆T in 2 cm diameter circle.
During a quenching process on a TTT diagram, we can transform pearlite into bainite. True or false?
IDENTIFY THE PHASE OF THE FOLLOWING USING THE PHASE DIAGRAM. Write your solutions. 1. 66kPa and 15C 2. 25kPa and -5C
. Using the isothermal transformation diagram for an iron-carbon alloy of eutectoid composition, specify the nature of the final composition in terms of microconstituents present and approximate percentages: a) Rapidly cool to 350 oC, hold for 104 s, and quench to room temperature. b) Rapidly cool to 250 oC, hold for 100 s, and quench to room temperature. c) Rapidly cool to 650 oC, hold for 20 s, rapidly cool to 400 oC, hold for 103 s, and quench to room temperature.
find the relative amounts (in terms of mass fractions) of the phases for the following alloys and temperature: 90 wt% Zn-10 wt% Cu at 400°C.
Is it possible to have a copper–zinc alloy that, at equilibrium, consists of an  phase of composition 75 wt% Zn– 25 wt% Cu, and also a liquid phase of composition 90 wt% Zn and 10 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why.
Phase Diagrams: You are given the lead tin (Pb-Sn) phase diagram. Below the eutectic isotherm is identified as the two phase region a + B. a) At 30wt % Sn, in the circles below draw the microscopic observations evolving at 3000C, 2250C, and 1000C for this hypoeutectic alloy. b) At a temperature just above the isotherm at 1830C, for the 30 wt% Sn Alloy, calculate the fractions of each phase present at equilibrium and the corresponding composition of each phase.
A 609 g eutectoid steel ( about 0.8%C) is heated to 1,002 C and cooled slowly through the eutectorid temperature. This results in the formation of cementite Fe3C (6.67%C) and ferrite (0.025%C). Calculate the number of grams of cementite that form in the steel.
Referring to Figure 1, answer the following: What are the liquidus and solidus temperatures for an 80%Pb20%Tl alloy? What is the composition of the solid solution phase for the aforementioned alloy once we hit the liquidus temperature upon cooling? For the same alloy above, use the inverse lever rule to calculate the %solid and %liquid at 325C
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
10.27 A hypothetical A-B alloy of composition 55 wt% B-45 wt% A at some temperature is found to consist of mass fractions of 0.5 for both a and 8 phases. If the composition of the B phase is 90 wt B-10 wt% A, what is the composition of the a phase?