An aluminum alloy cylinder with a diameter of 76 mm and a height of 150 mm. is subjected to a compressive load of 220 kN. Assume that the mate-rial is within the elastic region and a modulus of elasticity of 75 GPa. a. What will be the lateral strain if Poisson’s ratio is 0.33?b. What will be the diameter after load application?c. What will be the height after load application?

An aluminum alloy cylinder with a diameter of 76 mm and a height of 150 mm. is subjected to a compressive load of 220 kN. Assume that the mate-rial is within the elastic region and a modulus of elasticity of 75 GPa. a. What will be the lateral strain if Poisson’s ratio is 0.33?b. What will be the diameter after load application?c. What will be the height after load application?

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter14: Material Selection

Section: Chapter Questions

Problem 8ETSQ

See similar textbooks

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The dam were plotted on a load-displacement graph. P vs. L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/L =1392 kips/in. What is the modulus of elasticity?
An aluminum alloy rod has a circular cross section with a diameter of 8 mm. This rod is subjected to a tensile load of 4 kN. Assume that the material is within the elastic region and E = 69 GPa. a. What will be the lateral strain if Poisson’s ratio is 0.33? b. What will be the diameter after load application?
An aluminum alloy cylinder with a diameter of 76 mm and a height of150 mm. is subjected to a compressive load of 220 kN. Assume that the material is within the elastic region and a modulus of elasticity of 75 GPa.a. What will be the lateral strain if Poisson’s ratio is 0.33?b. What will be the diameter after load application?c. What will be the height after load application?
A 2-m long steel rod, 10-mm in diameter, is carrying a load of 20 kN. (a) what is the axial stress developed in the rod, in kN/m^2. Is the tensile or compressive? (b) compute the amount of elongation (in mm) in the steel rod caused by the applied load, (c) what will be the elongation (in mm) in the steel rod if the weight of the steel rod is included? Use density of the steel to be 7860 kg/m^3. Young's modulus of elasticity, E=200GPa. W=mg. Draw free body diagram of the steel rod.
A cylindrical specimen of stainless steel having an initial diameter of 12.8?? and initial length of 50.8?? is pulled in tension. Use the data provided below to a) Plot the data as engineering stress versus engineering strain using excel or similar software. b) Compute the modulus of elasticity. c) Determine the yield strength at a strain offset of 0.002. d) Determine the tensile strength of this alloy. e) What is the approximate ductility, in percent elongation? f) Compute the modulus of resilience. Load (?) Length (??) 0 50.800 12,700 50.825 25,400 50.851 38,100 50.876 50,800 50.902 76,200 50.952 89,100 51.003 92,700 51.054 102,500 51.181 107,800 51.308 119,400 51.562 128,300 51.816 149,700 52.832 159,000 53.848 160,400 54.356 159,500 54.864 151,500 55.880 124,700 56.642 Fracture