An aluminum pipe must not stretch more than 0.05in when it issubjected to a tensile load. Knowing that E=10.1x10^6psi and that the maximum allowable normal stress is 14ksi, determine (a) the maximum allowable length of the pipe, and (b) the required area of the pipe if the tensile load is 127.5kips.

An aluminum pipe must not stretch more than 0.05in when it issubjected to a tensile load. Knowing that E=10.1x10^6psi and that the maximum allowable normal stress is 14ksi, determine (a) the maximum allowable length of the pipe, and (b) the required area of the pipe if the tensile load is 127.5kips.

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 37CQ

See similar textbooks

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The dam were plotted on a load-displacement graph. P vs. L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/L =1392 kips/in. What is the modulus of elasticity?
The cross-sectional areas of a column are shown in the figure . Find the maximum allowable value of P (in N) for the column if the stress in the steel is 84.96 MPa , stress in the timber is 17.21 MPa , and stress in the concrete is 18.52 MPa. Round off the final answer to two decimal places.
Axial loads are applied to the compound rod that is composed of an aluminum segment rigidly connected between steel and bronze segments. P = 10 kN a. What is the stress (MPa) in the Bronze material? b. What is the stress in Aluminum in MPa? c. What is the stress in Steel in MPa?
Axial loads are applied to the compound rod that is composed of an aluminum segment rigidly connected between steel and bronze segments. P = 10 kN a. What is the stress (MPa) in the Bronze material? b. What is the stress in Aluminum in MPa? c. What is the stress in Steel in MPa?
Before the 400 – kN load is applied, the rigid platform rests on two steel bars, each of cross- sectional area 1400 mm2, as shown in the figure. The cross- sectional area of the aluminum bar is 2800 mm2. Compute the stress in the aluminum bar after the 400- kN load is applied. Use E = 200 GPa for steel and E = 70 GPa for aluminum. Neglect the weight of the platform.
A load applied to a machine component results in the state of plane stress ?x=80 MPa, ?y=100 MPa, ?xy=60 MPa. The component is made of a brittle high-strength steel that follows the maximum normal stress criterion with ?u=200 MPa. If increasing the load increases each stress component proportionally, determine the percentage increase that can be applied before the component fails.
A cylindrical brass specimen having a diameter of 1.10 cm and initial gage length of 4.04 cm is subjected to tensile strength test. The load-deformation values are given in the below table. The final length and final diameter of the specimen were measured as 4.33 cm and 0.92 cm, respectively. Complete the below table and plot true stress-true strain diagram and determine. Yield strength at 0.2 % off-set method. Poisson’s ratio of the material at 135 kN load (assume that there is no volume change) If the material were unloaded from 175 kN, what would be its final length? 1 nm=1*10-9 m, 1 0A=10-10 m