Force P and length change AL data are given in table below for the initial portion of a tension test on 7075-T651 Al alloy. The diameter before testing was 9.07 mm., and the gage length Linitial for t length change measurement was 50.8 mm. Calculate corresponding values of engineering stress and strain, and display these values on a stress-strain plot. (use the region for drawing your plot in question sheet) P, kN AL mm 7.22 0.0839 14.34 0.1636 21.06 26.8 0.241 0.308 0.380 31.7 34.1 0.484 35.0 0.614 0.924 1.279 1.622 1.994 36.0 36.5 36.9 37.2

Force P and length change AL data are given in table below for the initial portion of a tension test on 7075-T651 Al alloy. The diameter before testing was 9.07 mm., and the gage length Linitial for t length change measurement was 50.8 mm. Calculate corresponding values of engineering stress and strain, and display these values on a stress-strain plot. (use the region for drawing your plot in question sheet) P, kN AL mm 7.22 0.0839 14.34 0.1636 21.06 26.8 0.241 0.308 0.380 31.7 34.1 0.484 35.0 0.614 0.924 1.279 1.622 1.994 36.0 36.5 36.9 37.2

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Calculate the axial deformation of a 1” round steel bar, 1 foot long of material, C1045, when it is subjected to a force of 60,000 axially. Modulus of elasticity = 30 x 10^6 psi. Note: All units are in SI, for your reference.
During stress-strain test, the unit deformation at a stress of 35 MPa was observed to be 167 x 10^-6 m/m and at a stress of 140 MPa it was 667 x 10^-6. If the proportional limit was 200 MPa, what is the modulus of Elasticity (GPa)? What is the strain corresponding to a stress of 80 MPa?
2. A tensile test is performed on a bar of Dural (an aluminium alloy) of diameter 15 mm. The bar yields under a load of 30 kN and reaches a maximum load of 46 kN. Estimate the tensile yield stress and tensile strength of Dural
For a number of points during a tension test on Man-Ten steel, engineering stress and strain data are given in Table. Also given are minimum diameters measured in the necked region in the latter portions of the test. The initial diameter was 6.32 mm. (a) Determine the Young’s modulus; (b) Determine the true stress and strain throughout; (c) Calculate the true plastic strain for the beyond yielding.
(Suppose you need to design a tension test machine capable of testing specimens that have nominal ultimate stresses as high as σu = 100 ksi . How much force must the machine be capable of generating? Assume the testing specimen has the ASTM shape shown. Answer for this is 19.6 kip) (If the maximum nominal strain is ϵf = 0.7 just before the test specimen fractures and the test machine operates by moving only one grip, how far must that grip be designed to travel? The total length of the deforming part of the specimen is 3 in. Answer for this is 2.10 in) Do not know if this info is needed but this was the other 2 parts
A material has the following properties, ultimate Sul = σul = 350mpa, the strain hardening exponent n=0.20. Determine the value for the strength coefficient K.
For a tensile test it can be shown that the percent cold work (%CW) is related to strain according to the following relationship: %CW=(εε+1) × 100 Using this equation, compute the percent cold work experienced by naval brass (for which the stress-strain behavior is shown in the Animated Figure 6.12) when a stress of 415 MPa (60190 psi) is applied.
With aid of diagram, describe a tensile experiment. Include the stress-strain curve
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
When an aluminum tensile sample with an initial diameter of 12.827 mm was tested, a maximum load of 66.72 kN was recorded at an engineering strain of 0.4 . What is the load on an identical tensile sample with an engineering strain of 0.2 ?
Briefly describe the metallographic procedure. Briefly explain the ASTM grain-size standard. Draw a stress-strain curve for a ductile metal and mention plastic region and 5 important parameters (or points) in your curve. Additionally, explain these parameters (if necessary provide the corresponding equations). Briefly describe the necessities of a compression test for some materials. Explain the reason that buckling happens during the compression test. Explain the Izod impact test. Explain the Brinell hardness test. Explain the creep test. Design and explain fatigue test setup for a crankshaft. Explain the salt spray test in corrosion tests
Draw a typical stress vs strain tensile test curve for the following materials (two seperate graphs) and label the axis. A ductile metallic test specimen that is stretched to failure displaying a characteristic yield point and show the following parts on the curve. 1- Yield point 2- Ultimate Tensile Strength 3- Breaking point 4- Elastic Region 5- Plastic Region 6- Necking region