Q2/ For a 97.5 wt% Fe-2.5 wt% C at atemperature 700 oC, determine the following:a) The Number and types of The Phases Present.b) The Amount of Phases Present in Grams That forms per 100 G.c) Draw The Microstructure Of Phases Present At This Point And What is The React called?16001538°C1493°CL140081394°CY+L1200y, Austenite1000Temperature (°C)912°C800aY6004000(Fe)0.760.022a, Ferrite12.141147°C4.30y + Fe Cرقم الصفحة 1/ 1727°Ca + Fe3C243Composition (wt% C)Iron- Carbon Phase DiagramsCementite (Fe3C)566.7

Answered: Image /qna-images/answer/d026147e-da36-4175-ad74-65134d8c2020.jpg

Q2/ For a 97.5 wt% Fe-2.5 wt% C at a temperature 700 oC, determine the following: a) The Number and types of The Phases Present. b) The Amount of Phases Present in Grams That forms per 100 G. c) Draw The Microstructure Of Phases Present At This Point And What is The React called?

Q2/ For a 97.5 wt% Fe-2.5 wt% C at a temperature 700 oC, determine the following: a) The Number and types of The Phases Present. b) The Amount of Phases Present in Grams That forms per 100 G. c) Draw The Microstructure Of Phases Present At This Point And What is The React called?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Using the Ti-Cu phase diagram, if you start with 100 kg of a Ti-Cu mixture at 3000C and 10 wt. % Cu and cool down very slowly to points A (1400 C), B (950 C), C (800 C), and D (500 C), determine what phases are present at each letter, determine the compositions for each phase, and determine the weight in each phase. Point A): Phase(s) present Weight % of Cu in each phaseWeight of each phase Point B): Phase(s) present Weight % of Cu in each phaseWeight of each phase Point C): Phase(s) present Weight % of Cu in each phaseWeight of each phase Point D): Phase(s) present Weight % of Cu in each phaseWeight of each phase
In a binary phase diagram ( pressure omitted) what is the maximum number of phases that can coexist for at least one degree of freedom?
Q1/ The figure below shows the phase equilibrium diagram for copper and silver Answer the following paragraphs? Conpostin a% 39 o = « & o Tepertue (F) @ Composttan (w5 ) 0 1- define pointe E? 2- define pointe B? 3- define the line AE? 4- define the line BG? 5- define the line FG?
In a binary Fe-Fe3C system, what is the transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the concentrations of the total and partial phases? Data: eutectoid temperature: 723 ºC, eutectoid concentration: 0.76% C, limit concentration of ferrite: 0.022%, limit concentration of cementite: 6.7%.
In a binary Fe-Fe3C system, what is a transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the total and partial phases? Given:Eutectoid temperature=723°C; Eutectoid concentration=0.76% C; Limit concentration of ferrite=0.022%; Limiting concentration of cementite: 6.7%.
Consider the temperature-composition phase diagram shown below, which represents a solid-liquid equilibrium based on a (liquid) mixture of A and B at high temperatures. A mixture with overall B composition of 0.57. What is the ratio of the amount of solid containing 0.67 B and 0.33 A to the amount of the eutectic mixture at the eutectic temperature?
Referring to Figure 1, please answer the following [NOTE: SHOW YOUR WORK on Figure 1]:a. provide the specific name for the phase boundary lines denoted by A and B. b. identify the phases present at equilibrium in the phase fields denoted by C, D, and E. c. identify the specific name for the point denoted by F. d. What is the maximum solid solubility of Mg in Al? At what temperature does it occur? e. An Al-Mg alloy (10 wt% Mg, 90 wt% Al) is heated slowly (to insure equilibrium) from a temperature of 200 C: i. At what temperature does the first liquid phase form? ii. What is the composition of the liquid phase at the temperature in part i.? iii. At what temperature does complete melting (no solid phase remaining) occur? iv. What is the composition of the last solid remaining prior to complete melting? f. Using the equilibrium phase diagram of Figure 1, identify the phases present, their compositions, and their relative mass fractions at equilibrium for a 70 wt% Mg – 30 wt% Al…
As a future engineer, give a sample situation where Duhem’s Theorem can be applied in the industry. Enumerate all possible variables that must be specified to fully determine the intensive and extensive states of the system. Also, enumerate possible changes that would affect the intensive and extensive coordinates. 1. Describe the system. What are the phases and components present in the system?2. What are the extensive and intensive variables to completely determine the equilibrium state of the system?
A) Identify all congruent reactions and their coordinates in the phase diagramB) Identify all invariant reactions (reaction type and coordinates) in the phase diagramC) Starting from a liquid at 70 at.% Ni and 1800 degrees C, cool the liquid slowly such that thermodynamic equilibrium is always maintained.C1) At what temperature does solid first appear?C2) Identify the solid phase which appears first from the liquid state and its approximate compositionC3) At what temperature does the liquid finally disappear?C4) What is the liquid composition when it finally disappearsC5) Identify the last solid phase which appears during cooling and the temperature at which this last solid phase appearsC6) At the point where the last solid phase appears during cooling, identify the phases present, give their compositions, and calculate their fractions
Using the Mg-Pb phase diagram below, if you start at point A and cool down very slowly to room temperature (point D), sketch the microstructure associated with each letter, determine what phases are present at each letter, determine the compositions for each phase, and determine the weight in each phase. The Mg-Pb mixture has 20 wt. % Pb in it. You start with 100 kg.
For the system KNO3-NaNO3-H2O, a ternary point exists at 5°C at which the twoanhydrous salts are in equilibrium with a saturated solution containing 9.04% KNO3 and41.01% NaNO. Determine analytically the maximum weight of KNO3 which can berecovered pure from a salt mixture containing 70 g of KNO3 and 30 g NaNO3 bycrystallization from an aqueous solution at 5°C. Draw the phase diagram and show your solution.
10.27 A hypothetical A-B alloy of composition 55 wt% B-45 wt% A at some temperature is found to consist of mass fractions of 0.5 for both a and 8 phases. If the composition of the B phase is 90 wt B-10 wt% A, what is the composition of the a phase?