The following data was obtained from a tensile test onLoad (kN)1632567295110132142140135Extension (mm)0.20.40.70.91.52.55.08.510.012.0a specimen of 10mm diameter and gauge length 60mm.Using the graph paper supplied, plot the load-extensiondiagram and determine:(1) The tensile strength(2) 0.1% Proof Stress(3) Young's Modulus for the specimen

Answered: Image /qna-images/answer/07ca3596-dddc-4ea7-8a79-e87f88570c00.jpg

The following data was obtained from a tensile te Load (kN) 16 32 56 72 95 110 132 14 Extension (mm) 0.2 0.4 0.7 0.9 1.5 2.5 5.0 8. a specimen of 10mm diameter and gauge length Using the graph paper supplied, plot the load-ex diagram and determine: (1) The tensile strength (2) 0.1% Proof Stress (3) Young's Modulus for the specimen cisa Jo lao

The following data was obtained from a tensile te Load (kN) 16 32 56 72 95 110 132 14 Extension (mm) 0.2 0.4 0.7 0.9 1.5 2.5 5.0 8. a specimen of 10mm diameter and gauge length Using the graph paper supplied, plot the load-ex diagram and determine: (1) The tensile strength (2) 0.1% Proof Stress (3) Young's Modulus for the specimen cisa Jo lao

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.3P: A tensile test was performed on a metal specimen having a circular cross section with a diameter 0....

See similar textbooks

Similar questions

A tensile force of 20 kN is applied to a specimen with a gage length of 50mm. It isthen noted that the distance between the gage marks became 50.122mm. a,) What isthe modulus of elasticity of the specimen if its diameter is 10mm? b.) What is the axialstress of the specimen? Solution must have Free Body Diagram/drawing.
A tension test is being conducted on a steel-rod specimen with a gauge length of L0=50mm and initial diameter of d0=13mm. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 510 MPa , e = 693 MPa , g = 565 MPa , and ℎ = 0.15 mm/mm Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 65.0 mm.
Tension specimens (diameter d0 0.500 in., gage length L0 2.00 in.) made of structural materials A and B are tested to failure in tension. (a) At failure the distances between the gage marks are LAf 2.90 in. and LBf 2.22 in.; the corresponding diameters at the failure cross sections are dAf 0.263 in. and dBf 0.471 in., respectively. Determine the percent elongation in 2 in. and the percent reduction in area for these two materials, and classify each material as either brittle or ductile. (b) From these tensile tests the following data are also obtained: EA 10.0 103 ksi, (Y)A 5 ksi, (U)A 13 ksi; EB 10.4 103 ksi, (Y)B 73 ksi, (U)B 83 ksi. From the data given here, make rough sketches (to scale) of the stress-strain diagrams of materials A and B.
A water tank is 8 meters in diameter and 12 meters high. Ifthe tank is to be completely filled, determine the minimumthickness of the tank plating if the stress is limited to40 MPa.
Consider a metal bar 12.5 mm in diameter and 50 mm in length that is tested under uniaxial tension. The test results data are as follows: Force (kN) Final length (mm) Final diameter (mm) 122 56,14 12,19 120 62,05 11,60 114 68,57 11,03 (a) Complete the following table: Force (kN) Final length (mm) Final diameter (mm) True stress (MPa) True deformation (mm/mm) 122 56,14 12,19 120 62,05 11,60 114 68,57 11,03 (b) Determine the metal's work hardening coefficient. (c) The most likely crystal structure for this metal is?
A tension test is being conducted on a steel-rod specimen with a gauge length of L0=2 in and initial diameter of d0=0.5 in. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 74.0 ksi, e = 104.0 ksi , g = 85.0 ksi , and h = 0.15 in/in. Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 2.7 in . Assuming that the stress is constant over the cross-sectional area and if the tension force used is P = 11.0 kips, find the nominal stress experienced by the rod. Determine the force P needed to reach the ultimate stress in the steel-rod specimen.
a) A tension test was carried out for a specimen having 610 mm in length and an average diameter of 12.80 mm. The test was conducted until the specimen failed. The data record from a tensile test for the specimen is given in Table 1. A 50 mm gauge length was marked on the specimen before load applied.Referring to the data in Table 1;i) Plot a stress-strain diagram by using a scale of 1:0.02 mm/mm for the x-axis and 1:40 MPa for the y-axis. Redraw the elastic region by using a strain scale of 1:0.004 min/mm.ii) Determine the approximate modulus of elasticity, ultimate stress, and the yield strength of this material at 0.20% offset.iii) Calculate the modulus of toughness.iv) Calculate the final length of the specimen, if the specimen elongated about 26.78%.v) Calculate the percentage of reduction of area and the final diameter at breakage, if the cross-section area decreases to 105.13 mm2
Describe about the strain-controlled test.
Consider a bar with a rectangular cross-section area with a thickness of t = 0.5 in. and height of h = 3.5 in. When force P = 19 kips is applied to the bar, the strain gages attached to the surface of the bar reads εx = 740 µε along the direction of the force and εy = -170 µε in the perpendicular direction. Determine Poisson's ratio for this specimen? Determine the modulus of elasticity for this specimen?in Ksi
During a tensile test on a specimen the following results were obtained: Load (kN) 15 30 40 50 55 60 65 Extension (mm) 0.05 0.094 0.127 0.157 1.778 2.79 3.81 Load (kN) 70 75 80 82 80 70 Extension (mm) 5.08 7.62 12.7 16.0 19.05 22.9 Diameter of gauge length - 19 mm Gauge length = 100 mm Diameter at fracture = 16.49 mm Gauge length at fracture = 121 mm Plot the complete load extension graph and the straight line portion to an enlarged scale. Hence determine: (a) the modulus of elasticity; (d) the nominal stress at fracture; (b) the percentage elongation; (e) the actual stress at fracture; (c) the percentage reduction in area; (f) the tensile strength. !116 GN/m2; 21%; 24.7%; 247 MN/m2; 328 MN/m2; 289 MN/m2.] 1.10 Figure 1.24 shows a special spanner used to tighten screwed components. A torque is applied at the tommybar and is transmitted to the pins which engage into holes located into the end of a screwed component. (a) Using the data given in Fig. 1.24 calculate: (i) the diameter D of…
In a simple tensile test using a cylindrical test specimen (Dia.=10mm), the applied force was 120 kN and the extension was 2%. Find the modulus of elasticity of that specimen. If the standard modulus of elasticity is 200 GPa, is this material accepted or not? and why?
A tensile force of 20 kN is applied to a specimen with a gage length of 50mm. It is then noted that the distance between the gage marks became 50.122mm. a,) What is the modulus of elasticity of the specimen if its diameter is 10mm? b.) What is the axial stress of the specimen?Note: Please show detailed solutions with illustrations.