A bar of 30 cm diameter is subjected to a pull of 200 kN. The measured extension on gauge length of 3.50 m is 5 cm and change in diameter is 2 mm. Calculate: (i) Young's Modulus, (ii) Poisson's Ratio (iii) Bulk Modulus and (iv) Shear Modulus.

Q: 10. The following results were obtained in a tensile test on a mild steel specimen of original…

A:

Q: ows that the shear modulus of an aluminum specimen is 4.6 x 106psi. When the same specimen is used…

A:

Q: Determine the changes in length,breadth,thickness of a steel which is 4m long ,30mm wide,20 mm thick…

A: Consider a force 'P' acting longitudinally on a bar having material properties Modulus of…

Q: 9) Define the rolling resistance. 10) Define the slip angle.

A: Rolling Resistance It is the resistance offered by the body when it rolls on the ground or it is…

Q: 1. A tensile test is carried out on a specimen of mild steel of gauge length 40 mm and diameter 7.42…

A: Given: To find various properties of metal using test data.

Q: A compound die will be used to blank and punch a large washer out of 6061ST aluminum alloy sheet…

A:

Q: Tensile test under 40,000 N load was applied to a low carbon steel with a sample diameter of 6 mm.…

A: load on carbon steelP=40000Ndiameter of steel rod d1=6mmdiameter of specimen under load decrease to…

Q: Calculate the axial stresses of Galvani pipe, σg.

A: Answer : Axial stress in galvanic pipe =13.53398058 KPa. (Tensile)  Axial stress in bronze pipe…

Q: How we can measure shear modulus?

A: The earth's material reaction to shear deformation is measured in shear modulus. The ratio of…

Q: When an aluminum tensile sample with an initial diameter of 12.827 mm was tested, a maximum load of…

A: Given Data ⇒ Maximum load(F1)=66.72 KN Engineering strainε1=0.4 Engineering strainε2=0.2

Q: If you have a Bulk Deformation Process in Metalworking with a product in the Rolling Process that…

A: Solution      Calculate the final width  Using volume consistency we can find the final width

Q: A direct extrusion process is used to reduce a cylindrical part that has a diameter of 5 inch and is…

A:

Q: 02: A steel specimen 12mm diameter has gauge length 50mm. the steel specimen had tested via tensile…

A: We are suppose to solve only 3 subparts. Please post other subparts as a separate question.

Q: A tensile test is performed on a metal specimen, and it is found that a true plastic strain of 0.20…

A:

Q: titanium bar 9.4mm in diameter with a gauge length of 50mm is pulled in tension to failure. After,…

A:

Q: A cylindrical specimen of 1018 steel having a diameter of 6.35 mm and a gauge length of 38.1 mm is…

A: The cross-sectional area of the specimen is The stress in the element can be determined as, The…

Q: Q2c) Listed in the table below is the tensile stress-strain data for different grades of steels.…

A: A) the material which will show highest elongation, will show the greatest percentage reduction in…

Q: 3. A dimension of 225.00 mm is specified for a particular injection moulded component manufactured…

A: Given data: d=225.00 mm Need to determine the mould cavity dimensions.

Q: 4. How we can measure shear modulus? 5. What is the difference between a single shear and double…

A:

Q: A force of 25,000 N will cause 1cm x 1cm bar of carbon steel to stretch from 20 cm to 20.040 cm.…

A:

Q: For Flexural Stress, when we should use the Ix or Iy? Explain, draw diagram if necessary. In…

A: The standard formula for bending or flexural stress in a beam is, σ=MyINA Here, M is the bending…

Q: 2/ Aluminum tensile specimen with 12.5mm diameter, a gauge length of 50.8mm and the final ameter was…

A:

Q: • In a sheet metal forming press the shape to be formed is hemispherical cup of radius 15 cm in 2mm…

A:

Q: Based on the plotted curve, calculate the average/tangent Young's modulus and Poisson's ratio for…

A: we have to evaluate  the poisson's ratio & youngs modulus

Q: Force P and length change AL data are given in table below for the initial portion of a tension test…

A: Given data :-  Diameter = 9.07 mm Gauge Length = 50.8 mm

Q: A cylindrical sample that is produced from a metal is tested under compression. The metal has a…

A: Given data: The Young's modulus of the metal is E = 150 GPa. The shear modulus of the metal is G =…

Q: 1. Based on data collected as Table 1, plot graph Stress vs strain, determine YS, TS and E. Table 1:…

A:

Q: The following figure demonstrates the pressure acquired form a direct extrusion process versus the…

A: Given: Extrusion process

Q: 3. Estimate the force required for a 90° bending of a St 50 steel of thickness of 1.5 mm in a V die,…

A: Given :-  Angle = 90°  Thickness = 1.5 mm  Die opening = 7× thickness Tensile strength = 500 mpa…

Q: Q2c) Listed in the table below is the tensile stress-strain data for different grades of steels.…

A: 1) the material which is most ductile, will have highest strain at fracture point and it will also…

Q: The following data were recorded during the tensile test of a test specimen with a diameter of 12.8…

A: The given data is that of a tensile test. Material : Aluminum Diameter of specimen  = Do = 12.8 mm…

Q: Calculate the yield strength, tensile strength, strain and Young’s Modulus of a cylindrical tensile…

A: for solution refer below images.

Q: 7) Chapter 3: Problem 3.15: (SI Units) The flow curve for austenitic stainless steel has the…

A:

Q: Diameter of gauge length =19mm , Gauge length =100 mm Diameter at fracture = 16.49 mm , Gauge length…

A: Load(KN) Extension(mm) 0 0 15 0.05 30 0.094 40 0.127 50 0.157 55 1.778 60 2.79 65…

Q: Question 5: The graph below gives a plot of force versus total sample length in a tensile test of a…

A: Given data: The initial length of the cylindrical sample is lo = 10 cm. The initial diameter of the…

Q: How we can measure shear modulus?

A: Shear modulus or modulus of rigidity can be found from the torsion test. As a result of the twisting…

Q: In a rolling mill, the rollers can exert a pressure of 219 MPa on the sheet being rolled. If the…

A: Given:-h1=2 mmh2=2×0.25=0.5 mmμ=0.35To find:-Diameter

Q: cylindrical specimen of brass that has a diameter of 20 mm, a tensile modulus of 110 GPa, and a…

A: Given Data D=20 mm E=110 GPa P=40000 N L=120 mm

Q: QUESTION The following data were obtained during a tension test of a low carbon steel specimen…

A:

Q: Force P and length change AL data are given in table below for the initial portion of a tension test…

A: Given Data Di=9.07 mmLi=50.8 mm Value for the stress-strain is shown in above table. Now, The yield…

Q: 02: A steel specimen 12mm diameter has gauge length 50mm. the steel specimen had tested via tensile…

A: we are suppose to solve only 3 subparts of a question. please post other parts and other question as…

Q: A theater rigging company uses a safety factor of 10 for all its ropes, which means that all…

A:

Q: Q19-Derive an expression for true strain as a function of D and Do for a tensile test specimen of…

A: as per our guidelines, i solved 1st question only

Q: A three point bend test is performed on a block of ZrO2 that is 8 in.long,0.50.in.wide,and 0.25…

A: Given Specimen length = 8 in  Specimen width = 0.50 in Specimen thick 0.25 in Distance = 4 in Force…

Q: Q9) Mention two functions of the wringing motion used in gauge blocks.

A: To find : 2 functions of wringing motion used in gauge blocks

Forming and Shaping

Metal forming is a category of metalworking process through which the material can be given the desired shape and size by subjecting it to plastic deformation, where the component undergoes bulk deformation process upon application of loads. Unlike the shearing and machining process, the material does not undergo up to a failure point as indicated in the stress-strain curve. Hence, the stresses induced during the forming process are greater than yield strength but less than the failure strength of the material. The process does not lead to the loss of material, so it can be said to be an economical process. During forming, the material is subjected to tensile forces, compressive forces, bending, and shearing loading conditions. The material should possess the property of ductility to undergo the forming process.