HOME WORKre-NoFor a Pb-30% Sn alloy, determine the phasespresent, their amounts, and their compositions400sim Shaeen Bat 300°C, 200°C, and 30°CL.300LiquidusSolidusLiquidusL+Ba+LSolidus2001918361.997.5Eutectic(E)n BaSolvusSolvus-تعللق ل لصف100a + Ba +EE+BPb20406080SnMetalurgy | Bassim Shaheen Bachy.Weight percent tinTemperature ("C)

For 300°C As from the given composition the region at 300°C and 30 % Sn in PB-SN alloy is pure…

For a Pb-30% Sn alloy, determine the phases present, their amounts, and their compositions 400 at 300°C, 200°C, and 30°C L. 300 Liquidus Solidus Liquidus L+B a+L Solidu 200 a 19 183 61.9 97.5 Eutectic Solvus Solvus- (E) 100 a+ B a +E E+B Pb 20 40 60 80 Sn Metailurgy | Bassim Shaheen Bachy. Weight percent tin Temperature (C)

For a Pb-30% Sn alloy, determine the phases present, their amounts, and their compositions 400 at 300°C, 200°C, and 30°C L. 300 Liquidus Solidus Liquidus L+B a+L Solidu 200 a 19 183 61.9 97.5 Eutectic Solvus Solvus- (E) 100 a+ B a +E E+B Pb 20 40 60 80 Sn Metailurgy | Bassim Shaheen Bachy. Weight percent tin Temperature (C)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

10.27 A hypothetical A-B alloy of composition 55 wt% B-45 wt% A at some temperature is found to consist of mass fractions of 0.5 for both a and 8 phases. If the composition of the B phase is 90 wt B-10 wt% A, what is the composition of the a phase?
A 80%Ag-20%Cu alloy is slowly heated from room temperature (25°C).Determine (1) At what temperature does the first liquid phase form and what is this liquid’s composition?(2) At what temperature does all solid melt and what is the last remaining solid’s composition?
Calculate the amounts and compositions of phases at 726oC in a Fe-0.6% C alloy cooled under equilibrium conditions. Disregard the amounts of proeutectoid phases. A. 77.3% α, 22.7% Fe3C; C in α = 6.7% and C in Fe3C = 0.02% B. 91.3% α, 8.7% Fe3C; C in α = 0.02% and C in Fe3C = 6.7% C. 77.3% α, 22.7% Fe3C; C in α = 0.02% and C in Fe3C = 6.7% D. 91.3% α, 8.7% Fe3C; C in α = 0.05% and C in Fe3C = 8.4% E. None of the mentioned
Q1/ The figure below shows the phase equilibrium diagram for copper and silver Answer the following paragraphs? Conpostin a% 39 o = « & o Tepertue (F) @ Composttan (w5 ) 0 1- define pointe E? 2- define pointe B? 3- define the line AE? 4- define the line BG? 5- define the line FG?
A hypothetical A-B alloy of composition 54 wt% B-46 wt% A at some temperature is found to consist of mass fractions of 0.5 for both αand β phases. If the composition of the β phase is 89 wt% B-11 wt% A, what is the composition of the α phase? ________ wt% B
An alloy of 30 wt % Pb and 70 wt % Sn is slowly cooled from 250°C to 27°C: d) What is the amount and composition of each phase that is present at 183°C - ∆T ? e) What are the amounts of each phase present at room temperature? f) Draw the microstructure 183°C + ∆T and 183°C - ∆T in 2 cm diameter circle.
find the relative amounts (in terms of mass fractions) of the phases for the following alloys and temperature: 90 wt% Zn-10 wt% Cu at 400°C.
Using the Ti-Cu phase diagram, if you start with 100 kg of a Ti-Cu mixture at 3000C and 10 wt. % Cu and cool down very slowly to point D (500 C), determine what phases are present at each letter, determine the compositions for each phase, and determine theweight in each phase. Point D): Phase(s) present Weight % of Cu in each phaseWeight of each phase
Is it possible to have a copper–zinc alloy that, at equilibrium, consists of an  phase of composition 75 wt% Zn– 25 wt% Cu, and also a liquid phase of composition 90 wt% Zn and 10 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why.
Question: For 5.7 kg of a magnesium–lead alloy of composition 50 wt% Pb–50 wt% Mg, is it possible, at equilibrium, to have α and Mg2Pb phases with respective masses of 5.13 and 0.57 kg? If so, what will be the approximate temperature of the alloy? If such an alloy is not possible, then explain why.
From the phase diagram of the Fe-0.25wt%C alloy below, determine the phase fraction and elemental composition of the resulting phase immediately after solidification across the eutectoid line (725 C). a.alpha_eutectoid = 96.6 wt% and cementite = 29.85 wt% b.alpha_eutectoid = 96.6 wt% and cementite = 3.4 wt% c.alpha_eutectoid = 1.05 wt% and cementite = 29.85 wt% d.alpha_eutectoid = 29.85 wt% and cementite = 1.05 wt%
For an alloy containing 40% p Sn - 60% p Pb at a temperature of 150°C: (a) Which phases are gifts? (b) What is (are) the composition(s) of this (s) phase(s)? (c) Calculate as quantities relatives of each phase present in terms of the mass fraction. (image attached below)