During a tensile test on a specimen of steel the following data was recorded, diameter of specimen 6.6mm gauge length of 50mm ,elongation of a load of 6.0 KN of 0.043mm. Reduction of area at failure of 45percent. Calculate the youngs modulus of elasticity ,the yield stress and the ultimate stress

During a tensile test on a specimen of steel the following data was recorded, diameter of specimen 6.6mm gauge length of 50mm ,elongation of a load of 6.0 KN of 0.043mm. Reduction of area at failure of 45percent. Calculate the youngs modulus of elasticity ,the yield stress and the ultimate stress

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.5P: The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen...

See similar textbooks

Related questions

Q: The following observations were made during a tensile test on a mild steel specimen 40 mm in…

A: Given data : Tensile load P=40 KN Change in length ∆L=0.0202 mm Initial length L=200 mm Diameter of…

Q: 3.33 The following data are obtained from a tensile test of a 12.7-mm-diameter aluminum specimen…

A: As per the Guidelines of Bartleby We are supposed to answer only first three subparts. Ultimate…

Q: After fracture, the total length was 53.086 mm and the diameter was 9.982 mm. Plot the engineering…

A: “Since you have posted a question with multiple sub-parts, we will solve first three subparts for…

Q: EXAMPLE 2.4. In an experiment, a steel specimen of 13 mm diameter was found to elongate 0.2 mm in a…

Q: A hot-rolled steel bar has a diameter of 12 mm was subjected to a tension test as shown in the…

A: NOTE As per our company guidelines we are supposed to answer only first 3 sub-parts. Kindly repost…

Q: A high-yield-strength alloy steel bar with a rectangular cross section that has a width of 37.5 mm,…

A: Since we only answer up to 3 sub-parts, we’ll answer the first 3. Please resubmit the question and…

Q: A steel bar with a 30 mm diameter is tested in tension. By monitoring the load reading of the…

A: Solution Given Data Diameter of specimen= 30 mm yielding load=185 kN Fracture load= 215 kN

Q: A stainless-steel rod 16mm in diameter and 300mm long is put under a tensile load of 250 kN.…

A: Given data Initial diameter of the rod(Di) = 16 mm Then Area (Ai) = (π/4)*Di2 = 201.062 mm2…

Q: During a tensile test on a specimen of 1 cm² cross-section, maximum load observed was 8 tonnes and…

A: given- Area A=1 cm2Maximum load P=8 tonnes

Q: metal rod with 0.5 in. diameter and 12.0 in. length is put under a compressive load of 150 kips.…

A: Calculate the final length and the final diameter of this specimen under this load

Q: Q3: A cylindrical specimen of steel having an original diameter of (12.8mm) is tensile tested to…

Q: A tensile test is performed on a brass specimen 10mm in diameter using a gage lenght of 50mm. When…

A: Given data:d=10 mmL=50 mmδ=0.122 mm P=20 KN

Q: A tensile test is carried out on a steel rod of 14mm radius and gauge length of 140 mm. The yield…

A: Tensile test is carried out to draw the stress strain curve of the steel. The given data is:…

Q: snip

Q: Problem NO. 2. A student performed a tensile test in one of his samples, an aluminum specimen which…

Q: Problem 4: A tensile test is carried out on a bar of a mild steel of diameter 2 cm. the bar yields…

A: Question is based on the tensile test which is performed on mild steel bar .Diameter of mild steel…

Q: Question 4 A torsion test shows that the shear modulus of an aluminum specimen is 4.60 x 106 psi.…

Q: The tensile test was carried out on a steel bar of length 18 cm and a cross section of 18 mm in…

A: Schematic diagram of the given problem: Maximum permissible tensile stress σ=400 N/mm2 E=200×103…

Q: At a point on the free surface of an aluminum alloy (E = 10) x 10" psi and v = 1/3) machine…

Q: Problem 8: The following load elongation data were recorded during the tensile testing of a copper…

A: "Thank you for the question. As per our honor we are supposed to solve first three sub parts, kindly…

Q: Question One (Compulsory) The following results were obtained during a tensile testing of a highiy…

A: Note:- Hi! Thank you for the question, As per the honor code, we are allowed to answer three…

Q: A tensile test was conducted on a mild steel bar for construction application in Falcon company’s…

Q: A steel bolt 0.003 m2 in cross- section is subjected to a static mean load of 178 kN.Using Soderberg…

A: Given: The cross-sectional area of the bolt is 0.003 m2. The static mean load is 178 kN. The yield…

Q: A Charpy V Notch (CVN) test was performed on a steel specimen and produced the following readings:…

A: Charpy V-notch Test: The Charpy V-notch test is also known as Charpy impact test. This test is a…

Q: snip

A: (a) It is required to determine the stress. σ=LoadArea=250 lbπ4×0.51 in2=1223.80 psi Similarly…

Q: test conducted on a steel bar whose cross section is 0.5 in. by 4 in. is performed. An axial load of…

A: Given:- A=0.5*4 in P=30500lb △L=0.00103in Gauge Length = 2in △d=0.000078in t = 0.5 in To find:- a)…

Q: Question 4. A tensile test is carried out on a bar of mild steel of diameter 2 cm. The bar yields…

A: Solution: Mild steel bar diameter d =2cm Bar yield under a load Py=80kn…

Q: A tensile test is performed on a brass specimen 10mm in diameter using a gage length of 50mm When…

Q: b) Figure Q1 shows ceramic specimens subjected to the pure uniaxial force. Specimen A is compressed…

A: An elemental area can be subjected to stress due to applied load . For uniaxial it is subjected to…

Q: Prob- In a tensile test carried out in the laboratory on a steel specimen for 5 minutes. The strain…

A: given- strain=0.30time=5 mintues

Q: 10. A metal rod with 0.5 in. diameter and 12.0 in. length is put under a compressive load of 150…

Q: (b) (i) A tensile test specimen made from 0.4% C steel has a circular cross section of diameter d mm…

Q: A tensile test was performed on a metal specimen having a circular cross section with a diameter of…

A: Given that: Diameter of specimen, d=12 in.Gauge length, l = 2 in.Load, P =…

Q: A steel bar with a 30 mm diameter is tested in tension. By monitoring the load reading of the…

Q: This figure shows typical stress-strain behaviour for a brass. The inset figure shows the behaviour…

A: Given Data: Initial length of test sample is L=14 cm. Initial radius of test sample is R=2 mm.

Q: A torsion test shows that the shear modulus of an aluminum specimen is 4.60 x 10 6 psi. When the…

Q: A sample of a steel alloy has a yield strength of 560 MPa, ultimate tensile strength of 630 MPa, and…

Q: A steel specimen is tested in tension. The specimen is 1 in. wide by 0.5 in. thick in the test…

A: Given: The width of the specimen is 1 in. The thickness of the specimen is 0.5 in. The yield load of…

Q: Engineering strain of a mild steel sample is recorded as 0.100%. The true strain is 1. 0.010% 0.055%…

Q: A cylinder with a 6.0 in. diameter and 12.0 in. length is put under a compressive load of 150 kips.…

A: Given data

Q: During a tensile test on a specimen of steel the following data was recorded diameter of the…

A: Given Information:

Q: DURING THE STRESS-STRAIN TEST, THE UNIT DEFORMATION AT A STRESS OF 30 MPa WAS OBSERVED TO BE 110 x…

A: Answer Calculation of Modulus of elasticity We are given At stress = 30 Mpa we get strain 110* 10-6…

Q: A steel specimen is tested in tension. The specimen is 2 in. wide by 2.3 in. thick in the test…

Q: A steel rod, 12mm in diameter and 150mm long was subjected to a tensile test. After the test, the…

Q: A tensile stress is applied along the long axis of a cylindrical aluminum rodwith a diameter of 10…

A: Given data: Diameter =10 mm Change in dia=2.5 * 103 E=70 GPa Poisson’s ratio = 0.33.

Q: A torsion test shows that the shear modulus of an aluminum specimen is 4.60 x 10 psi. When the same…

A: Appreciate if there is detailed work with explanation and finds you helpful for ease of…

Question

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Trending now

This is a popular solution!

Step by step

Solved in 4 steps with 4 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The dam were plotted on a load-displacement graph. P vs. L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/L =1392 kips/in. What is the modulus of elasticity?
Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
A tensile test was conducted on a mild steel bar for construction application in Falcon company’sEngineering Materials lab. The following data was obtained from the test(i) diameter of the steel bar = 3cm(ii) Gauge length of the bar = 20 cm(iii) Load at elastic limit = 250 kN(iv) Extension at a load of 150kN = 0.21 mm(v) failure load = 380 kN(vi) Total extension = 60 mm(vii) diameter of the rod at failure = 2.25 cmDetermine (a) Young’s Modulus, (b) Stress at elastic limit, (c) percentage of elongation,(d) Percentage of decrease in area (d) failure stress
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1/2 inch. the gage lenght ( the lenght over which the elongation is measured ) is 2 inches. for a load 13.5 kips, the elongation was 4.66x10^-3 inches. if the load is assumed to be with in the linear elastic range of the material , determine the modulus of elasticity
The tensile test is carried out on a steel rod of 16mm diameter and gauge lengthof 150mm.The yield strength of the steel is 700 MPa. At the tension load of 75 KN, Calculate stress ands train of the steel rod, taking Young’s Modulus of Elasticity as 200,000 MPa. Find out if the steel rod is in elastic region or already yielded.
A steel bar with a 30 mm diameter is tested in tension. By monitoring the load reading of the testing machine, it was found that the specimen yielded at a load of 185 kN and fractured at 215 kN. Determine the tensile stresses at yield and at fracture. Estimate how much increase in length would occur at 70% of the yield stress in a 50 mm gauge length.
A cylindrical specimen of aluminum alloy having a diameter of 12.8 mm and a gauge length (lo) of 50.800 mm is pulled in tension. Use the load–elongation characteristics shown in the following table and answer the following questions. (10p) i- Convert the data as engineering stress (σ) versus engineering strain (ε). ii- Compute the modulus of elasticity (E) (with a precision of ±5000 MPa) iii- Determine the yield strength at a strain offset of 0.002 (σy) (with a precision of ±20 MPa) iv- Determine the tensile strength (TS) of this alloy.
A tensile test is performed on a brass specimen 10mm in diameter using a gage lenght of 50mm. When the tensile load P reachers a value of 20kN, the distance between the gage marks has increased by 0.122 mm. What is the modulus of elasticity of the brass.