Example 8.4. A specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i) The stress at elastic limit. (ii) Young's modulus. (iin Parcantaga alongation

Example 8.4. A specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i) The stress at elastic limit. (ii) Young's modulus. (iin Parcantaga alongation

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.1P

See similar textbooks

Similar questions

The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The dam were plotted on a load-displacement graph. P vs. L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/L =1392 kips/in. What is the modulus of elasticity?
Sketch the stress-strain curve of the following tension test??? In the tension test of a metal fracture occurs at maximum load. The conditions at fracture were: A = 100 mm and L, = 60 mm, the initial values were: A = 150 mm and L. 40 mm.
A steel wire with a diameter of d = 1/16” is bent around a cylindrical drum with a radius ofR = 36”.(a) Determine the maximum normal strain in the wire.(b) What is the minimum acceptable radius of the drum if the maximum normal strain mustremain below yield? Consider an elastic modulus of 30000 ksi and yield stress of 100ksi.(c) If R = 36”, what is the maximum acceptable diameter of the wire if the maximum normalstrain must remain below yield?
A cylindrical specimen of 1018 steel having a diameter of 6.35 mm and a gauge length of38.1 mm is pulled in tension. Use the load-elongation characteristics tabulated below. Determine the yield strength (σy) at a strain offset of 0.002.
A load applied to a machine component results in the state of plane stress ?x=80 MPa, ?y=100 MPa, ?xy=60 MPa. The component is made of a brittle high-strength steel that follows the maximum normal stress criterion with ?u=200 MPa. If increasing the load increases each stress component proportionally, determine the percentage increase that can be applied before the component fails.
A cylindrical brass specimen having a diameter of 1.10 cm and initial gage length of 4.04 cm is subjected to tensile strength test. The load-deformation values are given in the below table. The final length and final diameter of the specimen were measured as 4.33 cm and 0.92 cm, respectively. Complete the below table and plot true stress-true strain diagram and determine. Yield strength at 0.2 % off-set method. Poisson’s ratio of the material at 135 kN load (assume that there is no volume change) If the material were unloaded from 175 kN, what would be its final length? 1 nm=1*10-9 m, 1 0A=10-10 m
The tensile test is carried out on a steel rod of 16mm diameter and gauge lengthof 150mm.The yield strength of the steel is 700 MPa. At the tension load of 75 KN, Calculate stress ands train of the steel rod, taking Young’s Modulus of Elasticity as 200,000 MPa. Find out if the steel rod is in elastic region or already yielded.
Consider a cylindrical metal 6 mm in diameter and 50 mm long ispulled in tension. It is known that yield strength and elastic (Young’s) Modulus of thematerial are 200 MPa and 100 GPa, respectively, and its Poisson’s Ratio is 0.3.(a) Determine whether the deformation is elastic or plastic when 6000 N is applied.(b) Calculate specimen elongation (∆l) and reduction in diameter (∆d) when 5000 N isapplied? What are the values ∆l and ∆d when the load is released?(c) If necking occurs at a load of 8850 N, determine the UTS of the metal.(d) Calculate the ductility in terms of % E.L. if the length of the specimen at fracturepoint is 56.0 mm.