The questions below refer to the Fe-Fe3C phase diagram below. Composition (at% C) 1E 1600 1538°C 10 15 1493°C L 1400 1394°C Y+L 1200 1147°C 2.14 4.30 7. Austenite 1000 912 C Y+ Fe3C 800 727°C 0.76 0.022 600 a, Ferrite a + FezC Cei 400 0. 3. 4 (Fe) Composition (wt% C) Adapted from Binary Alloy Phase Diagrams, Vol. 1, 2nd edition, T. B. Massalski (Editor-in-Ch by permission of ASM International, Materials Park, OH. For an alloy with a composition of 3.5 wt% C slowly cooled from the complete melting temperature: At what temperature does the first solid phase form? At what temperature does complete solidification of the alloy occur? Temperature (°C)

The questions below refer to the Fe-Fe3C phase diagram below. Composition (at% C) 1E 1600 1538°C 10 15 1493°C L 1400 1394°C Y+L 1200 1147°C 2.14 4.30 7. Austenite 1000 912 C Y+ Fe3C 800 727°C 0.76 0.022 600 a, Ferrite a + FezC Cei 400 0. 3. 4 (Fe) Composition (wt% C) Adapted from Binary Alloy Phase Diagrams, Vol. 1, 2nd edition, T. B. Massalski (Editor-in-Ch by permission of ASM International, Materials Park, OH. For an alloy with a composition of 3.5 wt% C slowly cooled from the complete melting temperature: At what temperature does the first solid phase form? At what temperature does complete solidification of the alloy occur? Temperature (°C)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

From the phase diagram of the Fe-0.25wt%C alloy below, determine the phase fraction and elemental composition of the resulting phase immediately after solidification across the eutectoid line (725 C). a.alpha_eutectoid = 96.6 wt% and cementite = 29.85 wt% b.alpha_eutectoid = 96.6 wt% and cementite = 3.4 wt% c.alpha_eutectoid = 1.05 wt% and cementite = 29.85 wt% d.alpha_eutectoid = 29.85 wt% and cementite = 1.05 wt%
Calculate the amounts and compositions of phases at 726oC in a Fe-0.6% C alloy cooled under equilibrium conditions. Disregard the amounts of proeutectoid phases. A. 77.3% α, 22.7% Fe3C; C in α = 6.7% and C in Fe3C = 0.02% B. 91.3% α, 8.7% Fe3C; C in α = 0.02% and C in Fe3C = 6.7% C. 77.3% α, 22.7% Fe3C; C in α = 0.02% and C in Fe3C = 6.7% D. 91.3% α, 8.7% Fe3C; C in α = 0.05% and C in Fe3C = 8.4% E. None of the mentioned
10.15) A magnesium-lead alloy of mass 5.5 ka consists of a solid a phase that has a compo- sition that is just slightly below the solubility limit at 200°C (390°F). (a) What mass of lead is in the alloy? (b) If the alloy is heated to 350°C (660°F). how much more lead may be dissolved in the a phase without exceeding the solubility limit of this phase?
According to the lead-tin phase diagram below, what is the maximum solubility of lead in tin? a) 2.2 wt% b) 18.3 wt% c) 81.7 wt% d) 97.8 wt%
Copper-Nickel alloy is widely applied in industry. (a) List at least three applications where Cu-Ni alloy is used; (b) How many components and phases are shown in the below phase diagram? (c) For a mixture of 40 wt% Cu and 60 wt% Ni at 1320 oC, what phases are present? Identify theamount of these phases by applying “lever rule”.
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
The following questions are based on a high carbon steel with a composition of 1,5% C and 98,5% Fe. Please refer to the Fe-Fe3C binary phase diagram in Callister and Rethwhich 1) a Name the phases present and calculate the amounts of these phases just above the eutectoid temperature b, Give the amount of austenite present at 1100°C. c. Give the amount of pro-eutectoid ferrite just above the eutectoid temperature. d. With equilibrium cooling just below the eutectoid temperature calculate the total ferrite. e. Why must the samples be quenched rapidly to obtain high hardness?
Draw the iron-Fe3C phase diagram. Consider 0.4 and 1.1 wt% C steel alloy. It is cooled slowly from a temperature within austenite phase to room temperature. Show a) microstructure at 1000 °C b) microstructure at 730°C c) microstructure at 715°C and d) microstructure at room temperature e) determine the phase present, the phase compositions at 715 and 730 °C f) What do you say about mechanical properties of these alloys, depending on their microstructure at room temperature?
For an Fe-0.35% C alloy, determine the composition and amount of each phase present at 726 ° C; and the composition and amount of each microconstituent present at 726 °C.
4b) Figure 6 shows the Fe-Fe3C phase diagram. Evaluate (i) the temperature at which austenite first begins to transform on cooling; (ii) the primary microconstituent that forms; (iii) the composition and amount of each phase present at 728°C; (iv) the composition and amount of each phase present at 726°C; (v) Sketch the evolution of the microstructures of hypereutectoid steels with 1.1 wt% of carbon during the cooling in relationship to Fe-Fe3C phase diagram shown at 900°C, 800°C and 500°C, respectively.
An alloy of 30 wt % Pb and 70 wt % Sn is slowly cooled from 250°C to 27°C: a) Is this alloy hypoeutectic or hypereutectic? b) What is the composition of the first solid to form? c) What are the amounts and compositions of each phase that is present at 183°C + ∆T ? d) What is the amount and composition of each phase that is present at 183°C - ∆T ? e) What are the amounts of each phase present at room temperature? f) Draw the microstructure 183°C + ∆T and 183°C - ∆T in 2 cm diameter circle.
1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. At 720C we keep the alloy to maintain equilibrium. Determine the amounts of the following, in grams. Pearlite Proeutectoid phase Total cementite