In the Mond process for the purification of nickel, carbon monoxide is combined with heated nickel to produce Ni(CO)4, which is a gas and can therefore be separated from solid impurities.
Given that the standard free energies of formation of CO(g) and Ni(CO)4(g) are −137.3 and −587.4 kJ/mol, respectively, calculate the equilibrium constant of the reaction at 80°C. Assume that ΔG°f is temperature independent.
Want to see the full answer?
Check out a sample textbook solutionChapter 15 Solutions
Chemistry: Atoms First
- Without doing any calculations, predict the sign of rS for the following reaction: Zn(s) + 2 HCl(aq) ZnCl2(aq) + H2(g) (a) rS 0 (b) rS = 0 (c) rS 0arrow_forwardSilver carbonate, Ag2CO3, is a light yellow compound that decomposes when heated to give silver oxide and carbon dioxide: Ag2CO3(s)Ag2O(s)+CO2(g) A researcher measured the partial pressure of carbon dioxide over a sample of silver carbonate at 220C and found that it was 1.37 atm. Calculate the partial pressure of carbon dioxide at 25C. The standard enthalpies of formation of silver carbonate and silver oxide at 25C are 505.9 kJ/mol and 31.05 kJ/mol, respectively. Make any reasonable assumptions in your calculations. State the assumptions that you make, and note why you think they are reasonable.arrow_forwarda Calculate K1, at 25C for sulfurous acid: H2SO3(aq)H+(aq)+HSO3(aq) b Which thermodynamic factor is the most significant in accounting for the fact that sulfurous acid is a weak acid? Why?arrow_forward
- Cobalt(II) chloride hexahydrate, CoCl26H2O, is a bright pink compound, but in the presence of very dry air it loses water vapor to the air to produce the light blue anhydrous salt CoCl2. Calculate the standard free-energy change for the reaction at 25C: CoCl26H2O(s)CoCl2(s)+6H2O(g) Here are some thermodynamic data at 25C: What is the partial pressure of water vapor in equilibrium with the anhydrous salt and the hexahydrate at 25C? (Give the value in mmHg.) What is the relative humidity of air that has this partial pressure of water? The relative humidity of a sample of air is Relativehumidity=partialpressureofH2O(g)inairvaporpressureofwater100 What do you expect to happen to the equilibrium partial pressure over the hexahydrate as the temperature is raised? Explain.arrow_forwardElemental boron, in the form of thin fibers, can be made by reducing a boron halide with H2. BCl3(g) + 32 H2(g) B(s) + 3 HCl(g) Calculate rH, rS, and rG at 25 C for this reaction. Is the reaction predicted to be product-favored at equilibrium at 25 C? If so, is it enthalpy- or entropy-driven? [S for B(s) is 5.86 J/K mol.]arrow_forwardElemental boron, in the form of thin fibers, can be made by reducing a boron halide with H2. BCl3(g) + 3/2 H2(g) B(s) + 3HCl(g) Calculate H, S, and G at 25 C for this reaction. Is the reaction predicted to be product favored at equilibrium at 25 C? If so, is it enthalpy driven or entropy driven?arrow_forward
- Adenosine triphosphate, ATP, is used as a free-energy source by biological cells. (See the essay on page 624.) ATP hydrolyzes in the presence of enzymes to give ADP: ATP(aq)+H2O(l)ADP(aq)+H2PO4(aq);G=30.5kJ/molat25C Consider a hypothetical biochemical reaction of molecule A to give molecule B: A(aq)B(aq);G=+15.0kJ/molat25C Calculate the ratio [B]/[A] at 25C at equilibrium. Now consider this reaction coupled to the reaction for the hydrolysis of ATP: A(aq)+ATP(aq)+H2O(l)B(aq)+ADP(aq)+H2PO4(aq) If a cell maintains a high ratio of ATP to ADP and H2PO4 by continuously making ATP, the conversion of A to B can be made highly spontaneous. A characteristic value of this ratio is [ATP][ADP][H2PO4]=500 Calculate the ratio [B][A] in this case and compare it with the uncoupled reaction. Compared with the uncoupled reaction, how much larger is this ratio when coupled to the hydrolysis of ATP?arrow_forwardThe free energy of formation of one mole of compound refers to a particular chemical equation. For each of the following, write that equation. a KBr(s) b CH3Cl(l) c H2S(g) d AsH3(g)arrow_forwardFor the decomposition of formic acid, HCOOH(l)H2O(l)+CO(g) H = +29 kJ/mol at 25C. a Does the tendency of this reaction to proceed to a state of minimum energy favor the formation of water and carbon monoxide or formic acid? Explain. b Does the tendency of this reaction to proceed to a state of maximum entropy favor the formation of products or reactants? Explainarrow_forward
- Impure nickel, refined by smelting sulfide ores in a blast furnace, can be converted into metal from 99.90% to 99.99% purity by the Mond process. The primary reaction involved in the Mond process is Ni(s)+4CO(g)Ni(CO)4(g) a. Without referring to Appendix 4, predict the sign of S for the above reaction. Explain. b. The spontaneity of the above reaction is temperature-dependent. Predict the sign of Ssurr, for this reaction. Explain c. For Ni(CO)4(g), Hfo=607KJ/mol and S = 417 J/K mol at 298 K. Using these values and data in Appendix 4, calculate H and S for the above reaction. d. Calculate the temperature at which G = 0 (K = 1) for the above reaction, assuming that H and S do not depend on temperature. e. The first step of the Mood process involves equilibrating impure nickel with CO(g) and Ni(CO)4(g) at about 50C. The purpose of this step is to convert as much nickel as possible into the gas phase. Calculate the equilibrium constant for the above reaction at 50.C. f. In the second step of the Mood process, the gaseous Ni(CO)4 is isolated and heated to 227C. The purpose of this step is to deposit as much nickel as possible as pure solid (the reverse of the preceding reaction). Calculate the equilibrium constant for the preceding reaction at 227C. g. Why is temperature increased for the second step of the Mood process? h. The Mond process relies on the volatility of Ni(CO)4 for its success. Only pressures and temperatures at which Ni(CO)4 is a gas are useful. A recently developed variation of the Mood process carries out the first step at higher pressures and a temperature of l52C. Estimate the maximum pressure of Ni(CO)4(g) that can be attained before the gas will liquefy at 152C. The boiling point for Ni(CO)4 is 42C and the enthalpy of vaporization is 29.0 kJ/mol. [Hint: The phase change reaction and the corresponding equilibrium expression are Ni(CO)4(l)Ni(CO)4(g)K=PNi(CO)4 Ni(CO)4(g) will liquefy when the pressure of Ni(CO)4 is greater than the K value.]arrow_forwardIn muscle cells under the condition of vigorous exercise, glucose is converted to lactic acid (lactate),CH3CHOHCOOH, by the chemical reaction C6H12O6 2 CH3CHOHCOOHrG = 197 kJ/mol (a) If all of the Gibbs free energy from this reaction wereused to convert ADP to ATP, calculate how many molesof ATP could be produced per mole of glucose. (b) The actual reaction involves the production of 3 molATP per mole of glucose. Calculate the rG for thisoverall reaction. (c) Is the overall reaction in part (b) reactant-favored orproduct-favored?arrow_forwardThe standard free energies of formation and the standard enthalpies of formation at 298 K for difluoroacetylene (C2F2) and hexafluorobenzene (C6F6) are Gfo(KJ/mol) Hfo(KJ/mol) C2F2(g) 191.2 241.3 Hexane 78.2 132.8 For the following reaction: C6F6(g)3C2F2(g) a. calculate S at 298 K. b. calculate K at 298 K. c. estimate K at 3000. K, assuming H and S do not depend on temperature.arrow_forward
- General Chemistry - Standalone book (MindTap Cour...ChemistryISBN:9781305580343Author:Steven D. Gammon, Ebbing, Darrell Ebbing, Steven D., Darrell; Gammon, Darrell Ebbing; Steven D. Gammon, Darrell D.; Gammon, Ebbing; Steven D. Gammon; DarrellPublisher:Cengage LearningChemistry & Chemical ReactivityChemistryISBN:9781337399074Author:John C. Kotz, Paul M. Treichel, John Townsend, David TreichelPublisher:Cengage LearningChemistry & Chemical ReactivityChemistryISBN:9781133949640Author:John C. Kotz, Paul M. Treichel, John Townsend, David TreichelPublisher:Cengage Learning
- Chemistry by OpenStax (2015-05-04)ChemistryISBN:9781938168390Author:Klaus Theopold, Richard H Langley, Paul Flowers, William R. Robinson, Mark BlaserPublisher:OpenStaxChemistry: The Molecular ScienceChemistryISBN:9781285199047Author:John W. Moore, Conrad L. StanitskiPublisher:Cengage LearningChemistry: Principles and PracticeChemistryISBN:9780534420123Author:Daniel L. Reger, Scott R. Goode, David W. Ball, Edward MercerPublisher:Cengage Learning