Textbook Question
Chapter 2, Problem 64QTP
A metal has the following properties: UTS = 70,000 psi and n = 0.20. Calculate its strength coefficient, K.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
in tensile test data, show step by step how to find stress and strain in aluminium
Calculate the Vickers hardness when a 700-g load yields an indentation diagonal length of 0.050 mm.
Solve the question given below :
A piece of metal was indented at a load of 100 kgf with a 10 mm diameter tungsten carbide ball. If the indentation diameter is 20% of the ball diameter, calculate the hardness number of the metal.
Chapter 2 Solutions
Manufacturing Engineering And Technology
Ch. 2 - Distinguish between engineering stress and true...Ch. 2 - In a stress-strain curve, what is the proportional...Ch. 2 - Describe the events that take place when a...Ch. 2 - What is ductility, and how is it measured?Ch. 2 - In the equation =Kn, which represents the true...Ch. 2 - What is strain-rate sensitivity, and how is it...Ch. 2 - What test can measure the properties of a material...Ch. 2 - What testing procedures can be used to measure the...Ch. 2 - Describe the differences between brittle and...Ch. 2 - What is hardness? Explain.
Ch. 2 - Describe the features of a Rockwell hardness test.Ch. 2 - What is a Leeb test? How is it different from a...Ch. 2 - Differentiate between stress relaxation and creep.Ch. 2 - Describe the difference between elastic and...Ch. 2 - Explain what uniform elongation means in tension...Ch. 2 - Describe the difference between deformation rate...Ch. 2 - Describe the difficulties involved in conducting a...Ch. 2 - What is Hookes law? Youngs modulus? Poissons...Ch. 2 - Describe the difference between transgranular and...Ch. 2 - What is the reason that yield strength is...Ch. 2 - Why does the fatigue strength of a specimen or...Ch. 2 - If striations are observed under microscopic...Ch. 2 - What is an Izod test? Why are Izod tests useful?Ch. 2 - Why does temperature increase during plastic...Ch. 2 - What is residual stress? How can residual stresses...Ch. 2 - On the same scale for stress, the tensile true...Ch. 2 - What are the similarities and differences between...Ch. 2 - Can a material have a negative Poissons ratio?...Ch. 2 - It has been stated that the higher the value of m,...Ch. 2 - Explain why materials with high m values, such as...Ch. 2 - With a simple sketch, explain whether it is...Ch. 2 - Explain why the difference between engineering...Ch. 2 - Consider an elastomer, such as a rubber band. This...Ch. 2 - If a material (such as aluminum) does not have an...Ch. 2 - What role, if any, does friction play in a...Ch. 2 - Which hardness tests and scales would you use for...Ch. 2 - Consider the circumstance where a Vickers hardness...Ch. 2 - Which of the two tests, tension or compression,...Ch. 2 - List and explain briefly the conditions that...Ch. 2 - List the factors that you would consider in...Ch. 2 - On the basis of Fig. 2.5, can you calculate the...Ch. 2 - If a metal tension-test specimen is rapidly pulled...Ch. 2 - Comment on your observations regarding the...Ch. 2 - Will the disk test be applicable to a ductile...Ch. 2 - What hardness test is suitable for determining the...Ch. 2 - Wire rope consists of many wires that bend and...Ch. 2 - A statistical sampling of Rockwell C hardness...Ch. 2 - In a Brinell hardness test, the resulting...Ch. 2 - Some coatings are extremely thinsome as thin as a...Ch. 2 - Select an appropriate hardness test for each of...Ch. 2 - A paper clip is made of wire 0.5 mm in diameter....Ch. 2 - A 250-mm-long strip of metal is stretched in two...Ch. 2 - Identify the two materials in Fig. 2.5 that have...Ch. 2 - Plot the ultimate strength vs. stiffness for the...Ch. 2 - If you remove the layer of material ad from the...Ch. 2 - Prove that the true strain at necking equals the...Ch. 2 - Percent elongation is always defined in terms of...Ch. 2 - You are given the K and n values of two different...Ch. 2 - A cable is made of two strands of different...Ch. 2 - On the basis of the information given in Fig. 2.5,...Ch. 2 - In a disk test performed on a specimen 1.00 in. in...Ch. 2 - A piece of steel has a hardness of 300 HB....Ch. 2 - A metal has the following properties: UTS = 70,000...Ch. 2 - Using only Fig. 2.5, calculate the maximum load in...Ch. 2 - Estimate the modulus of resilience for a highly...Ch. 2 - A metal has a strength coefficient K = 100,000 psi...Ch. 2 - Plot the true stresstrue strain curves for the...Ch. 2 - The design specification for a metal requires a...Ch. 2 - Calculate the major and minor pyramid angles for a...Ch. 2 - If a material has a target hardness of 300 HB,...Ch. 2 - A Rockwell A test was conducted on a material and...Ch. 2 - For a cold-drawn 0.5% carbon steel, will a...Ch. 2 - A material is tested in tension. Over a 1-in. gage...Ch. 2 - A horizontal rigid bar cc is subjecting specimen a...Ch. 2 - List and explain the desirable mechanical...Ch. 2 - When making a hamburger, you may have observed the...Ch. 2 - An inexpensive claylike material called Silly...Ch. 2 - In tension testing of specimens, mechanical and...Ch. 2 - Demonstrate the impact toughness of a piece of...Ch. 2 - Using a large rubber band and a set of weights,...Ch. 2 - Find or prepare some solid circular pieces of...Ch. 2 - Take several rubber bands and pull them at...Ch. 2 - Devise a simple fixture for conducting the bend...Ch. 2 - By pressing a small ball bearing against the top...Ch. 2 - Describe your observations regarding Fig. 2.14c.Ch. 2 - Embed a small steel ball in a soft block of...Ch. 2 - Devise a simple experiment, and perform tests on...Ch. 2 - Obtain some solid and some tubular metal pieces,...Ch. 2 - Explain how you would obtain an estimate of the...Ch. 2 - Without using the words stress or strain, define...Ch. 2 - We know that it is relatively easy to subject a...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Can a metal have all the mechanical properties at ideal levels? Why or why not?arrow_forwardcompute the tensile strength and ductility of a cylindrical copper rod if it is cold worked such that the diameter is reduced from 12 to 10 mmarrow_forwardDraw a Stress/Strain graph of a mild tensile steel and identify the limit of proportionality and the yield pointarrow_forward
- Describe the behavior of tested materials (mild steel and aluminium) as it responds to increasing load, in tensile test experiment.arrow_forwardTensile test under 40,000 N load was applied to a low carbon steel with a sample diameter of 6 mm. As the diameter of the specimen under load decreases to 5 mm, calculate a) Engineering stress and% elongation values, b) Actual stress and% elongation values.arrow_forwardUnder an applied axial load, a rod elongates by 0.49 in. If the rod is 11 ft long, and has a 2.0 in. diameter. If the transverse deformation of the rod is 0.0024 in., calculate the material's Poisson's ratio: _____ . Pay calculate your answer to 3 significant figures.arrow_forward
- A metal wire of diameter 1.2 mm is used to carry a load of 1100 N. If the material of which the wire is made has a yield point of 950 MPa ultimate tensile strength of 1425 MPa then is this wire suitable for carrying that load? If yes, then support your answer with calculations and explain your results. If the answer is no, then explain why with calculations and calculate the required diameter of that wire to carry that load.arrow_forwardWhen an aluminum tensile sample with an initial diameter of 12.827 mm was tested, a maximum load of 66.72 kN was recorded at an engineering strain of 0.4 . What is the load on an identical tensile sample with an engineering strain of 0.2 ?arrow_forwardI did a torsion test to experimentally calculate the brass modulus of rigidity. My experimental modulus value is lower than the published. What could have caused this?arrow_forward
- A monocrystal of a CCC metal is oriented so that the direction [001] is parallel to an applied voltage. Consider that the critical effective shear stress required for the slip is 83 MPa and calculate the magnitude of the applied stress necessary to start the slip in the direction [111] of the sliding planes (110), (011) and ( 101).arrow_forwardFor a tensile test it can be shown that the percent cold work (%CW) is related to strain according to the following relationship: %CW=(εε+1) × 100 Using this equation, compute the percent cold work experienced by naval brass (for which the stress-strain behavior is shown in the Animated Figure 6.12) when a stress of 415 MPa (60190 psi) is applied.arrow_forwardA material has a strength coefficient of 150,000 psi. At the onset of plastic deformation, the material had an 18 percent increase over its initial length, and at the beginning of non-uniform deformation, the material experienced an engineering strain of 0.58. Calculate the engineering and true strains at yield. Also, calculate the engineering and true strains at the point where a maximum engineering stress is experienced by the material. Determine the strain-hardening index. Calculate the ultimate tensile strength. Calculate the modulus of elasticity. Given: K = 150,000 psi 18% increase in length ey = 0.58 Want: ey =? eu =? n =? UTS =? E =? εy =? εu =?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Welding: Principles and Applications (MindTap Cou...Mechanical EngineeringISBN:9781305494695Author:Larry JeffusPublisher:Cengage Learning
Welding: Principles and Applications (MindTap Cou...
Mechanical Engineering
ISBN:9781305494695
Author:Larry Jeffus
Publisher:Cengage Learning
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY