Concept explainers
(a)
The theoretical shear strength for aluminum, plain-carbon steel, and tungsten.
(a)
Answer to Problem 3.43P
The theoretical shear strength for aluminum, plain-carbon steel, and tungsten are
Explanation of Solution
Formula used:
The expression for the modulus of rigidity is given as,
Here,
The expression for the theoretical shear strength is given as,
Calculation:
The value of Young’s modulus and Poisson’s ratio for aluminum is,
The value of modulus of rigidity of aluminum can be calculated as,
The value of Young’s modulus and Poisson’s ratio for steel is,
The value of modulus of rigidity of steel can be calculated as,
The value of Young’s modulus and Poisson’s ratio for tungsten is,
The value of modulus of rigidity of tungsten can be calculated as,
The value of theoretical shear strength of aluminum can be calculated as,
The value of theoretical shear strength of steel can be calculated as,
The value of theoretical shear strength of tungsten can be calculated as,
Conclusion:
Therefore, the theoretical shear strength for aluminum, plain-carbon steel, and tungsten are
(b)
The theoretical tensile strength for aluminum, plain-carbon steel, and tungsten.
The ratios of their theoretical strength to actual strength.
(b)
Answer to Problem 3.43P
The theoretical tensile strength for aluminum, plain-carbon steel, and tungsten are
The ratios of theoretical strength to actual strength of aluminum, plain-carbon steel, and tungsten are
Explanation of Solution
Formula used:
The expression for the theoretical tensile strength is given as,
The expression for the ratio of theoretical tensile strength to actual tensile strength is given as,
Here,
Calculation:
The value of theoretical tensile strength of aluminum can be calculated as,
The value of theoretical tensile strength of steel can be calculated as,
The value of theoretical tensile strength of tungsten can be calculated as,
The actual tensile strength of the aluminum is,
The actual tensile strength of the steel is,
The actual tensile strength of the steel is,
The value of the ratio of theoretical tensile strength to actual tensile strength for aluminum can be calculated as,
The value of the ratio of theoretical tensile strength to actual tensile strength for steel can be calculated as,
The value of the ratio of theoretical tensile strength to actual tensile strength for tungsten can be calculated as,
Conclusion:
Therefore, the theoretical tensile strength for aluminum, plain-carbon steel, and tungsten are
Therefore, the ratios of theoretical strength to actual strength of aluminum, plain-carbon steel, and tungsten are
Want to see more full solutions like this?
Chapter 3 Solutions
Pearson eText for Manufacturing Processes for Engineering Materials -- Instant Access (Pearson+)
- Describe THREE (3) main points on the stress-strain curve for medium-carbon steel.arrow_forwardSpecify a copper alloy that requires at least 50% elongation and at least 300 MPa tensile strength.arrow_forwardDetermine the tensile and yield strengths for the following materials: (a) UNS G10200 hot-rolled steel. (b) SAE 1050 cold-drawn steel.arrow_forward
- Let's assume that the stress-strain elongation curve of a high-strength steel is given by this equation. o = 1.4*10º"ɛ 3 2.9*10*ɛ ² + 2.1*10°z Calculate the yield limit value of this steel. Oa (kgf/cm³) (For Yield Strength, use a straight line from the starting point and Calculate wwwwwww ww w m by moving the line parallel to the given curve)arrow_forwardI need the answer as soon as possiblearrow_forwardPlease no typing and no internet definitions thank youarrow_forward
- State the range of carbon content in terms of weight percentage that can be theoretically varied in steel. Upon increasing the carbon content in plain carbon steel within the theoretical range, will it enhance or retard the mechanical properties such as tensile strength, compressive strength and hardness.? Give your answer with the span of carbon content that the particular property can. It can prevail.arrow_forwardThe lower yield point for a certain plain carbon steelbar is found to be 135 MPa, while a second bar of the samecomposition yields at 260 MPa. Metallographic analysisshows that the average grain diameter is 50μm in the firstbar and 8μm in the second bar.a. Predict the grain diameter needed to cause a loweryield point of 205 MPa.b. If the steel could be fabricated to form a stablegrain structure of 500 nm grains, what strengthwould be predicted?c. Why might you expect the upper yield point to bemore alike in the first two bars than the lower yieldpoint?arrow_forwardI need the answer quicklyarrow_forward
- Question : Explain key assumptions in the theory of simple stress. Explain different parts of a characteristic stress-strain daigram of steel.(draw labeled and clean diagram)arrow_forwardDescribe the material behavior of Steelarrow_forwardIt is known that a brass alloy has a yield strength of 275 MPa, a tensile strength of 380 MPa and a modulus of elasticity of 103 GPa. It is determined that a 12.7 mm diameter and 250 mm long cylindrical sample made of this alloy is elongated by 7.6 mm under the tensile stress effect. Based on this information, is it possible to calculate the magnitude of the load required to generate the said elongation? If possible, calculate, if not, explain why.arrow_forward
- Welding: Principles and Applications (MindTap Cou...Mechanical EngineeringISBN:9781305494695Author:Larry JeffusPublisher:Cengage Learning