Question
Chapter 4, Problem 4.9P
To determine
The proof that the characteristic size in the Rosin-Rammler equation is the point where
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
According to the following Laboratory data:Draw the Particle Size Curve.Determine Cu and Cc from the granulometric curve and indicate if it is Uniform, Well Graded orBad Grade.Granulometric test; Total Weight = 24,077.0 g
A member 1.5 m long has a cross section 75 mm by75 mm. The member becomes 0.7 mm longer and0.01 mm narrower after loading. Determine Poisson’sratio for the material.
Explain what is setting time, slump value and workability of conrcete having
Plasticiser
Superplasticizer
Hyper plasticizer
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- 22. Explain the difference between Open Structured and Dense Structured Grinding Wheels.arrow_forwardAn aggregate sample was collected in a container and weighed as 528.7 g. The sample was oven dried and theoven dry weight was measured as 506.4 g. If the empty weight of the container was 79.6 g, determine the MC of theaggregatesarrow_forwardCoarse aggregate is placed in a rigid bucket and rodded with a tamping rod to determine its unit weight. The following data are obtained: Volume of bucket = 9.3 Liters Mass of empty bucket = 9 kg Mass of bucket filled with dry-rodded coarse aggregate: Trial 1 = 30.25 kg Trial 2 = 29.76 kg Trial 3 = 31.12 kga. Calculate the individual dry-rodded unit weight for each trial and the average dry-rodded unit weight of all trials.b. If the bulk dry specific gravity of the aggregate is 2.65, calculate the percent voids between aggregates particles for each trial and the average percent voids of all trials.arrow_forward
- 4. A series of tests are run on a HMAC Sample. The following data is given to you:% AC (Pb) = 10 %Gb = 1.040Gsb = 2.51Gmm = 2.696Mass of compacted HMAC sample = 840 grMass of compacted HMAC sample submerged in water = 512 grMass of compacted HMAC sample, SSD condition = 847 gra. Based on the above information what is the Gmb? b. Based on the above information what is the of VTM? c. Based on the above information what is the of VMA? d. Based on the above information what is the of VFA?arrow_forwardCalculate the value of SS of the misxture.arrow_forwardAn aggregate sample has a compacted dry unit weight of 1615 kg/m3 and a dry specific gravity of 2.15 If this aggregate is placed in a container and compacted with the same procedure used in the determination of compacted unit weight, what will be the amount of pores, in percent of the container volume, between the aggregate particles? (density of water = 1000 kg/m3)arrow_forward
- Sieve analysis of a sample of fine aggregate resulted in the following data No. Sieve number 4 8 16 30 50 100 Sieve opening (mm) 4.75 2.36 1.18 0.6 0.3 0.15 Weight retained (g) 13 75 120 126 105 61 A) The total weight of the sample, assuming no mass loss during the analysis, is______ (g) a) 505; b) 500; c) 550 B) The half sieve used in the experiment is________. a) No.8; b) No.50; c) none of the above C) The fineness modulus of the aggregate________. a) 6.13; b) 3.16; c) 1.36 D) The average size of the aggregate___________. a) No.30; b) No.4; c) No.16arrow_forwardRecommend and justify the potential usage of AR with BIM in constructionarrow_forwardUSE NCSP 2015arrow_forward
- If a specimen has a factor of safety of F.S. = 1.2 Dead Load + 1.6 Live Load = 1.2 DL + 1.6 LL, and a test shows that a specimen fails at a load of 5000 lb., would you expect the specimen to fail at DL = 1000 lb. And LL = 2000 lbs? Does DL= 1000lb and LL= 2000 lb. exceed allowable?arrow_forwardWhich of the following are to be considered during sampling? 1. Sample should be representative of the material 2. Sample should be properly taken to provide a reliable characterization of the material 3. Sufficient amount must be taken for all analysis a. 1 only b. 2 only c. 1 and 2 d. 1 and 3 d. 1, 2, and 3arrow_forwardShow complete and clear solution. Don't round off initial values, round off final ans only pls tyarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Solid Waste EngineeringCivil EngineeringISBN:9781305635203Author:Worrell, William A.Publisher:Cengage Learning,
Solid Waste Engineering
Civil Engineering
ISBN:9781305635203
Author:Worrell, William A.
Publisher:Cengage Learning,