Question
Chapter 41, Problem 47P
To determine
To find:
(a) the angle θ between adjacent nearest-neighbor bonds in the silicon lattice.
(b) the bond length in the silicon tetrahedron lattice.
Expert Solution & Answer
Trending nowThis is a popular solution!
Students have asked these similar questions
In solid KCI the smallest distance between the centers of a. potassium ion and a chloride ion is 314 pm. Calculate the length of the edge of the unit cell and the density of KCI, assuming it has the same structure as sodium chloride.
(b) Copper crystallises as FCC (face centred cubic). Given that the atomic radius and density of
a given copper sample are 1.28 x 10-10 m and 8.98 x 10' kg/m' respectively, carry out the following:
(i)
Calculate the mass of the copper sample. Take Avogadro's number, NA = 6.023 x 1023
atoms/mole.
If the interatomic planar spacing, d, in the sample above is 2.96 x 1010 m, determine the angle
at which the first Bragg reflection will occur from the (111) plane if x-radiation of wavelength
1.52 x 10-10 m is used for the analysis.
(ii)
(a) What is the minimum donor doping required to convert silicon into a conductor based on the definitions in Table ? (b) What is the minimum acceptor doping required to convert silicon into a conductor?
Chapter 41 Solutions
FUND.OF PHYSICS (LOOSELEAF) >CUSTOM<
Ch. 41 - Prob. 1QCh. 41 - Prob. 2QCh. 41 - Prob. 3QCh. 41 - Prob. 4QCh. 41 - Prob. 5QCh. 41 - Prob. 6QCh. 41 - Prob. 7QCh. 41 - Prob. 8QCh. 41 - Prob. 9QCh. 41 - Prob. 10Q
Ch. 41 - Prob. 11QCh. 41 - Prob. 1PCh. 41 - Prob. 2PCh. 41 - Prob. 3PCh. 41 - Prob. 4PCh. 41 - Prob. 5PCh. 41 - Prob. 6PCh. 41 - Prob. 7PCh. 41 - Prob. 8PCh. 41 - Prob. 9PCh. 41 - Prob. 10PCh. 41 - Prob. 11PCh. 41 - Prob. 12PCh. 41 - Prob. 13PCh. 41 - Prob. 14PCh. 41 - Prob. 15PCh. 41 - Prob. 16PCh. 41 - Prob. 17PCh. 41 - Prob. 18PCh. 41 - Prob. 19PCh. 41 - Prob. 20PCh. 41 - Prob. 21PCh. 41 - Prob. 22PCh. 41 - Prob. 23PCh. 41 - Prob. 24PCh. 41 - Prob. 25PCh. 41 - Prob. 26PCh. 41 - Prob. 27PCh. 41 - Prob. 28PCh. 41 - Prob. 29PCh. 41 - Prob. 30PCh. 41 - Prob. 31PCh. 41 - Prob. 32PCh. 41 - Prob. 33PCh. 41 - Prob. 34PCh. 41 - Prob. 35PCh. 41 - Prob. 36PCh. 41 - Prob. 37PCh. 41 - Prob. 38PCh. 41 - Prob. 39PCh. 41 - Prob. 40PCh. 41 - Prob. 41PCh. 41 - Prob. 42PCh. 41 - Prob. 43PCh. 41 - Prob. 44PCh. 41 - Prob. 45PCh. 41 - Prob. 46PCh. 41 - Prob. 47PCh. 41 - Prob. 48PCh. 41 - Prob. 49PCh. 41 - Prob. 50PCh. 41 - Prob. 51PCh. 41 - Prob. 52PCh. 41 - Prob. 53P
Knowledge Booster
Similar questions
- (b) Describe the nature and origin of various forces existing between the atoms of a crystal. Explain the formation of a stable bond using the potential energy versus interatomic distance curve. Assume that the potential energy of two particles in the field of each other is given by U(R) = - R where A and B are constants. R9 (i) Show that the particles form a stable compound for R= R. = (9B/A)/8 (R, is equilibrium separation) i) Show that for stable configuration, the energy of attraction is nine times the energy of repulsion. 8A (iii) Show that the potential energy of the system under stable configuration is 9Rearrow_forwardHcp structure . Show that the c/a ratio for an ideal hexagonal close- packed structure is (8/3)^1/2 = 1.633 . if c/a is significantly larger than this value , the crystal structure may be thought of as composed of planes of closely packed atoms, the planes being loosely stacked.arrow_forward3. (a) One way of treating the vibrational modes of a linear diatomic solid is to assume that the atoms have the same masses, but the springs on either side of an atom have spring constants K and G, respectively. Show that the dispersion relation of such a lattice is given by (K+G` +G)' - 4KGsin ka M where M is the mass of the ion, G and K the lattice constants, a is the periodic distance between masses and k the lattice wave vector. (i) (ii) Sketch the dispersion relation Discuss what happens when K = G and K >> G. (b) In diatomic (linear) lattice, why do we assume same o and k.arrow_forward
- A Si p- n junction with cross sectional area A= 0.01cm? is formed with N3=2x1017 cm3, Na= 1017cm3. Calculate: a) contact potential b) the depletion region width and c) the junction capacity at 0 and -2 Volts.arrow_forward(a) Based on a typical bond energy of 150 kBT and a typicalbond length of 0.15 nm, use dimensional analysis toestimate the frequency of vibration of covalent bonds.(b) Assume that the Lennard–Jones potential given byV(r)=a/r^12 -b/r^6describes a covalent bond (though real covalent bonds aremore appropriately described by alternatives such as theMorse potential that are not as convenient analytically).Using the typical bond energy as the depth of the potentialand the typical bond length as its equilibrium position, findthe parameters a and b. Do a Taylor expansion around thisequilibrium position to determine the effective springconstant and the resulting typical frequency of vibration.(c) Based on your results from (a) and (b), estimate the timestep required to do a classical mechanical simulation ofprotein dynamics.arrow_forwardSilicon is doped with 3×1018 arsenic atoms/cm3 and 8 × 1018 boron atoms/cm3. (a) Is this n- or p-type silicon? (b) What are the hole and electron concentrations at room temperature?arrow_forward
- (b) Copper crystallises as FCC (face centred cubic). Given that the atomic radius and density of a given copper sample are 1.28 x 1010 m and 8.98 x 10' kg/m' respectively, carry out the following: Calculate the mass of the copper sample. T'ake Avogadro's number, NA = 6.023 x 1023 atoms/mole. (i) (ii) If the interatomic planar spacing, d, in the sample above is 2.96 x 1010 m, determine the angle at which the first Bragg reflection will occur from the (111) plane if x-radiation of wavelength 1.52 x 10-10 m is used for the analysis. (c) Give two uses of pure copper and two commercial applications of copper alloys.arrow_forward(a) What maximum light wavelength will excite an electron in the valence band of diamond to the conduction band? The energy gap is 5.50 eV. (b) In what part of the electromagnetic spectrum does this wavelength lie?arrow_forwardSet up the relevant equations with estimates of all missing parameters. The molecular bond (spring constant) of HCl is about 470 N/m. The moment of incrtia is 2.3 x 10-47 kg-m². (a) At 300 K what is the probability that the molecule is in its lowest excited vibrational state? (c) Of the molecules in the vibrational ground state what is the ratio of the number in the gronnd rotational state to the number in the first excited rotational state?arrow_forward
- The density of solid KCl is about 1980 kg/m3. Compute the nearest-neighbor distance in KCl, that is, the distance between neighboring K+ and Cl- ions. Note that KCl has the same lattice structure as NaCl.arrow_forwardConsider a three-dimensional crystalline lattice formed of Cu and Zn atoms. The Cu atoms form a simple cubic lattice with the lattice constant a. The Zn atoms are at the center of the cube. a) Write down the structure factor S, associated with the reciprocal lattice vector G = vib1 + vzb2 + v3b3 in terms of the atomic form factors f and f, b) If Cu and Zn atoms randomly occupy every lattice site, then the form factor associated with every lattice site can be assumed to be the same, namely the average of the two form factors. Which Bragg spots will vanish in this case?arrow_forwardThe parameters o and & in Lennard-Jones potential in Argon (Ar) crystals are o = 3.40 x 10-10 m and ɛ = 1.67 x 10-21 J. The lattice sums for the BCC (body-centered cubic) structures are E C" Pī12 = 9.11418, ECC Pī = 12.2533, and the lattice sums for the FCC structures are 2CC Pī12 = potential, calculate the equilibrium separation and cohesive energies (in unit of electron voltage or eV) for BCC and FCC configurations. -6 %3| 12.13188, ECC Pi = 14.45392. Using the Lennard-Jones %3Darrow_forward
arrow_back_ios
arrow_forward_ios
Recommended textbooks for you
- Modern PhysicsPhysicsISBN:9781111794378Author:Raymond A. Serway, Clement J. Moses, Curt A. MoyerPublisher:Cengage Learning
Modern Physics
Physics
ISBN:9781111794378
Author:Raymond A. Serway, Clement J. Moses, Curt A. Moyer
Publisher:Cengage Learning