Textbook Question
Chapter 7, Problem 7.28QP
Students in the materials class prepared three 4″ × 8″ concrete cylinders with water–cement ratios of 0.50, 0.55, and 0.60, respectively. After curing for 7 days, the specimens were subjected to increments of compressive loads. The load versus deformation results were as shown in Table P7.28.
Assuming that the gauge length is the whole specimen height, determine the following:
- a. The compressive stresses and strains for each specimen at each load increment.
TABLE P7.28
Specimen No. | w/c Ratio | Load (kips) | Deformation (in.) | Stress (psi) | Strain (in./in.) | Secant Modulus (psi) |
1 | 0.50 | 0 | 0 | |||
1 | 5.77E-05 | |||||
5 | 2.89E-04 | |||||
10 | 5.77E-04 | |||||
15 | 8.66E-04 | |||||
2 | 0.55 | 0 | 0 | |||
1 | 4.88E-05 | |||||
5 | 2.90E-04 | |||||
10 | 6.20E-04 | |||||
15 | 1.09E-03 | |||||
3 | 0.60 | 0 | 0 | |||
1 | 5.30E-05 | |||||
5 | 3.08E-04 | |||||
10 | 7.62E-04 | |||||
15 | 1.48E-03 |
- b. Plot stresses versus strains for each specimen on one graph.
- c. If the ultimate stress is 3000, 2500 and 2000 psi at 0.50, 0.55 and 0.60, respectively, determine modulus of elasticity as the secant modulus at 40% of the ultimate stress at each water-cement ratio.
- d. Comment on the effect of increasing the water-cement ratio on the modulus of elasticity.
Expert Solution & Answer
![Check Mark](/static/check-mark.png)
Learn your wayIncludes step-by-step video
![Blurred answer](/static/blurred-answer.jpg)
schedule09:14
Students have asked these similar questions
Three 150 mm * 300 mm concrete cylinders with water to cement ratios of 0.4, 0.6, and 0.8, respectively. After curing for 28 days, the specimens were subjected to increments of compressive loads until failure. The load versus deformation results were as shown in Table .Assuming that the gauge length is the whole specimen height, it is required to do the following:a. The compressive stresses and strains for each specimen at each load increment.b. Plot stresses versus strains for all specimens on one graph.c. The ultimate strength for each specimen.d. The modulus of elasticity as the secant modulus at 40% of the ultimate stress for each specimen. e. The strain at failure for each specimen.f. The toughness for each specimen. g. Comment on the effect of increasing the water–cement ratio on the following:i. Ultimate strengthii. Modulus of elasticityiii. Ductilityiv. Toughness. Curves may be approximated with a series of straight lines.
Three 6 in. * 12 in. concrete cylinders with water to cement ratios of 0.4, 0.6,and 0.8, respectively. After curing for 28 days, the specimens were subjected to increments of compressive loads until failure. The load versus deformation results were as shown in Table .Assuming that the gauge length is the whole specimen height, it is required todo the following:a. The compressive stresses and strains for each specimen at each loadincrement.b. Plot stresses versus strains for all specimens on one graph.c. The ultimate strength for each specimen.d. The modulus of elasticity as the secant modulus at 40% of the ultimatestress for each specimen.e. The strain at failure for each specimen.f. The toughness for each specimen.g. Comment on the effect of increasing the water–cement ratio on thefollowing:i. Ultimate strengthii. Modulus of elasticityiii. Ductilityiv. Toughness. Curves may be approximated with a series of straight lines.
4. The state of two dimensional stress acting on a concrete lamina consists of a direct tensile
stress of 6 MPa and shear stress of 4 MPa, which cause cracking of concrete. Then what
will be the tensile strength of the concrete in MPa.?
Chapter 7 Solutions
EBK MATERIALS FOR CIVIL AND CONSTRUCTIO
Ch. 7 - The design engineer specifies a concrete strength...Ch. 7 - A project specifies a concrete strength of 24.1...Ch. 7 - A project specifies a concrete strength of at...Ch. 7 - What is your recommendation for the maximum size...Ch. 7 - A concrete mix with a 3-in. slump, w/c ratio of...Ch. 7 - Prob. 7.6QPCh. 7 - You are working on a concrete mix design that...Ch. 7 - Design the concrete mix according to the following...Ch. 7 - Design the concrete mix according to the following...Ch. 7 - The design of a concrete mix requires 1173 kg/m3...
Ch. 7 - Prob. 7.11QPCh. 7 - Prob. 7.12QPCh. 7 - Students in the materials lab mixed concrete with...Ch. 7 - Students in the materials lab mixed concrete with...Ch. 7 - Why is it necessary to measure the air content of...Ch. 7 - What do we mean by curing concrete? What will...Ch. 7 - Discuss five different methods of concrete curing.Ch. 7 - Draw a graph showing the typical relation between...Ch. 7 - Why is extra water harmful to fresh concrete, but...Ch. 7 - Discuss the change in volume of concrete at early...Ch. 7 - Discuss the creep response of concrete structures....Ch. 7 - Prob. 7.22QPCh. 7 - On one graph, draw a sketch showing the typical...Ch. 7 - Using Figure 7.34, a. Determine the ultimate...Ch. 7 - Three concrete mixes with the same ingredients,...Ch. 7 - Three concrete mixes with the same ingredients,...Ch. 7 - Three 100 mm 200 mm concrete cylinders with water...Ch. 7 - Students in the materials class prepared three 4 ...Ch. 7 - Three 150 mm 300 mm concrete cylinders with water...Ch. 7 - Three 6 in. 12 in. concrete cylinders with water...Ch. 7 - A normal-weight concrete has an average...Ch. 7 - Discuss the significance of the compressive...Ch. 7 - What is the standard size of PCC specimens to be...Ch. 7 - Prob. 7.34QPCh. 7 - What is the purpose of performing the flexure test...Ch. 7 - What are the advantages of using a third-point...Ch. 7 - Consider a standard flexural strength specimen of...Ch. 7 - To evaluate the effect of a certain admixture on...Ch. 7 - To evaluate the effect of a certain admixture on...Ch. 7 - Prob. 7.40QPCh. 7 - Prob. 7.41QPCh. 7 - A normal-weight concrete has an average...Ch. 7 - Three batches of concrete were prepared using the...Ch. 7 - Three batches of concrete were prepared using the...Ch. 7 - Prob. 7.45QPCh. 7 - Prob. 7.46QPCh. 7 - Discuss two nondestructive tests to be performed...Ch. 7 - Discuss the concept of concrete maturity meters.Ch. 7 - Discuss four alternatives that increase the use...Ch. 7 - What is self-consolidating concrete? How are its...Ch. 7 - Prob. 7.51QPCh. 7 - Two 6 in. 12 in. concrete cylinders with randomly...Ch. 7 - Discuss the concept of high-performance concrete....Ch. 7 - Comparing PCC with mild steel, answer the...Ch. 7 - Prob. 7.55QP
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
Using the data shown in Figure 2.5 determine the probability that the tangent of the friction angle for the mud...
Foundation Design: Principles and Practices (3rd Edition)
What is an object? What is a control?
Starting Out With Visual Basic (8th Edition)
Describe a method that can be used to gather a piece of data such as the users age.
Web Development and Design Foundations with HTML5 (8th Edition)
Define each of the following terms: supertype subtype specialization entity cluster completeness constraint enh...
Modern Database Management (12th Edition)
Corporate Sales A corporation has six divisions, each responsible for sales to different geographic locations. ...
Starting Out with C++ from Control Structures to Objects (9th Edition)
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- QI- A concrete cylindrical specimen 155 mm in diameter and 290 mm long is subjected to compressive loading up to failure. The following data shown in table below are obtained. Draw the stress- strain curve and determine: i) the concrete strength. ii) Initial Tangent Modulus. iii) Modulus of Elasticity. Iv) Secant Modulus at 90% of strength and v) State which type of stress strain behavior is this. Load, kN Deformation, mm×10* (Load - 8x16) (Deformation x 0.5x16) 222.5 103 413.1 206 635.2 324 730.4 378 856.1 432 953.6 486 1080.7 540 1171.2 756 1270.0 1025 1396.3 1395arrow_forwardThree 6 in. * 12 in. concrete cylinders with randomly oriented steel fiber contents of 0, 2, and 3% by weight, respectively. After curing for 28 days,the specimens were subjected to increments of compressive loads until failure. The load versus deformation results were as shown in Table .Assuming that the gauge length is the whole specimen height, determine thefollowing:a. The compressive stresses and strains for each specimen at each loadincrement.b. Plot stresses versus strains for all specimens on one graph.c. The modulus of elasticity for each specimen.d. The ultimate strength for each specimen.e. The strain at failure for each specimen.f. Toughness. Curves may be approximated with a series of straight lines g. Comment on the effects of increasing the fiber content on the following:i. Modulus of elasticityii. Ultimate strengthiii. Ductilityiv. Toughnessarrow_forward2. In a ready-mix concrete plant, cylindrical samples are prepared and tested periodically to detect any mix problem and to ensure that the compressive strength is higher than the lower specification limit. The minimum target value was set at 5,000 psi. The following compressive strength data were collected. Sample No. 1 2 3 4 5 6 7 8 9 10 Compressive strength (psi) 5595 5139 6359 5192 5188 5241 5964 5875 6155 5115 Sample No. 11 12 13 14 15 16 17 18 19 20 Compressive strength (psi) 6695 5449 5278 6697 5195 6021 5320 5657 6595 5235 a. Calculate the mean, standard deviation, and the coefficient of variation of the data b. Using a spreadsheet program, create a control chart for these data showing the target value and the lower specification limit. Is the plant production meeting the specification requirement? If not, comment on possible reasons. Comment on the data scatter.arrow_forward
- A center point loading is used to test concrete for flexure. The sample is 150mm x 150mm and has a clear span of 600mm. The sample failed when the load applied is 100,000N. What is the flexure stress at failure in MPa?arrow_forward! Three 150 mm x 300 mm concrete cylinders with randomly oriented steel fiber contents of 0, 2, and 3% by weight, respectively. After curing for 28 days, the specimens were subjected to increments of compressive loads until fail- ure. The load versus deformation results were as shown in Table P11.14. TABLE P11.14 Specimen No. Fiber Content (%) 1 2 3 2 Deformation (mm) Load (kN) 0.31 565 565 565 0.61 716 (failure) 756 792 0.91 641 756 1.22 440 690 1.52 378 641 1.83 351 (failure) 605 (failure) Assuming that the gauge length is the whole specimen height, determine the following: a. The compressive stresses and strains for each specimen at each load increment. b. Plot stresses versus strains for all specimens on one graph. c. The modulus of elasticity for each specimen. d. The ultimate strength for each specimen. e. The strain at failure for each specimen. f. Toughness. Curves may be approximated with a series of straight lines. g. Comment on the effects of increasing the fiber content on…arrow_forwardA concrete specimen with b = d is supported at both ends 600mm apart. It is tested for flexure strength with load at midspan of 100kN and failed with a flexural stress of 52.083 MPa. What is the dimension b and d of the specimen in mm?arrow_forward
- A 150mm x 300mm long cylindrical concrete specimen was tested for tensile strength. The sample failed when the applied force is 150,000N. What is the splitting tensile strength in MPa?arrow_forwardA concrete test cylinder with a cross-sectional area of 28.3 in squared is to be tested in axial compression. Before loading two marks are scribed on the cylinder precisely 8 in apart (as shown in the figure below) when the load is 40,000 lb the marks are measured and found to be 7.997 in apart determine the E value for this concrete. Assume an approximately linear relationship between stress and strain.arrow_forwardA cylindrical brass specimen having a diameter of 1.10 cm and initial gage length of 4.04 cm is subjected to tensile strength test. The load-deformation values are given in the below table. The final length and final diameter of the specimen were measured as 4.33 cm and 0.92 cm, respectively. Complete the below table and plot true stress-true strain diagram and determine. Yield strength at 0.2 % off-set method. Poisson’s ratio of the material at 135 kN load (assume that there is no volume change) If the material were unloaded from 175 kN, what would be its final length? 1 nm=1*10-9 m, 1 0A=10-10 marrow_forward
- When a specimen of M25 concrete is loaded to a stress level of 12.5 MPa, a strain of 500x10^-6 is recorded. If this load is allowed to stand for a long time, the strain increases to 1000 x 10^-6. In accordance with provisions of IS: 456-2000,considering the long-term effects, the effective modulus of elasticity of the concrete (in MPa) isarrow_forwardThere are 3 factors that may be the cause of the production error in the reinforced concrete element shown in the figure.arrow_forwardA 150mm diameter cylindrical concrete specimen was tested for splitting tensile strength. The splitting tensile stress at failure is 4.14 MPa, what is the applied force in kN? The sample length is 300mmarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Structural Analysis (10th Edition)Civil EngineeringISBN:9780134610672Author:Russell C. HibbelerPublisher:PEARSONPrinciples of Foundation Engineering (MindTap Cou...Civil EngineeringISBN:9781337705028Author:Braja M. Das, Nagaratnam SivakuganPublisher:Cengage Learning
- Fundamentals of Structural AnalysisCivil EngineeringISBN:9780073398006Author:Kenneth M. Leet Emeritus, Chia-Ming Uang, Joel LanningPublisher:McGraw-Hill EducationTraffic and Highway EngineeringCivil EngineeringISBN:9781305156241Author:Garber, Nicholas J.Publisher:Cengage Learning
![Text book image](https://compass-isbn-assets.s3.amazonaws.com/isbn_cover_images/9781337630931/9781337630931_smallCoverImage.jpg)
![Text book image](https://www.bartleby.com/isbn_cover_images/9780134610672/9780134610672_smallCoverImage.gif)
Structural Analysis (10th Edition)
Civil Engineering
ISBN:9780134610672
Author:Russell C. Hibbeler
Publisher:PEARSON
![Text book image](https://www.bartleby.com/isbn_cover_images/9781337705028/9781337705028_smallCoverImage.gif)
Principles of Foundation Engineering (MindTap Cou...
Civil Engineering
ISBN:9781337705028
Author:Braja M. Das, Nagaratnam Sivakugan
Publisher:Cengage Learning
![Text book image](https://www.bartleby.com/isbn_cover_images/9780073398006/9780073398006_smallCoverImage.gif)
Fundamentals of Structural Analysis
Civil Engineering
ISBN:9780073398006
Author:Kenneth M. Leet Emeritus, Chia-Ming Uang, Joel Lanning
Publisher:McGraw-Hill Education
![Text book image](https://www.bartleby.com/isbn_cover_images/9781337551663/9781337551663_smallCoverImage.gif)
![Text book image](https://www.bartleby.com/isbn_cover_images/9781305156241/9781305156241_smallCoverImage.jpg)
Traffic and Highway Engineering
Civil Engineering
ISBN:9781305156241
Author:Garber, Nicholas J.
Publisher:Cengage Learning
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY