Calculate the acidity and basicity degrees for the slag composed of 56 % SiO2; 18 % FeO; 5 % CaO, 21 % MgO (Molecular Weights; Ca: 40.08, O: 16, Fe: 55.85, Si: 28.08, Mg: 24.3). Examine this result in accordance with viscosity and melting point of that kind of slags. Calculate the amount of Cao that must be added to the slag to increase the basicity value to 1.5 for this slag,

Calculate the acidity and basicity degrees for the slag composed of 56 % SiO2; 18 % FeO; 5 % CaO, 21 % MgO (Molecular Weights; Ca: 40.08, O: 16, Fe: 55.85, Si: 28.08, Mg: 24.3). Examine this result in accordance with viscosity and melting point of that kind of slags. Calculate the amount of Cao that must be added to the slag to increase the basicity value to 1.5 for this slag,

Principles of Modern Chemistry

8th Edition

ISBN:9781305079113

Author:David W. Oxtoby, H. Pat Gillis, Laurie J. Butler

Publisher:David W. Oxtoby, H. Pat Gillis, Laurie J. Butler

Chapter22: Inorganic Materials

Section: Chapter Questions

Problem 9P

See similar textbooks

Similar questions

discuss the importace and methods of solid liquid separation processes of hydro metallurgy
Solutions of Cu (NO3)2, FeCl3, and CaCO3 of the same concentration are added to identical samples of silica sols with a positive charge of counterions. Which of the ions of these electrolytes will cause coagulation of the sol? What electrolyte is needed less?
Properties of Liquids and IMF. Give a brief explanation
With specific reference to Pauling’s rules of crystal chemistry, explain, with the aid of labeled sketches why the polymerization of silicate tetrahedra or borate triangles can (and often does) occur in crystal structures, whereas the extended polymerization of carbonate triangles or sulfate tetrahedra is rare in mineral structures.
The addition of dimethylglyoxime, H2C4H602N2, to a solution containing nickel(Il) ion gives rise to a precipitate: Nickel dimethylglyoxime is a bulky precipitate that is inconvenient to manipulate in amounts greater than 135 mg. The amount of nickel in a type of permanent-magnet alloy ranges between 22% and 38%. Calculate the sample size that should not be exceeded when analyzing these alloys for nickel.
1. "Band structure" of "Hatom chain" and "H mole chain" are drawn as "graphs" and "intermediate process". Describe it in detail.
Can nitrogen fit into the octahedral interstitial site in BCC iron? Justify your answer by calculation. Atomic radius of nitrogen is 0.071nm and lattice parameter of BCC iron is 0.2866 nm
Describe, with using necessary diagrams, the structure and/or microstructure of the following materials and justify their applications based on their properties. Plain carbon steel (0.25% C), as used to make a body panel for a car Duraluminum 2024: as used to make aircraft structures High density polyethylene (HDPE), as used to make non-carbonated drinks containers Silicon carbide, as used in ball type flow control valves Carbon fibre reinforced polymer (CFRP), as used in the construction of high-end automobile racing
1. What are the practical implications of alloying in carbon and alloy steels? 2. Make use of drawings of segments of the Fe-Cr phase diagram to illustrate the reason for the existence offerritic, martensitic and austenitic stainless steels by also noting the influence of specific alloying elementswhere-applicable. .
Which of the following statements regarding soda glass is incorrect? The modifying cations break the tetrahedral silicate network and make it easier to form glass objects Soda glasses are utilized for flat glass and hollow glass products The modifying cations occupy interstitial spaces in the silicate network Soda glasses contains mixtures of alkali and alkaline earth oxides that result in much more stable glasses than alkali silicates alone The modifying cations lower the melting point and increase the viscosity of the glass
Calculate the mass fractions of phases present in an alloy of lead tin with 35% Sn and 65%Pb and at 184° C?
Explain what type of carbonate polymorphs may be present in saw dust derived biochar prepared at 300 degrees?