Textbook Question
Chapter 1, Problem 48QTP
The following data are obtained in tension tests of brass:
Grain size (μm) | Yield stress (MPa) |
15 | 150 |
20 | 140 |
50 | 105 |
75 | 90 |
100 | 75 |
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
The following data are obtained from a tensile test of a copper specimen.
- The load at the yield point is 142 kN.
- Length of the specimen is 23 mm.
- The yield strength is 82 kN/mm2.
- The percentage of elongation is 48 %.
Determine the following
(i) Diameter of the specimen,
ii) Final length of the specimen,
iii) Stress under an elastic load of 15 kN,
iv) Young's Modulus if the elongation is 1.6 mm at 15 kN and
(v) Final diameter if the percentage of reduction in area is 20 %.
Solution
Initial Cross-sectional Area (in mm2)
Answer for part 1
The Diameter of the Specimen (in mm)
Answer for part 2
Final Length of the Specimen (in mm)
Answer for part 3
Stress at the elastic load (in N/mm2)
Answer for part 4
Young's Modulus of the Specimen (in N/mm2)
Answer for part 5
Final Area of the Specimen at Fracture (in mm)
Answer for part 6
Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen.
- The load at the yield point is 146 kN.
- Length of the specimen is 25 mm.
- The yield strength is 83 kN/mm2.
- The percentage of elongation is 40 %.
Determine the following
(i) Diameter of the specimen,
ii) Final length of the specimen,
iii) Stress under an elastic load of 14 kN,
iv) Young's Modulus if the elongation is 1.1 mm at 14 kN and
(v) Final diameter if the percentage of reduction in area is 25 %.
Solution
Initial Cross-sectional Area (in mm2)
Answer for part 1
The Diameter of the Specimen (in mm)
Answer for part 2
Final Length of the Specimen (in mm)
Answer for part 3
Stress at the elastic load (in N/mm2)
Answer for part 4
Young's Modulus of the Specimen (in N/mm2)
Answer for part 5
Final Area of the Specimen at Fracture (in mm)
Answer for part 6
Final Diameter of the Specimen after Fracture (in mm)
Answer for part 7
The following data are obtained from a tensile test of a copper specimen.
- The load at the yield point is 151 kN.
- Length of the specimen is 23 mm.
- The yield strength is 79 kN/mm2.
- The percentage of elongation is 45 %.
Determine the following
(i) Diameter of the specimen,
ii) Final length of the specimen,
iii) Stress under an elastic load of 17 kN,
iv) Young's Modulus if the elongation is 2.4 mm at 17 kN and
(v) Final diameter if the percentage of reduction in area is 24 %.
Find:
1)Stress at the elastic load (in N/mm2)
2)Young's Modulus of the Specimen (in N/mm2)
3)Final Area of the Specimen at Fracture (in mm)
4)Final Diameter of the Specimen after Fracture (in mm)
Chapter 1 Solutions
Manufacturing Engineering And Technology -- Access Card
Ch. 1 - What is the difference between an atom and a...Ch. 1 - Prob. 2RQCh. 1 - Prob. 3RQCh. 1 - Prob. 4RQCh. 1 - Define anisotropy. What is its significance?Ch. 1 - What effects does recrystallization have on the...Ch. 1 - What is strain hardening, and what effects does it...Ch. 1 - Explain what is meant by structure-sensitive and...Ch. 1 - Prob. 9RQCh. 1 - What influence does grain size have on the...
Ch. 1 - What is the relationship between the nucleation...Ch. 1 - What is a slip system, and what is its...Ch. 1 - Explain the difference between recovery and...Ch. 1 - What is hot shortness, and what is its...Ch. 1 - Explain the advantages and limitations of cold,...Ch. 1 - Describe what the orange peel effect is. Explain...Ch. 1 - Some metals, such as lead, do not become stronger...Ch. 1 - Describe the difference between preferred...Ch. 1 - Differentiate between stress relaxation and stress...Ch. 1 - What is twinning? How does it differ from slip?Ch. 1 - Prob. 21QLPCh. 1 - What is the significance of the fact that some...Ch. 1 - Is it possible for two pieces of the same metal to...Ch. 1 - Prob. 24QLPCh. 1 - A cold-worked piece of metal has been...Ch. 1 - What materials and structures can you think of...Ch. 1 - Two parts have been made of the same material, but...Ch. 1 - Do you think it might be important to know whether...Ch. 1 - Explain why the strength of a polycrystalline...Ch. 1 - Describe the technique you would use to reduce the...Ch. 1 - What is the significance of the fact that such...Ch. 1 - Prob. 32QLPCh. 1 - It has been noted that the more a metal has been...Ch. 1 - Is it possible to cold work a metal at...Ch. 1 - Comment on your observations regarding Fig. 1.14.Ch. 1 - Is it possible for a metal to be completely...Ch. 1 - Prob. 37QTPCh. 1 - Prob. 38QTPCh. 1 - Plot the data given in Table 1.1 in terms of...Ch. 1 - A strip of metal is reduced from 30 mm in...Ch. 1 - Prob. 41QTPCh. 1 - How many grains are there on the surface of the...Ch. 1 - Prob. 43QTPCh. 1 - Prob. 44QTPCh. 1 - Prob. 45QTPCh. 1 - A technician determines that the grain size of a...Ch. 1 - If the diameter of the aluminum atom is 0.28 nm,...Ch. 1 - The following data are obtained in tension tests...Ch. 1 - Prob. 50QTPCh. 1 - Prob. 51QTPCh. 1 - Prob. 52QTPCh. 1 - Same as Prob. 1.39, but ASTM no. versus...Ch. 1 - By stretching a thin strip of polished metal, as...Ch. 1 - Draw some analogies to mechanical fiberingfor...Ch. 1 - Draw some analogies to the phenomenon of hot...Ch. 1 - Take a deck of playing cards, place a rubber band...Ch. 1 - Give examples in which anisotropy is scale...Ch. 1 - The movement of an edge dislocation was described...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 151 kN. - Length of the specimen is 23 mm. - The yield strength is 79 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 17 kN, iv) Young's Modulus if the elongation is 2.4 mm at 17 kN and (v) Final diameter if the percentage of reduction in area is 24 %. THE QUESTION IS : FIND THE Final Diameter of the Specimen after Fracture (in mm)????arrow_forwardThe following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 147 kN. - Length of the specimen is 28 mm. - The yield strength is 75 kN/mm2. - The percentage of elongation is 49 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 16 kN, iv) Young's Modulus if the elongation is 1 mm at 16 kN and (v) Final diameter if the percentage of reduction in area is 22 Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm) Initial Cross-sectional Area (in mm2)arrow_forwardDraw a typical stress vs strain tensile test curve for the following materials (two seperate graphs) and label the axis. A ductile metallic test specimen that is stretched to failure displaying a characteristic yield point and show the following parts on the curve. 1- Yield point 2- Ultimate Tensile Strength 3- Breaking point 4- Elastic Region 5- Plastic Region 6- Necking regionarrow_forward
- The following data was obtained as a result of tensile testing of a standard 0.505 inch diameter test specimen of magnesium. After fracture, the gage length is 2.245 inch and the diameter is 0.466 inch. a). Calculate the engineering stress and strain values to fill in the blank boxes and plot the data. Load(lb) Gage Length (in) Stress (kpsi) Strain 0 2 1000 2.00154 2000 2.00308 3000 2.00462 4000 2.00615 5000 2.00769 5500 2.014 6000 2.05 6200 (max) 2.13 6000 (fracture) 2.255 b). Calculate the modulus of elasticity c). If another identical sample of the same material is pulled only to 6000 pounds and is unloaded from there, determine the gage length of the sample after unloading.arrow_forwardThe following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1.3 mm at 18 kN and Final diameter if the percentage of reduction in area is 25 %. Fine this ans 1-Initial Cross-sectional Area (in mm2) 2-The Diameter of the Specimen (in mm) 3-Final Length of the Specimen (in mm) 4-Stress at the elastic load (in N/mm2) 5-Young's Modulus of the Specimen (in N/mm2) 6-Final Area of the Specimen at Fracture (in mm) 7-Final Diameter of the Specimen after Fracture (in mm)arrow_forwardFor a piece of copper alloy, a standard stress test was applied to it, the following data was collected, from which a stress-strain diagram must be generated, where as data it is known that the initial diameter of the element is 0.505in. The analysis must include the following: 1.Modulus of Elasticity and modulus of resilience. 2.Percentage of elongation. 3.Percentage of area reduction. 4.Real and engineering stress at fracture. It is known that after the specimen fractures, its dimensions in terms of length and diameter are 3.014 and 0.374in, respectively.arrow_forward
- The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 143 kN. - Length of the specimen is 29 mm. - The yield strength is 71 kN/mm2. - The percentage of elongation is 48 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1 mm at 18 kN and Final diameter if the percentage of reduction in area is 29 %. Initial Cross-sectional Area 2.01 mm2. The Diameter of the Specimen 1.59 mm. Final Length of the Specimen 42.92 mm. Stress at the elastic load 8955.22 N/mm2. Find: Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)arrow_forwardThe following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 143 kN. - Length of the specimen is 29 mm. - The yield strength is 71 kN/mm2. - The percentage of elongation is 48 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1 mm at 18 kN and Final diameter if the percentage of reduction in area is 29 %. FIND: Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)arrow_forwardIn a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph.arrow_forward
- In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.arrow_forwardYou are called as an expert witness to analyze the fracture of a sintered silicon carbide plate that was fractured in bending when a blunt load was applied to the plate center. Measurement of the distance between the fracture origin and the mirror/mist boundary on the fracture surface gives a radius of 0.796 mm. You are given three pieces of the same SiC to test, and you determine that the mirror radius is 0.603, 0.203, and 0.162 mm for bending failure stress levels of 225, 368, and 442 MPa, respectively. What is your estimate of the stress present at the time of fracture for the original plate?arrow_forwardThe following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 150 kN. - Length of the specimen is 24 mm. - The yield strength is 78 kN/mm2. - The percentage of elongation is 42 %. Determine the following iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.7 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 26 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY