Chapter 13, Problem 38QTP
Estimate the roll force, F, and the torque for an AISI 1020 carbon-steel strip that is 200 mm wide, 10 mm thick, and rolled to a thickness of 7 mm. The roll radius is 200 mm, and it rotates at 200 rpm.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
A strip (300x30 mm) is fed through a rolling mill with two powered rolls (each with radius of 300 mm) rotating at the speed of 60 rpm. The flow stress of work material is 90 MPa, and the coefficient of friction between rolls and work is 0.12. For a single rolling operation performed at the contact angle of 6.28°, calculate the followings:a) Work thickness after rolling (in mm)
An annealed 4340 steel strip of 300 mm width and 7 mm thickness is rolled to a thickness of 5 mm. The roll radius is 175 mm and rotates at 180 rpm. Calculate the roll force and the power required for the process.
In a rolling operation using rolls of diameter 500 mm, if a 25
mm thick plate cannot be reduced to less than 20 mm in one
Pass, Estimate the coefficient of friction between the roll and the plate.
Chapter 13 Solutions
Manufacturing Engineering And Technology -- Access Card
Ch. 13 - What is the difference between a plate and a...Ch. 13 - Define roll gap, neutral point, and draft.Ch. 13 - What factors contribute to spreading in flat...Ch. 13 - What is forward slip? Why is it important?Ch. 13 - Describe the types of deflections that rolls...Ch. 13 - Describe the difference between a bloom, a slab,...Ch. 13 - Why may roller leveling be a necessary operation?Ch. 13 - List the defects commonly observed in flat...Ch. 13 - What are the advantages of tandem rolling? Pack...Ch. 13 - How are seamless tubes produced?
Ch. 13 - Why is the surface finish of a rolled product...Ch. 13 - What is a Sendzimir mill? What are its important...Ch. 13 - What is the Mannesmann process? How is it...Ch. 13 - Describe ring rolling. Is there a neutral plane in...Ch. 13 - How is back tension generated?Ch. 13 - Explain why the rolling process was invented and...Ch. 13 - Flat rolling reduces the thickness of plates and...Ch. 13 - Explain how the residual stress patterns shown in...Ch. 13 - Explain whether it would be practical to apply the...Ch. 13 - Describe the factors that influence the magnitude...Ch. 13 - Explain how you would go about applying front and...Ch. 13 - What typically is done to make sure that the...Ch. 13 - Make a list of parts that can be made by (a) shape...Ch. 13 - Describe the methods by which roll flattening can...Ch. 13 - It was stated that spreading in flat rolling...Ch. 13 - Flat rolling can be carried out by front tension...Ch. 13 - Explain the consequence of applying too high a...Ch. 13 - Note in Fig. 13.3f that the driven rolls (powered...Ch. 13 - Describe the importance of controlling roll...Ch. 13 - In Fig. 13.9a, if you remove the top compressive...Ch. 13 - Name several products that can be made by each of...Ch. 13 - List the possible consequences of rolling at (a)...Ch. 13 - It is known that in thread rolling, as illustrated...Ch. 13 - If a rolling mill encounters chatter, what process...Ch. 13 - Can the forward slip ever become negative? Why or...Ch. 13 - In Example 13.1, calculate the roll force and the...Ch. 13 - Calculate the individual drafts in each of the...Ch. 13 - Estimate the roll force, F, and the torque for an...Ch. 13 - A rolling operation takes place under the...Ch. 13 - Estimate the roll force and power for annealed...Ch. 13 - A flat-rolling operation is being carried out...Ch. 13 - A simple sketch of a four-high mill stand is shown...Ch. 13 - Obtain a piece of soft, round rubber eraser, such...Ch. 13 - If you repeat the experiment in Problem 13.45 with...Ch. 13 - Design a set of rolls to produce cross-sections...Ch. 13 - Design an experimental procedure for determining...Ch. 13 - Derive an expression for the thickest workpiece...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A metal strip is to be rolled from an initial wrought thickness of 3.5 mm to a final rolled thickness of 2.5 mm in a single pass rolling mill having rolls of 250 mm diameter. The strip is 450 mm wide. The average coefficient of friction in the roll gap is 0.08. Taking plane strain low stress of 140 MPa, for the metal and assuming negligible spreading, the roll separating force is.....arrow_forwardA 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a rolling operation. As the thickness is reduced, the plate widens by 3%. The entrance speed of the plate is 13 m/min and the roll radius is 310 mm with a rotational speed of 30 rpm. To do 5.1 If the final width of the sheet is 200 mm, calculate the required roll force. 5.2. Explain what is roll flattening, its effects and how it can be reduced.arrow_forwardA copper strip of 200 mm width and 300 mm thickness is to be rolled to a thickness of 295 mm The roll of radius 300 mm rotates at 100 rpm. The average shear strength of the work material is 180 MPa. Calculate the roll strip contact length and the roll force .arrow_forward
- In a rolling operation using a roll of diameter 1.5 m, if a 35 mm thick plate cannot be reduced to less than 12 mm in a single pass then calculate the coefficient of friction btween the rolls and the plate.arrow_forwardA 300 mm thick slab is being cold rolled using roll of 600 mm diameter. If the coefficient of friction is 0.08, the maximum possible reduction is,arrow_forwardA 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a rolling operation. As the thickness is reduced, the plate widens by 3%. The entrance speed of the plate is 13 m/min and the roll radius is 310 mm with a rotational speed of 30 rpm. 5.1 Calculate the minimum coefficient of friction required, that will make the rolling operation possible. 5.2 Calculate the exit velocity of the plate. 5.3 Calculate the forward slip. 5.4 If the final width of the sheet is 200 mm, calculate the required roll force. 5.5 Explain what is roll flattening, its effects and how it can be reduced.arrow_forward
- A solid cylindrical work piece is reduced in height by an open die forging process using flat dies on a mechanical press, powered by a 20 kW motor which operates at 35 strokes per minute with a stroke length of 160 mm. The work piece is 60 mm high and 100 mm in diameter and is to be reduced in height by 15%. The coefficient of friction during the operation is 0,18. Calculate the flow stress of work piece material if the press is set to operate at 90% of its maximum capacity.arrow_forwardA 300mm thick slab is being cold rolled using roll of 600mm diameter.If the coefficient of friction is 0.08. Determine the maximum possible reduction.arrow_forward1. A round wire made from 1020 carbon steel is being drawn from a diameter of 12.5 mm to 9.5 mm in a draw die of 10°. For a coefficient of friction of 0.15, calculate required drawing force. 2. How would the extrusion process be effected if the die angle is increased?arrow_forward
- An aluminium strip with a cross section of 200 mm × 8 mm is being rolled with 25% reduction of area, using 400 mm diameter steel rolls. The tensile yield stress of aluminium is 0.28 kN/mm2. Calculate i) The angle subtended by the deformation zone at the roll center. ii) The minimum coefficient of friction between the workpiece and the rolls for an unaided bite to be possible.arrow_forwardCalculate the bite angle when rolling plates 12 mm thick using work rolls 600 mm diameter and reducing the thickness by 3 mm.arrow_forwardA strip with cross section 120 X 6 mm is being rolled with 20 % reduction area, using rolls of 400mm diameter the coefficient of friction is 0.1 Determine the final strip thickness the angle of bite, length of deformation zonearrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Types of Manufacturing Process | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=koULXptaBTs;License: Standard Youtube License