Chapter 14, Problem 64RQ
To determine
The role of chaplets and importance of not melting the chaplets completely during pouring and the solidification of casting.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
what solidification time is required for a casting of 9.5 cm3 and a mold contact area of 10 cm2? The mold constant is 838 s/cm2.
A cylinder with a diameter of 40 mm and height of 80 mm solidifies in 3 minutes in a sand casting operation. What is the solidification time if the cylinder height is doubled? What is the time if the diameter is doubled?
Explain the working of principles of the die casting process which is most preferred of the high production rate?
Chapter 14 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 14 - What are some of the factors that influence the...Ch. 14 - What are the three basic categories of casting...Ch. 14 - What metals are frequently cast into products?Ch. 14 - What features combine to make cast iron and...Ch. 14 - Which type of casting is the most common and most...Ch. 14 - Prob. 6RQCh. 14 - Prob. 7RQCh. 14 - What is the simplest and least expensive type of...Ch. 14 - What is a match plate, and how does it aid...Ch. 14 - How is a cope-and-drag pattern different from a...
Ch. 14 - Prob. 11RQCh. 14 - Prob. 12RQCh. 14 - For what types of products might a loose-piece...Ch. 14 - What are the four primary requirements of molding...Ch. 14 - Prob. 15RQCh. 14 - Prob. 16RQCh. 14 - What is a muller, and what function does it...Ch. 14 - Prob. 18RQCh. 14 - What is a standard rammed specimen for evaluating...Ch. 14 - What is permeability, and why is it important in...Ch. 14 - How does the ratio of water to clay affect the...Ch. 14 - How is the hardness of molding sand determined?Ch. 14 - Prob. 23RQCh. 14 - How does the size and shape of the sand grains...Ch. 14 - Prob. 25RQCh. 14 - Prob. 26RQCh. 14 - Prob. 27RQCh. 14 - Prob. 28RQCh. 14 - Prob. 29RQCh. 14 - Prob. 30RQCh. 14 - What are hot tears, and what can cause them to...Ch. 14 - When might hand ramming be the preferred method of...Ch. 14 - Prob. 33RQCh. 14 - Prob. 34RQCh. 14 - Prob. 35RQCh. 14 - Prob. 36RQCh. 14 - What is stack molding?Ch. 14 - Prob. 38RQCh. 14 - What are the components of green sand?Ch. 14 - Prob. 40RQCh. 14 - Prob. 41RQCh. 14 - Prob. 42RQCh. 14 - What are some of the advantages and limitations of...Ch. 14 - Prob. 44RQCh. 14 - Prob. 45RQCh. 14 - Prob. 46RQCh. 14 - Prob. 47RQCh. 14 - Prob. 48RQCh. 14 - Prob. 49RQCh. 14 - Why do shell molds have excellent permeability and...Ch. 14 - Prob. 51RQCh. 14 - Prob. 52RQCh. 14 - Prob. 53RQCh. 14 - Prob. 54RQCh. 14 - Prob. 55RQCh. 14 - What is the sand binder in the core-oil process,...Ch. 14 - What is the binder in the hot-box core-making...Ch. 14 - What is the primary attraction of the cold-box...Ch. 14 - What is shelf life? How is it different from bench...Ch. 14 - Prob. 60RQCh. 14 - Prob. 61RQCh. 14 - Prob. 62RQCh. 14 - Prob. 63RQCh. 14 - Prob. 64RQCh. 14 - Prob. 65RQCh. 14 - Why are plaster molds only suitable for the...Ch. 14 - How does the Antioch process provide permeability...Ch. 14 - What is the primary performance difference between...Ch. 14 - Prob. 69RQCh. 14 - Prob. 70RQCh. 14 - Prob. 71RQCh. 14 - Describe the progressive construction of an...Ch. 14 - Why are investment casting molds generally...Ch. 14 - Prob. 74RQCh. 14 - What are some of the attractive features of...Ch. 14 - What recent development has made one-of-a-kind or...Ch. 14 - Prob. 77RQCh. 14 - Prob. 78RQCh. 14 - What are some of the benefits of not having to...Ch. 14 - What are some of the ways by which expanded...Ch. 14 - Prob. 81RQCh. 14 - Prob. 82RQCh. 14 - Prob. 83RQCh. 14 - Prob. 84RQCh. 14 - Prob. 85RQCh. 14 - Prob. 86RQCh. 14 - What are the most common single-use mold...Ch. 14 - What are the most common methods of core...Ch. 14 - Although cores increase the cost of castings, they...Ch. 14 - Several of the additive manufacturing processes...Ch. 14 - Additive manufacturing processes can also build...Ch. 14 - Cast iron cookware can offer a number of...Ch. 14 - Figure CS-14 shows the hitch ball component of a...Ch. 14 - Prob. 2.1CSCh. 14 - Prob. 2.2CSCh. 14 - Prob. 2.3CS
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A 5 cm cube solidifies in 4.6 min. Assume n=2. Calculate (a) the mold constant in Chvorinov’s rule and (b) the solidification time for a 1.25 cm X 12.5 cm X 15 cm bar cast under the same conditionsarrow_forwardOn the continuous growth, Calculate the interfacial undercooling if the melting temperature is 600 K and the latent heat of melting is given as 30 kJ/kg? (Assume the driving force for solidification as 45 kJ/kg?arrow_forwardHow can density effect in sand casting operation and how we can plan an experiment to see the effect ?arrow_forward
- . A round casting is 0.2 m in diameter and 1 m in length. Another casting of the same metal iselliptical in cross section, with a major-to-minor axis ratio of 2, and has the same length andcross sectional area as the round casting. Both pieces are cast under the same conditions.What is the difference in the solidification times of the two castings?arrow_forwardwhat are molten metal problems in a casting rocess ?why do those occur?arrow_forwardWhich ingot has greater mechanical resistance? Why? Explain in detail what occurred during solidification.arrow_forward
- In turbine blade casting, how is a single-crystal structure achieved? Select one or more: a. By using a curving coil-like channel in the casting mould b. By removing grain boundaries by hot working and recrystallisation c. By careful control of the temperatures of the mould d. By introducing impurities into the molten alloy in the mouldarrow_forwardA riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.arrow_forwardWhich one is better for the casting structure (a) and (b) in the following figures? Why?arrow_forward
- Is it possible to manufacture a propeller of a commercial-scale heavy-duty ship using the Investment Casting Process? Briefly support your explanation with reasoning if it is not possible.arrow_forwardQ#3: Explain in detail different components of a gating system in sand mold castingarrow_forwardA slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Explanation of Solidification of Metals & Alloys | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=G5z9KknF_s8;License: Standard Youtube License