A part made from annealed AISI 1018 steel undergoes a 20 percent cold-work operation.
- a) Obtain the yield strength and ultimate strength before and after the cold-work operation. Determine the percent increase in each strength.
- b) Determine the ratios of ultimate strength to yield strength before and after the cold-work operation. What does the result indicate about the change of ductility of the part?
(a)
The yield strength if annealed AISI 1018 steel undergoes a 20 percent cold-work operation.
The ultimate strength if annealed AISI 1018 steel undergoes a 20 percent cold-work operation.
The percentage increase in yield strength.
The percentage increase in ultimate strength.
Answer to Problem 9P
The yield strength if annealed AISI 1018 steel undergoes a 20 percent cold-work operation is
The ultimate strength if annealed AISI 1018 steel undergoes a 20 percent cold-work operation
The percentage increase in yield strength is
The percentage increase in ultimate strength is
Explanation of Solution
Write the expression for work load factor and area.
Here, the original area is
Write the expression for true strain.
Here, the true strain is
Calculate the new yield strength after cold work.
Here, the new yield strength is
Calculate the new ultimate strength after cold work.
Here, the new ultimate strength after clod work is
Calculate the percentage increase in yield strength.
Here, the percentage increase in yield strength is
Calculate the percentage increase in ultimate strength.
Here, the percentage increase in ultimate strength is
Conclusion:
Refer to Table A-22 “Results of Tensile Test of Some Metals” for annealed AISI 1018 steel.
Obtain the yield strength as
The steel undergoes
Substitute
Substitute
Substitute
Thus, the yield strength is
Substitute
Thus, the percentage increase in yield strength is
Substitute
Thus, the ultimate strength is
Substitute
Thus, the percentage increase in ultimate strength is
(b)
The ratio of ultimate and yield strength before cold-work operation.
The ratio of ultimate and yield strength after cold-work operation and explain the ductility of part with the help of result.
Answer to Problem 9P
The ratio of ultimate and yield strength before cold-work operation is
The ratio of ultimate and yield strength after cold-work operation is
Explanation of Solution
Calculate the ratio of ultimate strength to yield strength before cold work.
Here, the ratio of ultimate strength to yield strength is
Calculate the ratio of ultimate strength to yield strength after cold work.
Here, the ratio of ultimate strength to yield strength after cold work is
Conclusion:
Substitute
Thus, the ratio of ultimate strength to yield strength before cold work is
Substitute
Thus, the ratio of ultimate strength to yield strength after cold work is
From the calculated value of
Want to see more full solutions like this?
Chapter 2 Solutions
Shigley's Mechanical Engineering Design (McGraw-Hill Series in Mechanical Engineering)
- Using the graphs in Figures for Q2 (b) & (c), select a metal alloy for an application that requires a tensile strength of at least 370 MPa while maintaining a minimum ductility of 27%. If the metal may be cold worked, decide which of the following is a suitable material; copper, brass or 1040 steel. You need to explain your selection process.arrow_forwardIn the flow curve for pure aluminum, the strength coefficient = 175 MPa and strain-hardening exponent = 0.20. In a forming operation, the final true strain = 0.75. Determine a) the flow stress and b) average flow stress that the metal experienced.arrow_forwardDraw a Stress/Strain graph of a mild tensile steel and identify the limit of proportionality and the yield pointarrow_forward
- A low-carbon steel alloy was loaded in tension until just after yielding took place. A few Luders bands were visible on the surface. The bar can either be reloaded (a) immediately, (b) after a brief and moderate temperature aging treatment, or (c) after several weeks without any exposure to elevated temperature. In each of the three cases, how is the yield strength of the reloaded bar likely to compare to that of the original test?arrow_forwardUsing various tables, determine the specific strength (yield strength-to-density ratio) in unit of kN⋅m/kg for AISI 1015 hot-rolled steel, 7075-T6 aluminum alloy, Ti-0.2 Pd titanium alloy, and ASTM No. 60 gray cast iron.arrow_forwardThere is a disagreement about a spring steel failure and you, as an independent material scientist, were asked to clarify the issue that whether the failure was originated from improper application or flaw. How can you clarify the issue?arrow_forward
- 1)On a stress strain curve for structural steel, show various points like proportional limit, elastic limit, ultimate strength and rupture point. Give a brief description of these points. 2)How to determine the yield point for materials that do not exhibit a well defined yield point? Name some of such materials. 3)What is allowable load/stress. Give two different equations that determine the allowable load/stressarrow_forwardA 2.0-inch diameter 4140 steel bar is austenized and tempered in oil without Agitation, determine the resulting hardness at 0.6 inches below the surface, present all the Procedure to arrive at the answer (include sketch of the piece and graph used with steps Using word forms)arrow_forwardA metal sample on a tension in the test, , a tensile true strain 0.08, and true stress when the strain is 0.27. Determine the strength coefficient and strain hardening exponent in the flow curve equation.arrow_forward
- Determine the yield strength sy and the ultimate strength su of the A36 steel either from Materials Science class book/notes, or by researching over the internet.arrow_forwardHow does the carbon content in plane carbon steels affect the fracture toughness? Show this influence by A7 curves.arrow_forwardQ24. What is toughness of a material? Is it the same as hardness? Is it also measured in pascals? 3 Q25. What is brittle transition temperature? 2 Q26. What is the risk of using steels at temperatures above 350O?arrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY