Textbook Question
Chapter 27, Problem 34QTP
A 0.80-in.-thick copper plate is being machined by wire EDM. The wire moves at a speed of 4 ft/min and the kerf width is
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A slab-milling operation is carried out on a 200 mm long, 80-mm-wide annealed mild-steel workpiece having a feedrate of 0.1 mm/tooth and a depth of cut of 4.0 mm. The cutter of 50 mm diameter has 18 straight teeth and rotates at 135 rpm. The given specific energy for this material is 3.5 W s/mm3 and the slab mill is wider than the workpiece to be machined. Calculate:‧ the material-removal rate;‧ the power and torque required for this operation;‧ the cutting time.
(243 mm/min, 77760 mm3/min, 4.5 kW, 52.8 s)
A shaft of 0.5 m in length and 100cm in diameter is to be machined. What operation will you utilize on lathe to bring the specimen of size 50 cm diameter and 0.25 m length?
A student is using a lathe with 80-hp and 80% efficiency to fabricate a copper alloy with Sy= 1200 ksi. If the width of cut is 0.30 in. and the student set a rake angle of 0° and a cutting speed of 200 ft/ min while she assumed a coefficient of friction to be 0.5. What is the maximum depth of cut the student can achieve?
Chapter 27 Solutions
Manufacturing Engineering And Technology
Ch. 27 - Describe the similarities and differences between...Ch. 27 - Name the processes involved in chemical machining....Ch. 27 - Explain the difference between chemical machining...Ch. 27 - What is the underlying principle of...Ch. 27 - Explain how the EDM process is capable of...Ch. 27 - What are the important features of the Blue Arc...Ch. 27 - What are the capabilities of wire EDM? Could this...Ch. 27 - Explain why laser Microjet has a large depth of...Ch. 27 - Describe the advantages of water-jet machining.Ch. 27 - What is the difference between photochemical...
Ch. 27 - What type of workpiece is not suitable for...Ch. 27 - What is an undercut? Why must it be considered in...Ch. 27 - Explain the principle of hybrid machining.Ch. 27 - Give technical and economic reasons that the...Ch. 27 - Why is the preshaping or premachining of parts...Ch. 27 - Explain why the mechanical properties of workpiece...Ch. 27 - Prob. 17QLPCh. 27 - Prob. 18QLPCh. 27 - Why has electrical-discharge machining become so...Ch. 27 - Prob. 20QLPCh. 27 - Which of the advanced machining processes would...Ch. 27 - Which of the processes described in require a...Ch. 27 - Describe your thoughts regarding the laser-beam...Ch. 27 - Are deburring operations still necessary for some...Ch. 27 - List and explain factors that contribute to a poor...Ch. 27 - What is the purpose of the abrasives in...Ch. 27 - Which of the processes described in this chapter...Ch. 27 - Is kerf width important in wire EDM? Explain.Ch. 27 - Comment on your observations regarding Fig. 27.4.Ch. 27 - Why may different advanced machining processes...Ch. 27 - A 200-mm-deep hole that is 30 mm in diameter is...Ch. 27 - If the operation in Problem 27.31 were performed...Ch. 27 - A cutting-off operation is being performed with a...Ch. 27 - A 0.80-in.-thick copper plate is being machined by...Ch. 27 - Explain why it is difficult to produce sharp...Ch. 27 - Make a list of the processes described in this...Ch. 27 - Would the processes described in this chapter be...Ch. 27 - Prob. 38SDPCh. 27 - Describe your thoughts as to whether the...Ch. 27 - Make a list of machining processes that may be...Ch. 27 - At what stage is the abrasive in abrasive...Ch. 27 - Describe the similarities and differences among...Ch. 27 - Describe the similarities and differences among...Ch. 27 - Describe any workpiece size limitations in...Ch. 27 - Suggest several design applications for the types...Ch. 27 - Based on the topics covered in Parts III and IV,...Ch. 27 - Review Example 27.1 and explain the relevant...Ch. 27 - Precision engineering is a term that is used to...Ch. 27 - With appropriate sketches, describe the principles...Ch. 27 - Make a table of the process capabilities of the...Ch. 27 - One of the general concerns regarding advanced...Ch. 27 - It can be seen that several of the processes...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A motorised metal guillotine machine is required to cut 45 mm diameter hole in a plate of 20 mm thickness at rate of 35 holes per minute. It requires a torque of 7 Nm for an area of hole in mm2. If the cutting takes 1/10 of a second and the speed of its flywheel varies from 165 rpm to 145 rpm, calculate:arrow_forwardNote: Read the question carefully and give me right solutions according to the question. In orthogonal cutting of steel tube of 150 mm diameter and 2 mm thick, the cutting force was 130 kg and feed force was 35 kg for chip thickness of 0.3mm. The orthogonal cut was taken at 60 meter per minute with a feed of 0.14 mm/rev. If the back rack angle of the cutting tool was - 8 o (minus 8 degree), then calculate the shear strain and strain energy per unit volume.arrow_forwardA 78 mm thick plate is to be milled down to a thickness of 60 mm using an 80 mm face milling cutter. Calculate the processing time if the cutting depth is 6 mm, the feed/rev is 1.1 mm and the cutting speed is 15 m/min, and if the over run for a 620 mm long plate is 10 mm.arrow_forward
- a rod is to be manufactured using turning operations and is made of Nickel alloy. The rod is 80 mm in length and 15 mm in diameter. The final required diameter is 10 mm and the spindle rotates at N = 500 rpm while the tool axial speed is 100 mm/ min. Calculate material removal rate, cutting speed, cutting time, the power dissipated, and cutting force.arrow_forwardIn a turning operation, cutting speed =200 m/min; feed = 0.25mm mm/rev, and depth of cut = 4.00mm Thermal diffusivity of the work material = 20m mm^2/s and volumetric specific heat =3.5(10^ -3 )J/mm^ 3 -C If the temperature increase above ambient temperature (20degreesC) is the angle measured by a tool-chip thermocouple to be 700degreesC, determine the specific energy for the work material in this operation.arrow_forwardDraw the forces and angles involved in the cutting process and calculate shear angle (0), friction coefficient and tangential force if ,cutting force = 80 kN, resultant of forces =100kN, friction force=75kN, rake angle =20° undeformed chip thickness = 0.65mm and deformed chip thickness = 0.72mmarrow_forward
- A mild steel block of width 40 mm is being milled using a straight slab cutter 70 mm diameter with 30 teeth. If the cutter rotates at 40 rpm, and depth of cut is 2 mm, what is the value of maximum uncut chip thickness when the table feed is 20 mm/min?arrow_forwardcalculate the time taken to complete a 300 mm long cut on an aluminium plate using a 75 mm diameter slab mill with 6 teeth.arrow_forwarda) Define specific energy for plane strain machining (cutting). b) In plane-strain orthogonal machining, the two main sources of energy dissipation are deformation along the shear plane (~70%) and friction at the tool-chip contact along the rake face (~30%). Consider plane-strain machining of a rigid perfectly-plastic work material whose uniaxial yield stress is 700 MPa, and is independent of strain rate and temperature. A tool of zero-degree rake angle is employed. Measurements showed the (deformed) chip thickness to be twice that of the undeformed chip thickness. Based on the aforementioned distribution of energy, estimate the specific energy for this process.arrow_forward
- Draw the forces and angles involved in the cutting process and calculate shear angle (Ø), friction coefficient and tangential force ,cutting force = 80 kN, resultant of forces =100KN. friction force=75KN, rake angle =20' undeformed chip thickness = 0.65mm and deformed chip thickness = 0.72mm vjallarrow_forwardManufacturing Process In a turning operation on stainless steel with hardness = 200 HB, the cutting speed = 200m/min, feed = 0.25 mm/rev, and depth of cut =7.5 mm. Determine how much power will the lathe machine draw in performing this operation if its mechanical efficiency = 90 %. Use specific energy value is: U = 2.8 J/mmarrow_forwardA student is performing a turning operation with a workpiece with an initial diameter of 40 mm to produce a 30 mm diameter rod that is 100 mm long. The lathe power is 20 kW and is operating on 85% mechanical efficiency. If the student set the cutting speed to 0.5 m/min and the cutting tool is set to have a rake angle of 5 degrees: a.) What material can we choose for the rod is the coefficient of friction is 0.5? b.) If we select 4130 normalized heat-treated steel for the rod, and coefficient of friction is 0.5, what will the maximum depth of cut we can achieve?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
HOME SHOP JIGS & FIXTURES PART 1, TYPES OF JIGS & ACCESSORIES AND THE THEORIE BEHIND THE TOOLS; Author: THATLAZYMACHINIST;https://www.youtube.com/watch?v=EXYqi42JimI;License: Standard Youtube License