Concept explainers
The solidification time of rectangular casting.
Answer to Problem 5.68P
Given information:
The equation:-
Another casting is of same metal and of rectangular cross-section:
The length and cross-section area are same as of cylindrical casting.
Solidification time of cylindrical casting
Explanation of Solution
Calculation:
First the surface area and volume for each casting:-
Cylindrical casting:-
Rectangular casting:-
Conclusion:The solidification time of rectangular casting is 1.88 min.
Want to see more full solutions like this?
Chapter 5 Solutions
Manufacturing Processes for Engineering Materials (6th Edition)
- A molten drop of liquid metal which is in spherical form will solidify in 5 second . what is a solidification time of same molten drop with double the radius.arrow_forwardcompute the diameter of the sphere (mm) that will freeze in the same time in same casting process with a 62.5mm x 150mm x 225mm plate. Assume that constant mold for this casting is 55 mm^2/sarrow_forwardA vertical centrifugal casting process is used to produce bushings that are 0.2 m outside diameter and 0.2 m in long. If the rotational speed during solidification is 500 rpm, determine the inside diameter at the bottom of the bushing if the diameter at the top is 0.084 m. * Add filearrow_forward
- Determine the time required to fill the mold cavity along with the riser as shown in the following figure. A slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.arrow_forwarda riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.arrow_forwardIn sand casting of hollow part of lead, a cylindrical core of diameter 120 mm and height 180 mm is placed inside the mould cavity. The densities of core material and lead are 1600 kg/m³ and 11300 kg/m³ respectively. The net force (in N) that tends to lift he core during pouring of molten metal will be. . . . .arrow_forward
- Discuss the die casting process and specify the typesarrow_forwardSolidification time of a metallic alloy casting is (a) Directly proportional to its surface area (b) Inversely proportional to the specific heat of the cast material (c) Inversely proportional to the thermal diffusively of the mould material (d) Inversely proportional to the pouring temparrow_forwardFor sand-casting a steel rectangular plate with dimensions 80mm×120mm×20mm, a cylindrical riser has to be designed. The height of the riser is equal to its diameter. The total solidification time for the casting is 2 minutes. In Chvorinov‟s law for the estimation of the total solidification time, exponent is to be taken as 2. For a solidification time of 3 minutes in the riser, the diameter (in mm) of the riser is ____arrow_forward
- 1. A square section riser be designed for a sand-casting mold. The casting itself is a quarter-cylinder with a diameter of 12cm and a length 20cm. The total solidification time for this casting = 0.9 min. The square for the riser will have a height-to-width ratio of 2.0. Determine the dimensions of the riser so that it is total solidification time = 1.2 min.arrow_forward10. Volume of a cube of side / and volume of a sphere of radius rare equal Both the cube and the sphere are solid and of same material They are being cast. What is the ratio of the solidification time of the cube to the same of sphere?arrow_forwardDescribe the stages involved in the contraction of metals during casting.(a) Contraction of the molten metals as it cools prior to its solidification.(b) Contraction of the metal during phase change from liquid to solid.(c) Contraction of the solidified metals as its temperature drops to ambient temperature.(d) All of above.(e) None of above.2. What kinds of defects in castings?(a) Hot tear.(b) Surface scar.(c) Plastic deformation.(d) Ductile flow.3. How does porosity have detrimental effects on the mechanical and physical properties ofcastings?(a) Pores in castings are resulted from internal discontinuities when that are prone topropagate under external stresses.(b) The toughness of a material will decrease as a result of porosity.(c) Physical properties, such as thermal and electrical conductivity, also be adverselyaffected by porosity.(d) Pores increase the strength and elastic modulus.(e) Porosity increases both the thermal and electrical conductivity4. Thermosetting plastics can…arrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY