Using the following table, draw a melting point diagram and estimate the eutectic temperature and composition: Percent composition Melting point range (°C) 100% A 125-126 75% A-25% B 115-120 65% A- 35% B 128-131 50% A- 50% B 135-140 100% B 151-152 Can you suggest what additional points you need to give a more accurate measure of the eutectic point?

Using the following table, draw a melting point diagram and estimate the eutectic temperature and composition: Percent composition Melting point range (°C) 100% A 125-126 75% A-25% B 115-120 65% A- 35% B 128-131 50% A- 50% B 135-140 100% B 151-152 Can you suggest what additional points you need to give a more accurate measure of the eutectic point?

Welding: Principles and Applications (MindTap Course List)

8th Edition

ISBN:9781305494695

Author:Larry Jeffus

Publisher:Larry Jeffus

Chapter26: Welding Metallurgy

Section: Chapter Questions

Problem 12R: What is a eutectic composition?

See similar textbooks

Similar questions

An alloy of 30 wt % Pb and 70 wt % Sn is slowly cooled from 250°C to 27°C: d) What is the amount and composition of each phase that is present at 183°C - ∆T ? e) What are the amounts of each phase present at room temperature? f) Draw the microstructure 183°C + ∆T and 183°C - ∆T in 2 cm diameter circle.
From the phase diagram of the Fe-0.25wt%C alloy below, determine the phase fraction and elemental composition of the resulting phase immediately after solidification across the eutectoid line (725 C). a.alpha_eutectoid = 96.6 wt% and cementite = 29.85 wt% b.alpha_eutectoid = 96.6 wt% and cementite = 3.4 wt% c.alpha_eutectoid = 1.05 wt% and cementite = 29.85 wt% d.alpha_eutectoid = 29.85 wt% and cementite = 1.05 wt%
Referring to Figure 1, answer the following: What are the liquidus and solidus temperatures for an 80%Pb20%Tl alloy? What is the composition of the solid solution phase for the aforementioned alloy once we hit the liquidus temperature upon cooling? For the same alloy above, use the inverse lever rule to calculate the %solid and %liquid at 325C
BINARY PHASE DIAGRAMS Please only answer parts d and e as the rest have been solved. Show full detailed explanation to answers with diagrams if necessary a)(i) What is the melting point of pure Mg?(ii) What is the maximum solubility of Mg in Pb and at what temperaturedoes this occur? (b) A 50 wt.% Pb-50wt% Mg alloy is slowly cooled from 700 °C to 400 °C.(i) At what temperature does the first solid phase form?(ii) What is the composition of this solid phase?(iii) At what temperature does all the liquid solidify?(iv) What is the composition of the last remaining liquid phase?(v) What is the freezing range? (c) What is the mass fraction of solid and liquid of a 60 wt.% Mg alloy at atemperature of 500 °C.(d) Draw and label the microstructure of an 80 wt.% Mg alloy at 600 °C.(e) A Mg-Pb alloy of mass 5.5 kg has a composition just slightly below thesolubility limit of 200 °C.(i) What mass of lead is in the alloy?(ii) If the alloy is heated to 350 °C how much more lead can be dissolvedin…
Describe the phases present at the eutectic temperature when the overall composition is x(Cu)= 0.5
3 Materials Science. From picture below.Describe in detail the phase transformations (showing cooling curves, corresponding optical backgrounds, etc.) that takes place during solidification of the following alloys:(a) 99% Cu - 1% Al(b) 96% Cu - 4% Al(c) 80% Cu - 20% Al
A 80%Sn-20%Pb alloy is melted fully at 300°C and then slowly cooled down to 182°C. Sketch the microstructures at 300°C, 200°C, and 182°C, respectively. Label all phases and indicate their approximate compositions. Also, determine the follows for this alloy at 182°C. (1) The weight fractions of α and β phases.(2) The weight fractions of primary β and eutectic structure.(3) The weight fraction of eutectic β .
10.27 A hypothetical A-B alloy of composition 55 wt% B-45 wt% A at some temperature is found to consist of mass fractions of 0.5 for both a and 8 phases. If the composition of the B phase is 90 wt B-10 wt% A, what is the composition of the a phase?
5 During decommissioning work, in order to determine the number of radionuclides deposited in a section of iron pipe, you grind up a small section of the pipe into a fine powder to carry out a reaction at 400 0C. Preliminary analysis shows that the predominant iron species are FeO and Fe2O3 Is it safe to use an aluminum crucible for heating your sample? What about a graphite crucible? Provide a short but detailed explanation referencing Ellingham diagrams, calculating Gibbs Free Energy, as well as provide any relevant reactions.
A hypothetical A-B alloy of composition 54 wt% B-46 wt% A at some temperature is found to consist of mass fractions of 0.5 for both αand β phases. If the composition of the β phase is 89 wt% B-11 wt% A, what is the composition of the α phase? ________ wt% B
For a lead-tin alloy of composition 80 wt% Sn-20 wt% Pb and at 180 °C, do the following:(a) Determine the mass fractions of the α and β phases.(b) Determine the mass fractions of primary β and eutectic microconstituents.(c) Determine the mass fraction of eutectic β
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)