A brass blank was produced using a force of 25.194 tonnes. The blanking punch radius was measured as 87.889 mm. The blank was prepared to be deep drawn with a 98 mm diameter punch. If you know that the drawing ratio = 1.7959, the deep drawing die radius = 10 mm and the yield strength of :brass = 135 MPa, determine a) The blank thickness mm b) Shear strength of brass = MPa c) Tensile strength of brass = !3!

A brass blank was produced using a force of 25.194 tonnes. The blanking punch radius was measured as 87.889 mm. The blank was prepared to be deep drawn with a 98 mm diameter punch. If you know that the drawing ratio = 1.7959, the deep drawing die radius = 10 mm and the yield strength of :brass = 135 MPa, determine a) The blank thickness mm b) Shear strength of brass = MPa c) Tensile strength of brass = !3!

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

An automated blanking and forming line is designed to from 2 mm thick sheet, made from 2024 Aluminum, T4 temper, into a square sheet metal part. Elongation at 50mm 20% Young’s Modulus 70GPa Yield strength 325 MPa UTS 470 A) What is the force required to punch a square piece that is 500 mm on each edge? B) If the sheet blank was bent to a radius of 5 mm, what will be the radius after springback occurs? C) What is the required bend angle to achieve a 90° final bend angel for a bend radius of 5 mm?
Thank you in advance If you have a Bulk Deformation Process in Metalworking with a product in the Rolling Process that has the following information: Original Thickness = 0.85” , Original Width = 12” , Entering Velocity = 28”/min, Final Thickness = 0.66, Exiting Velocity (in/min) = 30 (use 4 digits for answers) Final Width = _____________ in.
1. The friction in direct extrusion is ________ Indirect extrusion. a) Greater than. b) Equal to. c) Less than.2. The Temperature in hot forming process is ____. a) (0 to 0.4) Tm. b) (0.5 to 0.75) Tm. c) 0.9 Tm. d) 0.4 Tm. e) 0.8 Tm. f) (0.3 to 0.5) Tm. Where Tm is the melting temperature of the work piece.3. Maximum draft in rolling depends on _______. a) Coefficient of friction and roll radius. b) Thickness of plate. c) Smoothness of roll Surface. d) Roll rotational speed.e) Width of the plate. f) Length of the plate.4. In deep drawing process, the drawing ratio (DR) has a higher limit (value) of:- a) 6. b) 1. c) 4. d) 5. e) 7. f) 2. g) Zero.5. Spring Back is a phenomena usually associated with which of the following processes:-a) Extrusion. b) Forging. c) Bending. d) Wire drawing. e) Rolling. f) Sheet metal cutting. g) Deep Drawing.
In a single pass rolling process using 412mm diameter steel rollers, strip of width 120mm and thickness 8mm undergoes 10%reduction of thickness. The angle of bite in radians is.
A compound die will be used to blank and punch a large washer out of 6061ST aluminum alloy sheet stock 3.50 mm thick. The outside diameter of the washer is 50.0 mm and the inside diameter is 15.0 mm. Determine (a) the punch and die sizes for the blanking operation, and (b) the punch and die sizes for the punching operation Vallue for allowance = 0.060
The maximum possible draft in rolling which is the difference between initial and final thickness of the sheet metal, depends on A. Rolling force B. Roll radius C. Roll width D. Yield shear stress of the material
Manufacturer process A compound die will be used to blank and punch a large rectangle (90x150mm blank dimensions) out of 6061ST aluminum alloy sheet stock 3.5 mm thick. The diameter of inside hole is 25 mm. The aluminum sheet metal has a tensile strength = 310 MPa. Determine the minimum tonnage press (force) to perform the blanking and punching operation (1) assume that blanking and punching occur simultaneously and (2) assume that punching occurs first, then blanking. Take: Ac=0.06
A compound die will be used to blank and punch a large rectangle (90x150mm blank dimensions) out of 6061ST aluminum alloy sheet stock 3.5 mm thick. The diameter of inside hole is 25 mm. The aluminum sheet metal has a tensile strength 310 MPa. Determine the minimum tonnage press (force) to perform the blanking and punching operation (1) assume that blanking and punching occur simultaneously and (2) assume that punching occurs first, then blanking, Take: Ac-0.06
A cylindrical ingot with D0 = 50 mm and h0 = 40 mm is cold forged using an open die.The final height is 20 mm. The coefficient of form / friction between the die and the workpiece isconsider Kf = 1.10.The material from which the ingot is made has the following characteristics:K = 600 MPa and η = 0.12.Determine the force (F) on the operation:a) Force required at the moment of reaching the yield point (ℇ = 0.002)b) Force required when you have a height of h = 30 mmc) Force required when there is a final height of h = 20 mmd) Construct the graphs: Force vs Δh and effort vs Δh
1. Derive an expression for the reduction r in drawing as a function of drawing ratio DR.2. A cup is to be drawn in a deep drawing operation. The height of the cup is 75 mm and its insidediameter = 100 mm. The sheet-metal thickness = 2 mm. If the blank diameter = 225 mm, determine(a) drawing ratio, (b) reduction, and (c) thickness-to-diameter ratio. (d) Does the operation seem feasible?3. A drawing operation is used to form a cylindrical cup with inside diameter = 65 mm and height =50mm. The starting blank size = 140 mm and the stock thickness = 2.8mm. determine (a) drawing forceand (b) holding force, given that the tensile strength of the sheet metal (low-carbon steel) = 350 MPa andyield strength = 190 MPa. The die corner radius = 6 mm. Based on these data, is the operation feasible?
A stainless steel part is blanked from a larger sheet (0.5m wide, 1.0m long, 0.004m thick). Determine the tonnage (force) requirement for the blanking operation if the material shear strength is 600 MPa.
A circular shape blank will be cut of 107 mm diameter from a strip of 3.5 mm with a clearance value of 0.25 mm. Take the shear strength as 400 MPa. Determine The appropriate punch diameter. Blanking force. Blanking force when the blade angle is 5.70 o.