Question
Chapter 2, Problem 2.58P
To determine
The expression for the toughness of material.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
A tensile test specimen of 1045 hot-rolled steel having a diameter of 0.505 in. and a gage length of 2.00 in. was tested to fracture.
Stress and strain data obtained during the test are shown. Determine the modulus of elasticity.
Stress (ksi)
240
200
160-
120-
80
40-
0+
0
0
Upper scale
O 79100 ksi
E
O 94000 ksi
O 86700 ksi
O 63200 ksi
O 51900 ksi
Lower scale.
0.025 0.050 0.075 0.100 0.125 0.150 0.175
0.002 0.004 0.006 0.008 0.010 0.012 0.014
Strain (in./in.)
A material has the following properties, ultimate Sul = σul = 350mpa, the strain hardening exponent n=0.20. Determine the value for the strength coefficient K.
A tensile specimen havign a diameter of 6 mm and a gauge length of 50 mm was tested to fracture and the stress-strain diagram is show. Poisson's ratio of material, v = 0.3
Determine the load P that the sample is subjected to when a stress of 300 MPa is applied. What is the instantaneous diameter of the sample given a longitudinal strain of 0.002?
Chapter 2 Solutions
Pearson eText for Manufacturing Processes for Engineering Materials -- Instant Access (Pearson+)
Ch. 2 - Prob. 2.1QCh. 2 - Prob. 2.2QCh. 2 - Prob. 2.3QCh. 2 - Prob. 2.4QCh. 2 - Prob. 2.5QCh. 2 - Prob. 2.6QCh. 2 - Prob. 2.7QCh. 2 - Prob. 2.8QCh. 2 - Prob. 2.9QCh. 2 - Prob. 2.10Q
Ch. 2 - Prob. 2.11QCh. 2 - Prob. 2.12QCh. 2 - Prob. 2.13QCh. 2 - Prob. 2.14QCh. 2 - Prob. 2.15QCh. 2 - Prob. 2.16QCh. 2 - Prob. 2.17QCh. 2 - Prob. 2.18QCh. 2 - Prob. 2.19QCh. 2 - Prob. 2.20QCh. 2 - Prob. 2.21QCh. 2 - Prob. 2.22QCh. 2 - Prob. 2.23QCh. 2 - Prob. 2.24QCh. 2 - Prob. 2.25QCh. 2 - Prob. 2.26QCh. 2 - Prob. 2.27QCh. 2 - Prob. 2.28QCh. 2 - Prob. 2.29QCh. 2 - Prob. 2.30QCh. 2 - Prob. 2.31QCh. 2 - Prob. 2.32QCh. 2 - Prob. 2.33QCh. 2 - Prob. 2.34QCh. 2 - Prob. 2.35QCh. 2 - Prob. 2.36QCh. 2 - Prob. 2.37QCh. 2 - Prob. 2.38QCh. 2 - Prob. 2.39QCh. 2 - Prob. 2.40QCh. 2 - Prob. 2.41QCh. 2 - Prob. 2.42QCh. 2 - Prob. 2.43QCh. 2 - Prob. 2.44QCh. 2 - Prob. 2.45QCh. 2 - Prob. 2.46QCh. 2 - Prob. 2.47QCh. 2 - Prob. 2.48QCh. 2 - Prob. 2.49PCh. 2 - Prob. 2.50PCh. 2 - Prob. 2.51PCh. 2 - Prob. 2.52PCh. 2 - Prob. 2.53PCh. 2 - Prob. 2.54PCh. 2 - Prob. 2.55PCh. 2 - Prob. 2.56PCh. 2 - Prob. 2.57PCh. 2 - Prob. 2.58PCh. 2 - Prob. 2.59PCh. 2 - Prob. 2.60PCh. 2 - Prob. 2.61PCh. 2 - Prob. 2.62PCh. 2 - Prob. 2.63PCh. 2 - Prob. 2.64PCh. 2 - Prob. 2.65PCh. 2 - Prob. 2.66PCh. 2 - Prob. 2.67PCh. 2 - Prob. 2.68PCh. 2 - Prob. 2.69PCh. 2 - Prob. 2.70PCh. 2 - Prob. 2.71PCh. 2 - Prob. 2.72PCh. 2 - Prob. 2.73PCh. 2 - Prob. 2.74PCh. 2 - Prob. 2.75PCh. 2 - Prob. 2.76PCh. 2 - Prob. 2.78PCh. 2 - Prob. 2.79PCh. 2 - Prob. 2.80PCh. 2 - Prob. 2.81PCh. 2 - Prob. 2.82PCh. 2 - Prob. 2.83PCh. 2 - Prob. 2.84PCh. 2 - Prob. 2.85PCh. 2 - Prob. 2.86PCh. 2 - Prob. 2.87PCh. 2 - Prob. 2.88PCh. 2 - Prob. 2.89PCh. 2 - Prob. 2.90PCh. 2 - Prob. 2.91PCh. 2 - Prob. 2.92PCh. 2 - Prob. 2.93PCh. 2 - Prob. 2.94PCh. 2 - Prob. 2.95PCh. 2 - Prob. 2.96PCh. 2 - Prob. 2.97PCh. 2 - Prob. 2.98PCh. 2 - Prob. 2.99PCh. 2 - Prob. 2.100PCh. 2 - Prob. 2.101P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A metallic tube has an outer diameter of 500 mm and a wall thickness of 30 mm (Figure 4). The working internal pressure of the tube is 15 MPa and the fracture toughness of the material (K₁c) ranges from 40 MN/m³/2 to 50 MN/m³/2. Select a value for Kic and determine the size of the largest flaw the tube can contain. Assume that for this geometry K σφπα. = 30 mm! 500 mm Figure surface flaws 4 (not to scale)arrow_forwardIn a creep test, a material with E = 600 MPa is initially loaded with a stress o, = 297 MPa. 1.5 hr after the initial loading, the strain in the material is measured to be 0.12, and after another hour, it is found to be 0.1832. What will be the strain in the material 3 hours after the initial loading? How much time did it take for the strain to reach a value of 0.001?arrow_forwardName the points on the stress-strain diagram. Describe them. ( Stress B Elastic Behaviou Strain Plastic Behaviour E.arrow_forward
- 100 mm must elongate only 5 mm when a tensle load of 100,000 N is applied. Under these A cylindrical specimen of a brass alloy having a circumstances what must be the radius of the specimen? Consider this brass alloy to have the stress-strain behavior shown in Figure below. Tensile strengh 450 MPa (65,000 p A00 10 pu 300 200- 30 Yield strength 250 MPa (36,000 psi 2아 100 1아 100 0.005 0.20 0.30 0.40arrow_forwardThe stress–strain diagram for an aluminum alloy specimen having an original diameter of 0.5 in. and a gauge length of 2 in. is given in the figure. Determine approximately the modulus of resilience and the modulus of toughness for the material.arrow_forwardA component made of Aluminium 6061-T651 has an edge crack with length equal to 15 mm, as shown The yield stress of the material is oy = 280 MPa and its fracture toughness (KIC) ranges from 40 MN/m³/2 to 60 MN/m³/2. Select a value for Kic and evaluate the maximum load this component can withstand. 15 mm P P↓ 100 mm 30 mmarrow_forward
- A bar of 4340 steel has an Sy = 50 ksi. Which of these statements is true: If Sy = 50 ksi, than the normal stress in the bar is always 50 ksi. If a normal stress of 40 ksi is applied to the bar, it will undergo plastic deformation. The Sy = 50 ksi indicates bar is behaving in a brittle manner. O Any normal stress above 50 ksi will cause plastic deformation in the bar.arrow_forwardIdentify the material as shown in figure below. Nominal Strain Rigid Material Perfectly plastic material Elastic plastic material Linear elastic material Nominal Stressarrow_forwardThe factor of safety for mechanical components that are subjected to fatigue loading should be based on yield strength. Select one: O True O Falsearrow_forward
- III-A component is subjected to a cyclic loading at the frequency of once every 5 minutes for 5 years. The cycle is between 220 MPa in tension and 50 MPa in compression. The fracture toughness of the material is 80 MPa√m, Y = 1.12, C = 1.62 x 10-12 (MPa and m) and n = 3.2, and we know that it has initial cracks of length 0.1 mm. At the end of the 5 years, because of the failure of other components, the stresses become 10 times larger. Is the component able to hold the new cyclic loading? If so, for how long? If not, explain.arrow_forwardMatch the image with the material property depicted by the image. - 1. 2. Behavior depicted in image A - 1. 2. Behavior depicted in image B 1. Brittle behavior 2. Ductile behaviorarrow_forwardA tensile test specimen of 1045 hot-rolled steel having a diameter of 0.505 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the ultimate strength. Stress (ksi) 60 50- 40- 30- 20 10- 0 0 0 Upper scale O 66 ksi 28 ksi O 72 ksi O 53 ksi O 62 ksi Lower scale. 0.025 0.050 0.075 0.100 0.125 0.150 0.175 0.002 0.004 0.006 0.008 0.010 0.012 0.014 Strain (in./in.)arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Stresses Due to Fluctuating Loads Introduction - Design Against Fluctuating Loads - Machine Design 1; Author: Ekeeda;https://www.youtube.com/watch?v=3FBmQXfP_eE;License: Standard Youtube License