Whether the percentage elongations of materials are calculated on the basis of Figure 2.6 or not and also explain the reason
Answer to Problem 2.1Q
The percentage elongations of materials cannot be calculated on the basis of Figure 2.6.
Explanation of Solution
Given:
The Figure 2.6 represents the graph between true strain and true stress.
Concept used:
Write the expression for percentage elongation.
Here, E is percentage elongation,
Calculation:
From Figure 2.6 the value of fracture strain and necking strain can be calculated but the original gage length cannot be calculated from Figure 2.6.
Equation (1) represented that elongation is function of the gage length, and gage length cannot be calculated from Figure 2.6. Therefore, the percentage elongations of materials cannot be calculated by Figure 2.6.
Conclusion:
Thus, the percentage elongations of materials cannot be calculated on the basis of Figure 2.6.
Want to see more full solutions like this?
Chapter 2 Solutions
Pearson eText for Manufacturing Processes for Engineering Materials -- Instant Access (Pearson+)
- Draw two schematic graphs using pencil showing a typical stress-strain curve for aluminum. The first graph should show engineering stress vs engineering strain, and the second graph should show true stress vs true strain. Label the showing: (i) elastic modulus (ii) proportional limit (iii) yield stress (iv)yield strain (v) fracture stress (vi) fracture strain on each graph. You may showboth graphs on one plot. Explain the difference between engineering stress and true stress.arrow_forwardPlease annotate the attached stress strain graph of 0.9% carbon steel to show the different phases. From the graph work out the following: 1) modulus of elasticity 2) tensile strength 3) the ductility in % elongation 4) yield strength at a strain offset of 0.002arrow_forward5b.You used a material to design a system. The more you apply external force, the more the system becomes rigid. Use a sketch to explain how the material is disobeying the stress and strain characteristics. Give two(2) examples.arrow_forward
- The corner of a 0.4m_0.3m_0.2 m cubic element is displaced to point C, whose coordinates are (0.398,0.303, 0.199) mm, as shows in Fig. Assuming all straight lines remain straight during deformation, find the state of strain at point Carrow_forwardExplain what the meaning of strain hardening is, how it happens in the materials. Do you think strain hardening is useful? Explain your answerarrow_forwardGiven the stress plot, how do you make strain plots for each of the models/materials given (Maxwell and Kelvin-Voigt)?arrow_forward
- why use yield strength not tensile strength? You are drawing wire which you want the wire to elongate pernamently, and not return back to original shape .arrow_forwardThe figure below shows a rectangular OB element made of 0.5 cm thick aluminum sheet, attached to the ground at one end and supported by a coil spring at point A. The spring was measured with a force of 10 kN, a 1 mm shrinkage. Find bending at point B using the Castigliano method.arrow_forward1) Draw (using a normal graph paper) a conventional stress-strain diagram for ANY metallic material (e.g. steel, aluminium, copper, brass, iron, tungsten). The diagram should be as accurate as possible using a suitable scale (e.g. 1cm: 10 N). 2) Calculate the Modulus of Elasticity, Modulus of Toughness and Modulus of Resilience for the material from the stress-strain diagram. Show your calculations in detail on a separate A4 piece of paper.arrow_forward
- A material has a linear elastic perfectly plastic stress-strain. A cylindrical specimen of that material having an initial length of 35 mm and a tadius of 7 mm is pulled until it elongates 0.8mm. a. Calculate the stain and the corresponding stress at that elongation value. b. Afterward, the specimen is released to zero stress level, how does the final length of the specimen compare with its original length? How much plastic deformation remains if it exists?arrow_forwardcylindrical bar of aluminum 20 mm in diameter is to be deformed elastically in tension. Aforce of 17,000 N. produces a reduction in specimen diameter of 3*10-3 mm if its elastic modulus is100 GPa. Draw the deformation situation and Compute Poisson’s ratio for this material if its elasticmodulus is 100 GPa?arrow_forwardSpecifically a mechanics of materials problem. Question in pic below. Hint: The solution must include relevant free body diagrams defining terms and that are consistent with the computations you make. Justify your computation of shear stress. This justification should include a sketch showing the “broken” part exposing the surface area upon which the shear stress actsarrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY