Textbook Question
Chapter 3, Problem 3.22QP
Getting measurements from Figure 3.18, determine approximate values of the following items for steel with different carbon contents. Use one system of units only as specified by the instructor.
- a. a Yield stress
- b. Ultimate strength
- c. Strain at failure
- d. Effect on modulus of elasticity
- e. Approximate toughness. Curves may be approximated with a series of straight lines.
- f. Comment on the effect of increasing carbon content on items a through e above.
Expert Solution & Answer
![Check Mark](/static/check-mark.png)
Want to see the full answer?
Check out a sample textbook solution![Blurred answer](/static/blurred-answer.jpg)
Students have asked these similar questions
Getting measurements from Figure , determine approximate values of the following items for steel with different carbon contents. Use one system of units only as specified by the instructor.a. Yield stressb. Ultimate strengthc. Strain at failured. Effect on modulus of elasticitye. Approximate toughness. Curves may be approximated with a series of straight lines.f. Comment on the effect of increasing carbon content on items a through e above.
A wood beam is strengthened using two steel plates as shown in the figure below.
*Inserted Photo*
The beam has simple supports and an overhang and is subjected to a point load and a uniform load as shown in the figure below.
Â
Calculate the maximum tensile and compressive stresses of the beam. Assume that Ew = 11 GPa and Es = 200 GPa. (Enter your answers in MPa. Use the deformation sign convention.)
maximum tensile stress in wood ? MPa
maximum tensile stress in steel ? MPa
maximum compressive stress in wood ? MPa
maximum compressive stress in steel ? MPa
A high-yield-strength alloy steel bar with a rectangular cross section that has a width of 37.5 mm, a thickness of 6.25 mm, and a gauge length of 203 mm was tested in tension to rupture, according to ASTM E-8 method. The load and deformation data were as shown in Table Using a spreadsheet program, obtain the following:a. A plot of the stress–strain relationship. Label the axes and show units.b. A plot of the linear portion of the stress–strain relationship. Determine modulus of elasticity using the best-fit approach.c. Proportional limit.d. Yield stress.e. Ultimate strength.f. If the specimen is loaded to 155 kN only and then unloaded, what is the permanent deformation?g. In designing a typical structure made of this material, would you expect the stress applied in (f) safe? Why?
Chapter 3 Solutions
Pearson eText for Materials for Civil and Construction Engineers -- Instant Access (Pearson+)
Ch. 3 - What is the chemical composition of steel? What is...Ch. 3 - Why does the ironcarbon phase diagram go only to...Ch. 3 - Draw a simple ironcarbon phase diagram showing the...Ch. 3 - What is the typical maximum percent of carbon in...Ch. 3 - Calculate the amounts and compositions of phases...Ch. 3 - Briefly discuss four heat treatment methods to...Ch. 3 - Define alloy steels. Explain why alloys are added...Ch. 3 - Prob. 3.8QPCh. 3 - Specifically state the shape and size of the...Ch. 3 - What are the typical uses of structural steel?
Ch. 3 - What is the range of thicknesses of cold-formed...Ch. 3 - Why is coil steel used for cold-formed steel...Ch. 3 - If a steel with a 33 ksi yield strength is used...Ch. 3 - Why is reinforcing steel used in concrete? Discuss...Ch. 3 - What is high-performance steel? State two HPS...Ch. 3 - Name three mechanical tests used to measure...Ch. 3 - The following laboratory tests are performed on...Ch. 3 - Sketch the stress-strain behavior of steel, and...Ch. 3 - Three steel bars with a diameter of 25 mm and...Ch. 3 - Three steel bars with a diameter of 0.5 in. and...Ch. 3 - Draw a typical stressstrain relationship for steel...Ch. 3 - Getting measurements from Figure 3.18, determine...Ch. 3 - A steel specimen is tested in tension. The...Ch. 3 - A steel specimen is tested in tension. The...Ch. 3 - A No. 10 steel rebar is tested in tension. By...Ch. 3 - A mild steel specimen originally 300 mm long is...Ch. 3 - A tension stress of 70 ksi was applied on a 12-in....Ch. 3 - A tensile stress is applied along the long axis of...Ch. 3 - A cylindrical steel alloy rod with a 0.5 in....Ch. 3 - A round steel alloy bar with a diameter of 0.75...Ch. 3 - A 19-mm reinforcing steel bar and a gauge length...Ch. 3 - Testing a round steel alloy bar with a diameter of...Ch. 3 - During the tension test on a steel rod within the...Ch. 3 - A grade 36 round steel bar with a diameter of 0.5...Ch. 3 - A high-yield-strength alloy steel bar with a...Ch. 3 - Estimate the cross-sectional area of a 350S125-27...Ch. 3 - An ASTM A615 grade 60 number 10 rebar with a gauge...Ch. 3 - A 32-mm rebar with a gauge length of 200 mm was...Ch. 3 - A steel pipe having a length of 3 ft. an outside...Ch. 3 - A steel pipe having a length of 1 m, an outside...Ch. 3 - A drill rod with a diameter of 10 mm is made of...Ch. 3 - A drill rod with, a diameter of 1/2 in. is made of...Ch. 3 - Prob. 3.43QPCh. 3 - An engineering technician performed a tension test...Ch. 3 - A Charpy V Notch (CVN) test was performed on a...Ch. 3 - Prob. 3.46QPCh. 3 - Prob. 3.47QPCh. 3 - How can the flaws in steel and welds be detected?...Ch. 3 - Determine the welding zone classification of A36...Ch. 3 - Briefly define steel corrosion. What are the four...Ch. 3 - Discuss the main methods used to protect steel...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.arrow_forwardThe results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.arrow_forwardA round aluminum alloy bar with a 0.25-in. diameter and a 1-in. gauge length was tested in tension to fracture according to ASTM E-8 method. The load and deformation data were as shown in Table P4.8.Using a spreadsheet program, obtain the following: a. A plot of the stress–strain relationship. Label the axes and show units. b. A plot of the linear portion of the stress–strain relationship. Determine modulus of elasticity using the best fit approach. c. Proportional limit. d. Yield stress at an offset strain of 0.002 in/in. e. Initial tangent modulus. f. If the specimen is loaded to 3200 lb only and then unloaded, what is the permanent change in gauge length? g. When the applied load was 1239 lb, the diameter was measured as 0.249814 in. Determine Poisson’s ratio.arrow_forward
- An aluminum alloy bar with a rectangular cross section that has a width of 12.5 mm, thickness of 6.25 mm, and a gauge length of 50 mm was tested in tension to fracture according to ASTM E-8 method. The load and deformation data were as shown in Table P4.6. Using a spreadsheet program, obtain the following: a. A plot of the stress-strain relationship. Label the axes and show units. b. A plot of the linear portion of the stress-strain relationship. Determine the modulus of elasticity using the best fit approach. c. Proportional limit. d. Yield stress at an offset strain of 0.002 m/m. e. Tangent modulus at a stress of 450 MPa. f. Secant modulus at a stress of 450 MPa. TABLE P4.6 Load (kN) AL (mm) Load (kN) AL (mm) 33.5 1.486 3.3 0.025 35.3 2.189 14.0 0.115 37.8 3.390 25.0 0.220 39.8 4.829 29.0 0.406 40.8 5.961 30.6 0.705 41.6 7.386 31.7 0.981 41.2 8.047 32.7 1.245arrow_forwardA 19-mm reinforcing steel bar and a gauge length of 75 mm was subjected to ten- sion, with the results shown in Table P3.27. Using a computer spreadsheet pro- gram, plot the stress-strain relationship. From the graph, determine the Young's modulus of the steel and the deformation corresponding to a 150-kN load. TABLE P3.27 Load, kN Deformation, mm 54 0.084 163 0.168 284 0.336 330 1.428 366 3.360arrow_forwardCalculate the total deformation of steelbars shown in Figure. (d1=15 mm, d2=25 mm and E=210 GPa) A= 5, B=3, C=8arrow_forward
- What is the value of reduction factor of the beam, if the stress in the steel is 400 MPa, and the Modulus of Elasticity of the Steel is 200,000 MPa. O 0.671 0.692 O 0.660 O 0.650 None of the Choices O 0.681arrow_forwardDetermine the ductility of the following steel samples that undergo tensile strength test. All dimensions in millimeter.arrow_forwardThree steel bars have a diameter of 25 mm and carbon contents of 0.2, 0.5, and 0.8%, respectively. The specimens were subjected to tension until rupture. The load versus deformation results were as shown in Table P3.19. If the gauge length is 50 mm, determine the following: a. The tensile stresses and strains for each specimen at each load increment. b. Plot stresses versus strains for all specimens on one graph. TABLE P3.19 Specimen No. Carbon Content (%) 1 3 0.2 0.5 0.8 Deformation (mm) Load (kN) 0.00 0.07 133 133 133 0.10 137 191 191 0.15 142 196 285 0.50 147 201 324 1.00 140 199 383 2.50 155 236 447 5.00 196 295 491 (Rupture) 7.50 226 336 10.00 241 341 12.50 218 304 (Rupture) 13.75 196 (Rupture) c. The proportional limit for each specimen. d. The 0.2% offset yield strength for each specimen. e. The modulus of elasticity for each specimen. f. The strain at rupture for each specimen. g. Comment on the effect of increasing the carbon content on the following: Yield strength ii.…arrow_forward
- A tensile test specimen of stainless steel alloy having a diameter of 0.495 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the modulus of elasticity. 120 Upper scale 90 60 Lower scale 30 0.040 0.004 0.060 0.006 0.120 0.012 0.020 0.100 0.010 0.0 0.080 0.008 0.0 0.002 Strain (in./in.) Stress (ksi)arrow_forwardA 32-mm rebar with a gauge length of 200 mm was subjected to tension to fracture according to ASTM E-8 method. The load and deformation data were as shown in TableUsing a spreadsheet program obtain the following:a. A plot of the stress–strain relationship. Label the axes and show units.b. A plot of the linear portion of the stress–strain relationship. Determine modulus of elasticity using the best-fit approach.c. Proportional limit.d. Yield stress.e. Ultimate strength.f. If the rebar is loaded to 390 kN only and then unloaded, what is the permanent change in length?arrow_forward3. Reproduce the table from NSCP 2015 showing the values of strength reduction phi under different conditions of strain in steel.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Steel Design (Activate Learning with these NEW ti...Civil EngineeringISBN:9781337094740Author:Segui, William T.Publisher:Cengage LearningMaterials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
![Text book image](https://www.bartleby.com/isbn_cover_images/9781337094740/9781337094740_smallCoverImage.gif)
Steel Design (Activate Learning with these NEW ti...
Civil Engineering
ISBN:9781337094740
Author:Segui, William T.
Publisher:Cengage Learning
![Text book image](https://www.bartleby.com/isbn_cover_images/9781111988609/9781111988609_smallCoverImage.gif)
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
The History of Iron and Steel; Author: Real Engineering;https://www.youtube.com/watch?v=7E__zqy6xcw;License: Standard Youtube License