Chapter 7, Problem 7.8QP
Design the concrete mix according to the following conditions:
Design Environment
Building frame
Required design strength = 27.6 MPa
Minimum dimension = 150 mm
Minimum space between rebar = 40 mm
Minimum cover over rebar = 40 mm
Statistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples).
Only air entrainer is allowed.
Available Materials
Air entrainer: Manufacture specification 6.3 ml/1% air/100 kg cement. Coarse aggregate: 19 mm nominal maximum size, river gravel (rounded)
Bulk oven-dry specific gravity = 2.55, absorption = 3.6%
Oven-dry rodded density = 1761 kg/m3
Moisture content = 2.5%
Fine aggregate: Natural sand
Bulk oven-dry specific gravity = 2.659, absorption = 0.5%
Moisture content = 2%
Fineness modulus = 2.47
Expert Solution & Answer
Learn your wayIncludes step-by-step video
schedule20:19
Students have asked these similar questions
Design the concrete mix according to the following conditions:Design EnvironmentBuilding frameRequired design strength = 27.6 MPaMinimum dimension = 150 mmMinimum space between rebar = 40 mmMinimum cover over rebar = 40 mmStatistical data indicate a standard deviation of compressive strength of2.1 MPa is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification 6.3 mL/1% air/100 kg cement.Coarse aggregate: 19 mm nominal maximum size, river gravel (rounded)Bulk oven-dry specific gravity = 2.55, absorption = 3.6,Oven-dry rodded density = 1761 kg/m3Moisture content = 2.5,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.659, absorption = 0.5,Moisture content = 2,Fineness modulus = 2.47
Design the concrete mix according to the following conditions:Design Environment• Building beamo Required design strength = 27.6 MPao Minimum dimension = 150 mmo Minimum space between rebar = 40 mmo Minimum cover over rebar = 40 mmo Statistical data indicate a standard deviation of compressive strengthof 2.1 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Moderate Sulphate exposure.• Available Materialso Air entrainer:▪ Manufacture specification 6.3 mL/1% air/100 kg cement.o Coarse aggregate:▪ 19 mm nominal maximum size▪ River gravel (rounded)▪ Bulk oven-dry specific gravity = 2.55▪ Absorption = 3.6▪ Oven-dry rodded density = 1761 kg/m3▪ Moisture content = 2.5o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.659▪ Absorption = 0.5▪ Moisture content = 2▪ Fineness modulus = 2.47o Cement▪ Type II (Moderate Sulphate Resistant)▪ Specific Gravity = 3.15Based on this information, find the following and summarize the findings in a table
d) The amount…
Design the concrete mix according to the following conditions:Design Environment• Building beamo Required design strength = 27.6 MPao Minimum dimension = 150 mmo Minimum space between rebar = 40 mmo Minimum cover over rebar = 40 mmo Statistical data indicate a standard deviation of compressive strengthof 2.1 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Moderate Sulphate exposure.• Available Materialso Air entrainer:▪ Manufacture specification 6.3 mL/1% air/100 kg cement.o Coarse aggregate:▪ 19 mm nominal maximum size▪ River gravel (rounded)▪ Bulk oven-dry specific gravity = 2.55▪ Absorption = 3.6▪ Oven-dry rodded density = 1761 kg/m3▪ Moisture content = 2.5o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.659▪ Absorption = 0.5▪ Moisture content = 2▪ Fineness modulus = 2.47o Cement▪ Type II (Moderate Sulphate Resistant)▪ Specific Gravity = 3.15Based on this information, find the following and summarize the findings in a table.a) Required…
Chapter 7 Solutions
Materials for Civil and Construction Engineers (2nd Edition)
Ch. 7 - The design engineer specifies a concrete strength...Ch. 7 - A project specifies a concrete strength of 24.1...Ch. 7 - A project specifies a concrete strength of at...Ch. 7 - What is your recommendation for the maximum size...Ch. 7 - A concrete mix with a 3-in. slump, w/c ratio of...Ch. 7 - Prob. 7.6QPCh. 7 - You are working on a concrete mix design that...Ch. 7 - Design the concrete mix according to the following...Ch. 7 - Design the concrete mix according to the following...Ch. 7 - The design of a concrete mix requires 1173 kg/m3...
Ch. 7 - Prob. 7.11QPCh. 7 - Prob. 7.12QPCh. 7 - Students in the materials lab mixed concrete with...Ch. 7 - Students in the materials lab mixed concrete with...Ch. 7 - Why is it necessary to measure the air content of...Ch. 7 - What do we mean by curing concrete? What will...Ch. 7 - Discuss five different methods of concrete curing.Ch. 7 - Draw a graph showing the typical relation between...Ch. 7 - Why is extra water harmful to fresh concrete, but...Ch. 7 - Discuss the change in volume of concrete at early...Ch. 7 - Discuss the creep response of concrete structures....Ch. 7 - Prob. 7.22QPCh. 7 - On one graph, draw a sketch showing the typical...Ch. 7 - Using Figure 7.34, a. Determine the ultimate...Ch. 7 - Three concrete mixes with the same ingredients,...Ch. 7 - Three concrete mixes with the same ingredients,...Ch. 7 - Three 100 mm 200 mm concrete cylinders with water...Ch. 7 - Students in the materials class prepared three 4 ...Ch. 7 - Three 150 mm 300 mm concrete cylinders with water...Ch. 7 - Three 6 in. 12 in. concrete cylinders with water...Ch. 7 - A normal-weight concrete has an average...Ch. 7 - Discuss the significance of the compressive...Ch. 7 - What is the standard size of PCC specimens to be...Ch. 7 - Prob. 7.34QPCh. 7 - What is the purpose of performing the flexure test...Ch. 7 - What are the advantages of using a third-point...Ch. 7 - Consider a standard flexural strength specimen of...Ch. 7 - To evaluate the effect of a certain admixture on...Ch. 7 - To evaluate the effect of a certain admixture on...Ch. 7 - Prob. 7.40QPCh. 7 - Prob. 7.41QPCh. 7 - A normal-weight concrete has an average...Ch. 7 - Three batches of concrete were prepared using the...Ch. 7 - Three batches of concrete were prepared using the...Ch. 7 - Prob. 7.45QPCh. 7 - Prob. 7.46QPCh. 7 - Discuss two nondestructive tests to be performed...Ch. 7 - Discuss the concept of concrete maturity meters.Ch. 7 - Discuss four alternatives that increase the use...Ch. 7 - What is self-consolidating concrete? How are its...Ch. 7 - Prob. 7.51QPCh. 7 - Two 6 in. 12 in. concrete cylinders with randomly...Ch. 7 - Discuss the concept of high-performance concrete....Ch. 7 - Comparing PCC with mild steel, answer the...Ch. 7 - Prob. 7.55QP
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
Consider a soil that is being placed as a fill and compacted using a sheepsfoot roller (a piece of construction...
Foundation Design: Principles and Practices (3rd Edition)
Determine the resultant internal loadings acting on the cross sections at points F and G of the frame.
Mechanics of Materials (10th Edition)
The ____________ is always transparent.
Web Development and Design Foundations with HTML5 (9th Edition) (What's New in Computer Science)
Explain the different aspects of the cost of a programming language.
Concepts of Programming Languages (11th Edition)
What is an algorithm?
Starting Out With Visual Basic (8th Edition)
The switch in the bottom loop of Fig. P6.1 is closed at t = 0 and then opened at a later time t1. What is the d...
Fundamentals of Applied Electromagnetics (7th Edition)
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- Design the concrete mix according to the following conditions:Design EnvironmentPavement slab, Bozeman, Montana (cold climate)Required design strength = 3000 psiSlab thickness = 12 in.Statistical data indicate a standard deviation of compressive strength of250 psi is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification is 0.15 fl oz/1% air/100 lb cement.Coarse aggregate: 2 in. nominal maximum size, crushed stoneBulk oven-dry specific gravity = 2.573, absorption = 2.8,Oven-dry rodded density = 120 pcfMoisture content = 1,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.540, absorption = 3.4,Moisture content = 4.5,Fineness modulus = 2.68arrow_forwardDesign the concrete mix according to the following conditions: Design environment Tennis court, subjected to freezing Required design strength =21 MPa Slab thickness=300 mm Statistical data indicate a standard deviation of compressive strength of 3.7 MPa is expected (for 50 samples) Only air entrainer is allowed Available materials: Air=7% Air entertainer: Manufacturer specification is 9.0 ML /1% air/100kg cement Slump=50 mm Coarse aggregate: 50 mm nominal maximum size, crushed stone Bulk volume oven-dry specific gravity=2.61, absorption=2.8%, oven-dry rodded density=1870 kg/m3 Moisture content=1% Fine aggregate: Natural sand Bulk oven-dry specific gravity=2.54, absorption=3.4% Moisture content= 4.5% Fineness modulus=2.60 Cement: Type I, relative density=3.1arrow_forwardDesign a concrete mix for the following conditions and constraints using the absolute volume method:Design EnvironmentBuilding frameRequired design strength = 27.6 MPaMinimum dimension = 150 mmMinimum space between rebars = 40 mmMinimum cover over rebars = 40 mmStatistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples)Only air entrainer is allowedAvailable MaterialsAir EntrainerManufacturer specification 6.3 ml/1% air / 100 kg cementCoarse aggregate19 mm nominal maximum size, river gravel (rounded)Bulk oven dry specific gravity = 2.55, Absorption = 0.3%Oven dry-rodded density = 1761 kg/m3Moisture content = 2.5%Fine aggregateNatural sandBulk oven-dry specific gravity = 2.659, Absorption = 0.5%Moisture content = 2%Fineness modulus = 2.47arrow_forward
- Design the concrete mix according to the following conditions:Design EnvironmentPavement slab, subjected to freezingRequired design strength = 21 MPaSlab thickness = 300 mmStatistical data indicate a standard deviation of compressive strength of1.7 MPa is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification is 9.5 mL/1% air/100 kgcement.Coarse aggregate: 2 in. nominal maximum size, crushed stoneBulk oven-dry specific gravity = 2.573, absorption = 2.8,Oven-dry rodded density = 1922 kg/m3Moisture content = 1,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.540, absorption = 3.4,Moisture content = 4.5,Fineness modulus = 2.68arrow_forwardDesign a concrete mix for the following conditions and constraints using the Absolute Volume Method. The material description are as follows: I. Design Environment i. Retaining Wall exposed to moderate sulfate exposure ii. Required Design Compressive Strength = 27.6 MPa iii. Standard Deviation of Compressive Strength of 1.8 MPa is expected (25 sample only) iv. Minimum dimension = 200 mm v. Minimum space between re-bars = 50 mm vi. Minimum cover over re-bars = 50 mm vii. Maximum Slump is required viii. Only air entrained is allowed II. Available Materials i. Air Entrained – Manufacture Specification 5.5ml/1% air/100 kg cement (use maximum or +2% air content) ii. Coarse Aggregates 25 mm Nominal Maximum Aggregate Size Rounded River Gravel (Note: apply water content reduction) Bulk Oven-dry specific gravity = 2.65 Absorption = 0.2%…arrow_forwardQ. Using the British methods, design a concrete mix to bear an average compressive strength of 35 MPa at 28 days, to cast a room slab with the following dimensions (5 width x 4 length x 0.2 depth m) and 200 mm space distance of reinforcement. Consider the following properties: o Cement used is type I Portland cement ® Required slump = 30 — 60 mm o Coarse aggregate: ® Crushed rocks * Maximum size of 40 mm, e The fine aggregate: * Crushed rocks = Falls in zone 3 o Assume zone A for figure 1 o AssumeK = 1.64arrow_forward
- (ASAP PLEASE) Design a concrete mix for the following conditions and constraints using the Absolute Volume Method. The material description are as follows: I. Design Environment i. Retaining Wall exposed to moderate sulfate exposure ii. Required Design Compressive Strength = 27.6 MPa iii. Standard Deviation of Compressive Strength of 1.8 MPa is expected (25 sample only) iv. Minimum dimension = 200 mm v. Minimum space between re-bars = 50 mm vi. Minimum cover over re-bars = 50 mm vii. Maximum Slump is required viii. Only air entrained is allowed II. Available Materials i. Air Entrained – Manufacture Specification 5.5ml/1% air/100 kg cement (use maximum or +2% air content) ii. Coarse Aggregates 25 mm Nominal Maximum Aggregate Size Rounded River Gravel (Note: apply water…arrow_forwardDesign the concrete mix according to the following conditions. Design Environment Pavement slab, Baguio City (severe cold climate) Required design strength = 3000 psi Slab thickness = 12 in. Statistical data indicate a standard deviation of compressive strength of 250 psi is expected (more than 30 samples). Only air entrainer is allowed. Available Materials: Air entrainer: Manufacture specification is 0.15 fl oz/1% air/100 lb cement. Coarse aggregate: 2 in. nominal maximum size, crushed stone Bulk oven-dry specific gravity = 2.573 Absorption = 0.1% Oven-dry rodded density = 120 pcf Moisture content = 1% Fine aggregate: Natural sand Bulk oven-dry specific gravity = 2.54 Absorption = 0.2% Moisture Content = 3.67% Fineness modulus = 2.68 Find the following requirements: Required Compressive Strength Water-Cement Ratio Coarse Aggregate Requirement Check Aggregate Size Air Content (Use Maximum) Slump (Use Maximum) Water Content Cement Requirement Admixture Fine Aggregate…arrow_forwardDesign the concrete mix according to the following conditions:Design Environment• Concrete slabo Subjected to freeze and thaw.o Required design strength = 21 MPao Slab thickness = 300 mm.o Statistical data indicate a standard deviation of compressive strengthof 1.7 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Available Materials:o Air entrainer:▪ Manufacture specification is 9.5 mL/1% air/100 kg cement.o Coarse aggregate:▪ 25 mm nominal maximum size▪ Crushed stone▪ Bulk oven-dry specific gravity = 2.573▪ Absorption = 2.8▪ Oven-dry rodded density = 1922 kg/m3▪ Moisture content = 1o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.540▪ Absorption = 3.4▪ Moisture content = 4.5▪ Fineness modulus = 2.60o Cement:▪ Type I Cement▪ Specific gravity = 3.15Find the required quantities of cement, water, coarse aggregate, fine aggregate, aircontent, and admixture per 1 m3 of concrete. Summarize the findings in a table.Based on this information, find the…arrow_forward
- Design the concrete mix according to the following conditions:Design Environment• Concrete slabo Subjected to freeze and thaw.o Required design strength = 21 MPao Slab thickness = 300 mm.o Statistical data indicate a standard deviation of compressive strengthof 1.7 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Available Materials:o Air entrainer:▪ Manufacture specification is 9.5 mL/1% air/100 kg cement.o Coarse aggregate:▪ 25 mm nominal maximum size▪ Crushed stone▪ Bulk oven-dry specific gravity = 2.573▪ Absorption = 2.8▪ Oven-dry rodded density = 1922 kg/m3▪ Moisture content = 1o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.540▪ Absorption = 3.4▪ Moisture content = 4.5▪ Fineness modulus = 2.60o Cement:▪ Type I Cement▪ Specific gravity = 3.15…arrow_forwardCompute for the corrected amount of water needed in the concrete mix if the mass of fine and coarse aggregates are 650 kg and 780 kg, and both have an absorption of 1.5% and 2% respectively. Water/cement ratio is 0.50 and the mass of cement is 260kg.arrow_forwardA concrete mix includes the following ingredients per cubic meter: a. Cement = 400 kg b. Water = 176 kg c. No admixture Table P6.30 shows possible changes that can be made to the mix ingredi- ents. Indicate in the appropriate boxes in the table what will happen in each case for the workability and the ultimate compressive strength as increase, decrease, or approximately the same.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Structural Analysis (10th Edition)Civil EngineeringISBN:9780134610672Author:Russell C. HibbelerPublisher:PEARSON
Principles of Foundation Engineering (MindTap Cou...Civil EngineeringISBN:9781337705028Author:Braja M. Das, Nagaratnam SivakuganPublisher:Cengage Learning
Fundamentals of Structural AnalysisCivil EngineeringISBN:9780073398006Author:Kenneth M. Leet Emeritus, Chia-Ming Uang, Joel LanningPublisher:McGraw-Hill Education
Traffic and Highway EngineeringCivil EngineeringISBN:9781305156241Author:Garber, Nicholas J.Publisher:Cengage Learning
Structural Analysis (10th Edition)
Civil Engineering
ISBN:9780134610672
Author:Russell C. Hibbeler
Publisher:PEARSON
Principles of Foundation Engineering (MindTap Cou...
Civil Engineering
ISBN:9781337705028
Author:Braja M. Das, Nagaratnam Sivakugan
Publisher:Cengage Learning
Fundamentals of Structural Analysis
Civil Engineering
ISBN:9780073398006
Author:Kenneth M. Leet Emeritus, Chia-Ming Uang, Joel Lanning
Publisher:McGraw-Hill Education
Traffic and Highway Engineering
Civil Engineering
ISBN:9781305156241
Author:Garber, Nicholas J.
Publisher:Cengage Learning
Aggregates in Concrete Mix Design; Author: Tyler Ley;https://www.youtube.com/watch?v=sNz3kBKKpvw;License: Standard Youtube License