Question
Chapter 3, Problem 3H.12E
(a)
Interpretation Introduction
Interpretation:
Radius of silver has to be determined.
Concept Introduction:
Density of unit cell is as follows:
Here,
(b)
Interpretation Introduction
Interpretation:
Radius of chromium has to be determined.
Concept Introduction:
Refer to part (a).
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Iodine has an orthorhombic unit cell for which the a, b, and c lattice parameters are 0.479, 0.725, and 0.978 nm, respectively. (a) If the atomic packing factor and atomic radius are 0.547 and 0.177 nm, respectively, determine the number of atoms in each unit cell. (b) The atomic weight of iodine is 126.91 g/mol; compute its theoretical density.
NaH crystallizes with the same crystal structure as NaCl. The edge length of the cubic unit cell of NaH is 4.880 Å.(a) Calculate the ionic radius of H−. (The ionic radius of Li+ is 0.0.95 Å.)(b) Calculate the density of NaH.
At room temperature, the edge length of the cubic unit cell in elemental silicon is 5.431 Å, and the density of silicon at the same temperature is 2.328 g cm-3 . Each cubic unit cell contains eight silicon atoms. Using only these facts, perform the following operations.(a) Calculate the volume (in cubic centimeters) of one unit cell.(b) Calculate the mass (in grams) of silicon present in a unit cell.(c) Calculate the mass (in grams) of an atom of silicon.(d) The mass of an atom of silicon is 28.0855 u. Estimate Avogadro’s number to four significant figures.
Chapter 3 Solutions
CHEM PRINCIPLES LL W/ACHIEVE ONE-SEM
Ch. 3 - Prob. 3A.1ASTCh. 3 - Prob. 3A.1BSTCh. 3 - Prob. 3A.2ASTCh. 3 - Prob. 3A.2BSTCh. 3 - Prob. 3A.3ASTCh. 3 - Prob. 3A.3BSTCh. 3 - Prob. 3A.1ECh. 3 - Prob. 3A.2ECh. 3 - Prob. 3A.3ECh. 3 - Prob. 3A.4E
Ch. 3 - Prob. 3A.5ECh. 3 - Prob. 3A.6ECh. 3 - Prob. 3A.7ECh. 3 - Prob. 3A.8ECh. 3 - Prob. 3A.9ECh. 3 - Prob. 3A.10ECh. 3 - Prob. 3B.1ASTCh. 3 - Prob. 3B.1BSTCh. 3 - Prob. 3B.2ASTCh. 3 - Prob. 3B.2BSTCh. 3 - Prob. 3B.3ASTCh. 3 - Prob. 3B.3BSTCh. 3 - Prob. 3B.4ASTCh. 3 - Prob. 3B.4BSTCh. 3 - Prob. 3B.5ASTCh. 3 - Prob. 3B.5BSTCh. 3 - Prob. 3B.6ASTCh. 3 - Prob. 3B.6BSTCh. 3 - Prob. 3B.7ASTCh. 3 - Prob. 3B.7BSTCh. 3 - Prob. 3B.8ASTCh. 3 - Prob. 3B.8BSTCh. 3 - Prob. 3B.1ECh. 3 - Prob. 3B.2ECh. 3 - Prob. 3B.5ECh. 3 - Prob. 3B.6ECh. 3 - Prob. 3B.9ECh. 3 - Prob. 3B.10ECh. 3 - Prob. 3B.11ECh. 3 - Prob. 3B.12ECh. 3 - Prob. 3B.13ECh. 3 - Prob. 3B.14ECh. 3 - Prob. 3B.15ECh. 3 - Prob. 3B.16ECh. 3 - Prob. 3B.17ECh. 3 - Prob. 3B.18ECh. 3 - Prob. 3B.19ECh. 3 - Prob. 3B.20ECh. 3 - Prob. 3B.21ECh. 3 - Prob. 3B.22ECh. 3 - Prob. 3B.23ECh. 3 - Prob. 3B.24ECh. 3 - Prob. 3B.25ECh. 3 - Prob. 3B.26ECh. 3 - Prob. 3B.27ECh. 3 - Prob. 3B.28ECh. 3 - Prob. 3B.29ECh. 3 - Prob. 3B.30ECh. 3 - Prob. 3B.31ECh. 3 - Prob. 3B.32ECh. 3 - Prob. 3B.33ECh. 3 - Prob. 3B.34ECh. 3 - Prob. 3B.35ECh. 3 - Prob. 3B.36ECh. 3 - Prob. 3B.37ECh. 3 - Prob. 3B.38ECh. 3 - Prob. 3B.39ECh. 3 - Prob. 3B.40ECh. 3 - Prob. 3B.41ECh. 3 - Prob. 3B.42ECh. 3 - Prob. 3C.1ASTCh. 3 - Prob. 3C.1BSTCh. 3 - Prob. 3C.2ASTCh. 3 - Prob. 3C.2BSTCh. 3 - Prob. 3C.3ASTCh. 3 - Prob. 3C.3BSTCh. 3 - Prob. 3C.1ECh. 3 - Prob. 3C.2ECh. 3 - Prob. 3C.3ECh. 3 - Prob. 3C.4ECh. 3 - Prob. 3C.5ECh. 3 - Prob. 3C.6ECh. 3 - Prob. 3C.7ECh. 3 - Prob. 3C.8ECh. 3 - Prob. 3C.9ECh. 3 - Prob. 3C.10ECh. 3 - Prob. 3C.11ECh. 3 - Prob. 3C.12ECh. 3 - Prob. 3C.13ECh. 3 - Prob. 3C.14ECh. 3 - Prob. 3C.15ECh. 3 - Prob. 3C.16ECh. 3 - Prob. 3D.1ASTCh. 3 - Prob. 3D.1BSTCh. 3 - Prob. 3D.2ASTCh. 3 - Prob. 3D.2BSTCh. 3 - Prob. 3D.1ECh. 3 - Prob. 3D.2ECh. 3 - Prob. 3D.3ECh. 3 - Prob. 3D.4ECh. 3 - Prob. 3D.5ECh. 3 - Prob. 3D.6ECh. 3 - Prob. 3D.7ECh. 3 - Prob. 3D.8ECh. 3 - Prob. 3D.9ECh. 3 - Prob. 3D.10ECh. 3 - Prob. 3D.11ECh. 3 - Prob. 3D.12ECh. 3 - Prob. 3D.13ECh. 3 - Prob. 3D.14ECh. 3 - Prob. 3D.15ECh. 3 - Prob. 3D.16ECh. 3 - Prob. 3D.17ECh. 3 - Prob. 3D.18ECh. 3 - Prob. 3E.1ASTCh. 3 - Prob. 3E.1BSTCh. 3 - Prob. 3E.1ECh. 3 - Prob. 3E.2ECh. 3 - Prob. 3E.3ECh. 3 - Prob. 3E.4ECh. 3 - Prob. 3E.5ECh. 3 - Prob. 3E.6ECh. 3 - Prob. 3E.7ECh. 3 - Prob. 3E.8ECh. 3 - Prob. 3E.9ECh. 3 - Prob. 3E.10ECh. 3 - Prob. 3E.13ECh. 3 - Prob. 3E.14ECh. 3 - Prob. 3F.1ASTCh. 3 - Prob. 3F.1BSTCh. 3 - Prob. 3F.2ASTCh. 3 - Prob. 3F.2BSTCh. 3 - Prob. 3F.3ASTCh. 3 - Prob. 3F.3BSTCh. 3 - Prob. 3F.1ECh. 3 - Prob. 3F.2ECh. 3 - Prob. 3F.3ECh. 3 - Prob. 3F.4ECh. 3 - Prob. 3F.5ECh. 3 - Prob. 3F.6ECh. 3 - Prob. 3F.7ECh. 3 - Prob. 3F.8ECh. 3 - Prob. 3F.9ECh. 3 - Prob. 3F.10ECh. 3 - Prob. 3F.11ECh. 3 - Prob. 3F.12ECh. 3 - Prob. 3F.13ECh. 3 - Prob. 3F.14ECh. 3 - Prob. 3F.15ECh. 3 - Prob. 3F.16ECh. 3 - Prob. 3F.17ECh. 3 - Prob. 3F.18ECh. 3 - Prob. 3F.19ECh. 3 - Prob. 3F.20ECh. 3 - Prob. 3F.21ECh. 3 - Prob. 3F.22ECh. 3 - Prob. 3G.1ECh. 3 - Prob. 3G.2ECh. 3 - Prob. 3G.3ECh. 3 - Prob. 3G.4ECh. 3 - Prob. 3G.5ECh. 3 - Prob. 3G.6ECh. 3 - Prob. 3G.7ECh. 3 - Prob. 3G.8ECh. 3 - Prob. 3G.9ECh. 3 - Prob. 3G.10ECh. 3 - Prob. 3G.11ECh. 3 - Prob. 3G.12ECh. 3 - Prob. 3G.13ECh. 3 - Prob. 3G.14ECh. 3 - Prob. 3G.15ECh. 3 - Prob. 3G.16ECh. 3 - Prob. 3G.17ECh. 3 - Prob. 3G.18ECh. 3 - Prob. 3H.1ASTCh. 3 - Prob. 3H.1BSTCh. 3 - Prob. 3H.2ASTCh. 3 - Prob. 3H.2BSTCh. 3 - Prob. 3H.3ASTCh. 3 - Prob. 3H.3BSTCh. 3 - Prob. 3H.4ASTCh. 3 - Prob. 3H.4BSTCh. 3 - Prob. 3H.5ASTCh. 3 - Prob. 3H.5BSTCh. 3 - Prob. 3H.1ECh. 3 - Prob. 3H.2ECh. 3 - Prob. 3H.3ECh. 3 - Prob. 3H.4ECh. 3 - Prob. 3H.5ECh. 3 - Prob. 3H.6ECh. 3 - Prob. 3H.7ECh. 3 - Prob. 3H.8ECh. 3 - Prob. 3H.9ECh. 3 - Prob. 3H.10ECh. 3 - Prob. 3H.11ECh. 3 - Prob. 3H.12ECh. 3 - Prob. 3H.13ECh. 3 - Prob. 3H.14ECh. 3 - Prob. 3H.15ECh. 3 - Prob. 3H.16ECh. 3 - Prob. 3H.17ECh. 3 - Prob. 3H.19ECh. 3 - Prob. 3H.20ECh. 3 - Prob. 3H.23ECh. 3 - Prob. 3H.24ECh. 3 - Prob. 3H.25ECh. 3 - Prob. 3H.26ECh. 3 - Prob. 3H.27ECh. 3 - Prob. 3H.28ECh. 3 - Prob. 3H.29ECh. 3 - Prob. 3H.30ECh. 3 - Prob. 3H.31ECh. 3 - Prob. 3H.32ECh. 3 - Prob. 3H.33ECh. 3 - Prob. 3H.34ECh. 3 - Prob. 3H.35ECh. 3 - Prob. 3H.36ECh. 3 - Prob. 3I.1ASTCh. 3 - Prob. 3I.1BSTCh. 3 - Prob. 3I.2ASTCh. 3 - Prob. 3I.2BSTCh. 3 - Prob. 3I.3ASTCh. 3 - Prob. 3I.3BSTCh. 3 - Prob. 3I.4ASTCh. 3 - Prob. 3I.4BSTCh. 3 - Prob. 3I.1ECh. 3 - Prob. 3I.2ECh. 3 - Prob. 3I.3ECh. 3 - Prob. 3I.4ECh. 3 - Prob. 3I.5ECh. 3 - Prob. 3I.6ECh. 3 - Prob. 3I.7ECh. 3 - Prob. 3I.8ECh. 3 - Prob. 3I.11ECh. 3 - Prob. 3I.12ECh. 3 - Prob. 3I.13ECh. 3 - Prob. 3I.14ECh. 3 - Prob. 3I.15ECh. 3 - Prob. 3I.16ECh. 3 - Prob. 3J.1ASTCh. 3 - Prob. 3J.1BSTCh. 3 - Prob. 3J.2ASTCh. 3 - Prob. 3J.2BSTCh. 3 - Prob. 3J.3ASTCh. 3 - Prob. 3J.3BSTCh. 3 - Prob. 3J.1ECh. 3 - Prob. 3J.2ECh. 3 - Prob. 3J.3ECh. 3 - Prob. 3J.4ECh. 3 - Prob. 3J.5ECh. 3 - Prob. 3J.6ECh. 3 - Prob. 3J.7ECh. 3 - Prob. 3J.8ECh. 3 - Prob. 3J.9ECh. 3 - Prob. 3J.10ECh. 3 - Prob. 3J.11ECh. 3 - Prob. 3J.12ECh. 3 - Prob. 3J.13ECh. 3 - Prob. 3J.14ECh. 3 - Prob. 3J.15ECh. 3 - Prob. 3J.16ECh. 3 - Prob. 3.1ECh. 3 - Prob. 3.2ECh. 3 - Prob. 3.3ECh. 3 - Prob. 3.4ECh. 3 - Prob. 3.5ECh. 3 - Prob. 3.6ECh. 3 - Prob. 3.7ECh. 3 - Prob. 3.8ECh. 3 - Prob. 3.9ECh. 3 - Prob. 3.10ECh. 3 - Prob. 3.11ECh. 3 - Prob. 3.12ECh. 3 - Prob. 3.13ECh. 3 - Prob. 3.15ECh. 3 - Prob. 3.18ECh. 3 - Prob. 3.19ECh. 3 - Prob. 3.23ECh. 3 - Prob. 3.24ECh. 3 - Prob. 3.25ECh. 3 - Prob. 3.26ECh. 3 - Prob. 3.27ECh. 3 - Prob. 3.29ECh. 3 - Prob. 3.31ECh. 3 - Prob. 3.32ECh. 3 - Prob. 3.35ECh. 3 - Prob. 3.36ECh. 3 - Prob. 3.37ECh. 3 - Prob. 3.38ECh. 3 - Prob. 3.40ECh. 3 - Prob. 3.41ECh. 3 - Prob. 3.42ECh. 3 - Prob. 3.45ECh. 3 - Prob. 3.47ECh. 3 - Prob. 3.49ECh. 3 - Prob. 3.50ECh. 3 - Prob. 3.51ECh. 3 - Prob. 3.53ECh. 3 - Prob. 3.54ECh. 3 - Prob. 3.55ECh. 3 - Prob. 3.56ECh. 3 - Prob. 3.57ECh. 3 - Prob. 3.58ECh. 3 - Prob. 3.59ECh. 3 - Prob. 3.60ECh. 3 - Prob. 3.61ECh. 3 - Prob. 3.62ECh. 3 - Prob. 3.63ECh. 3 - Prob. 3.64ECh. 3 - Prob. 3.65ECh. 3 - Prob. 3.66ECh. 3 - Prob. 3.67ECh. 3 - Prob. 3.68E
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, chemistry and related others by exploring similar questions and additional content below.Similar questions
- A metal crystallizes in the face-centered cubic crystal structure with a unit cell edge of 3.52 x 10 -8 cm.The density of the metal is 8.90 g/cc. (a) What is the mass, in grams, of a single atom of this element? (b) What is the atomic weight of the element (g/mol). (c) What is the radius, in cm, of an atom of the element?arrow_forwardTitanium carbide, TiC, adopts the rock-salt (NaCl) crystal structure. (i) Draw the unit cell indicating clearly the position of all atoms.(ii) The unit cell parameter for TiC is 0.4329 nm. Calculate the C-Cdistance, the Ti-C bond length and the Ti-Ti distance.arrow_forward1.Indium has a tetragonal unit cell for which the a and c lattice parameters are 0.459 and 0.495 nm, respectively. (a) If the atomic packing factor and atomic radius are 0.693 and 0.1625 nm, respectively, determine the number of atoms in each unit cell. (b) The atomic weight of indium is 114.82 g/mol; compute its theoretical density.arrow_forward
- Account for the following :(a) Glass objects from ancient civilizations are found to become milky in appearance.(b) Window glass panes of old buildings are thicker at the bottom than at the top.arrow_forward1) Palladium (electron configuration is [Kr]4d¹) crystallizes in a face-centered cubic unit cell. its density is 12.0 g/cm³. (NA = 6.02 x 10²³) (a) What is the total mass of palladium atoms contained within one unit cell? (b) Calculate the atomic radius (r) of Pd.arrow_forward(3) The unit cell length of NaCl is 5.63 Å. Determine the density of NaCl.arrow_forward
- Gallium has an orthorhombic structure, with a0 = 0.45258 nm, b0 = 0.45186 nm, and c0 = 0.76570 nm. The atomic radius is 0.1218 nm. The density is 5.904 g cm3, and the atomic weight is 69.72 g mol. Determine (a) the number of atoms in each unit cell; and (b) the packing factor in the unit cell.arrow_forwardAt room temperature, monoclinic sulfur has the unit-cell dimensions a = 11.04 Å, b = 10.98 Å, c = 10.92 Å, and B = 96.73°. Each cell contains 48 atoms of sulfur. (a) Explain why it is not necessary to give the values of the angles a and y in this cell. (b) Compute the density of monoclinic sulfur (in g cm¯³).arrow_forward(b) Many structures of ionic compounds have been described in terms of close packing of a large anion, X, with a cation, A, occupying tetrahedral or octahedral holes. (1) In a cubic close packed lattice, how many octahedral holes are there per lattice ion? (ii) What is the formula of a compound based upon a cubic close packed lattice in which of the octahedral holes are filled? (ii) State the coordination numbers and geometries of A and X In the crystal lattice in part (b)(ii) above.arrow_forward
- (a) Pure iron has a change in crystal structure from BCC to FCC when heating up above 912°C. If the atomic radius of an Fe atom is 0.124 nm, calculate the volumes of the FCC and BCC unit cells. (b)Recall that there are two atoms per BCC unit cell, and four atoms per FCC unit cell. With this information in mind, calculate the percent change in volume of a sample of pure Fe as it transforms from an FCC to a BCC structure upon cooling below 912°C. Specify if this percent change manifests as an increase or decrease in volume of the sample.arrow_forwardWhich type of intermolecular force accounts for each of these differences? (a) CH3OH boils at 65 °C; CH3SH boils at 6 °C. (b) Xe is a liquid at atmospheric pressure and 120 K, whereas Ar is a gas under the same conditions. (c) Kr, atomic weight 84 amu, boils at 120.9 K, whereas Cl2, molecular weight about 71 amu, boils at 238 K. (d) Acetone boils at 56 °C, whereas 2-methylpropane boils at -12 °C. CH3 CH3 O C CH3 CH3 CH3 CH Acetone 2-Methylpropanearrow_forward(a)What is the atomic radius (in nm) of a certain metal particle if it crystallizes with a face-centered cubic unit ceno.38 nm on an edge?(b) What will be its theoretical density if it has an atomic weight of 88.9 g/molarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Chemistry: The Molecular ScienceChemistryISBN:9781285199047Author:John W. Moore, Conrad L. StanitskiPublisher:Cengage Learning
Chemistry: The Molecular Science
Chemistry
ISBN:9781285199047
Author:John W. Moore, Conrad L. Stanitski
Publisher:Cengage Learning
Unit Cell Chemistry Simple Cubic, Body Centered Cubic, Face Centered Cubic Crystal Lattice Structu; Author: The Organic Chemistry Tutor;https://www.youtube.com/watch?v=HCWwRh5CXYU;License: Standard YouTube License, CC-BY