Chapter 4, Problem 4.10QP
An aluminum alloy cylinder with a diameter of 3 in. and a height of 6 in. is subjected to a compressive load of 50,000 pounds. Assume that the material is within the elastic region and a modulus of elasticity of 11 × 106 psi.
a. What will be the lateral strain if Poisson’s ratio is 0.33?
b. What will be the diameter after load application?
c. What will be the height after load application?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
An aluminum alloy cylinder with a diameter of 3 in. and a height of 6 in. is subjected to a compressive load of 50,000 pounds. Assume that the material is within the elastic region and a modulus of elasticity of 11 * 106 psi. a. What will be the lateral strain if Poisson’s ratio is 0.33? b. What will be the diameter after load application? c. What will be the height after load application?
An aluminum alloy cylinder with a diameter of 76 mm and a height of150 mm. is subjected to a compressive load of 220 kN. Assume that the material is within the elastic region and a modulus of elasticity of 75 GPa.a. What will be the lateral strain if Poisson’s ratio is 0.33?b. What will be the diameter after load application?c. What will be the height after load application?
A wood beam is strengthened using two steel plates as shown in the figure below.
*Inserted Photo*
The beam has simple supports and an overhang and is subjected to a point load and a uniform load as shown in the figure below.
Calculate the maximum tensile and compressive stresses of the beam. Assume that Ew = 11 GPa and Es = 200 GPa. (Enter your answers in MPa. Use the deformation sign convention.)
maximum tensile stress in wood ? MPa
maximum tensile stress in steel ? MPa
maximum compressive stress in wood ? MPa
maximum compressive stress in steel ? MPa
Chapter 4 Solutions
Materials for Civil and Construction Engineers (2nd Edition)
Ch. 4 - Name the two primary factors that make aluminum an...Ch. 4 - Prob. 4.2QPCh. 4 - An aluminum alloy specimen with a radius of 0.28...Ch. 4 - An aluminum alloy bar with a radius of 7 mm was...Ch. 4 - Decode the characteristics of a 6063 T831...Ch. 4 - A round aluminum alloy bar with a 0.6 in. diameter...Ch. 4 - An aluminum alloy bar with a rectangular cross...Ch. 4 - A round aluminum alloy bar with a 0.25-in....Ch. 4 - An aluminum alloy rod has a circular cross section...Ch. 4 - An aluminum alloy cylinder with a diameter of 3...
Ch. 4 - A 3003-H14 aluminum alloy rod with 0.5 in....Ch. 4 - The stressstrain relation of an aluminum alloy bar...Ch. 4 - An aluminum specimen originally 300 mm long is...Ch. 4 - A tension stress of 40 ksi was applied on a 12-in....Ch. 4 - A tension test was performed on an aluminum alloy...Ch. 4 - In Problem 4.15, plot the stressstrain...Ch. 4 - Referring to Figure 4.5, determine approximate...Ch. 4 - Prob. 4.18QPCh. 4 - A tensile stress is applied along the long axis of...Ch. 4 - A cylindrical aluminum alloy rod with a 0.5 in....Ch. 4 - Prob. 4.21QPCh. 4 - Discuss galvanic corrosion of aluminum. How can...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.arrow_forwardA tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.arrow_forwardThe results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.arrow_forward
- Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.arrow_forwardAccording to Figure 5-20, is ii possible to completely separate one of the four materials from the other three? Explain your answer.arrow_forwardA cylindrical specimen of stainless steel having an initial diameter of 12.8?? and initial length of 50.8?? is pulled in tension. Use the data provided below to a) Plot the data as engineering stress versus engineering strain using excel or similar software. b) Compute the modulus of elasticity. c) Determine the yield strength at a strain offset of 0.002. d) Determine the tensile strength of this alloy. e) What is the approximate ductility, in percent elongation? f) Compute the modulus of resilience. Load (?) Length (??) 0 50.800 12,700 50.825 25,400 50.851 38,100 50.876 50,800 50.902 76,200 50.952 89,100 51.003 92,700 51.054 102,500 51.181 107,800 51.308 119,400 51.562 128,300 51.816 149,700 52.832 159,000 53.848 160,400 54.356 159,500 54.864 151,500 55.880 124,700 56.642 Fracturearrow_forward
- A compressive load of 50 KN is applied 150 on the axis of a steel-round bar of 8 mm diameter. Compute its stress and strain if the given modulus of elasticity is 75 GPa. Please draw a figure.arrow_forwardA composite column is formed by placing a steel bar 20 mm diameter and 200 mm long, inside an alloy cylinder of the same length whose internal and external diameters are 20 mm and 25 mm respectively. The column is then subjected to an axial load of 50 kN. Modulus of elasticity for steel and alloy is 200000MPa and 70000MPa respectively. Which of the following gives the stress in the steel bar? a. 132.98 MPa b. 46.54 MPa c. 74.80 MPa d. 166.23 MPaarrow_forwardQuestion 1: A 25mm diameter aluminum rod is loaded axially in tension with a load of 100kN. The rod is 4 m in length. Aluminum has a modulus of elasticity of 69GPa and a Poisson’s ratio of 0.35. 1) What is the decrease in diameter of the rod due to the applied load? 2) What is the new length of the rod?arrow_forward
- Consider a rectangular specimen of aluminium has a dimension of 10 ?? × 12.7 ?? is pulled in tension with 35500 N. Calculate the resulting strain. Given the modulus of elasticity is 69 × 103??? and assume that the deformation is elastic.arrow_forwardA steel pipe having a length of 3 ft, an outside diameter of 5 in., and a wall thickness of 1/2 in. is subjected to an axial compression of 50,000 lb. Assuming a modulus of elasticity of 30 * 106 psi and a Poisson’s ratio of 0.27, finda. the shortening of the pipe,b. the increase in the outside diameter, andc. the increase in the wall thickness.arrow_forwardA cylindrical rod of steel (E = 207 GPa),4mm in diameter is to be deformed by atensile force. Determine the force (in N)that will produce an elastic reduction of2.5 x 10-3mm in diameter if Poisson’sratio is 0.30. Show complete solution and formulas used.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Steel Design (Activate Learning with these NEW ti...Civil EngineeringISBN:9781337094740Author:Segui, William T.Publisher:Cengage Learning
Solid Waste EngineeringCivil EngineeringISBN:9781305635203Author:Worrell, William A.Publisher:Cengage Learning,
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
Steel Design (Activate Learning with these NEW ti...
Civil Engineering
ISBN:9781337094740
Author:Segui, William T.
Publisher:Cengage Learning
Solid Waste Engineering
Civil Engineering
ISBN:9781305635203
Author:Worrell, William A.
Publisher:Cengage Learning,
How Cast Iron Pans Are Made — How to Make It; Author: Eater;https://www.youtube.com/watch?v=aIBt0uFwjY8;License: Standard Youtube License