Materials for Civil and Construction Engineers (4th Edition)
4th Edition
ISBN: 9780134320533
Author: Michael S. Mamlouk, John P. Zaniewski
Publisher: PEARSON
expand_more
expand_more
format_list_bulleted
Videos
Textbook Question
Chapter 3, Problem 3.29QP
A cylindrical steel alloy rod with a 0.5 in. diameter is subjected to tension. Determine the magnitude of the load required to produce a 10-4 in. change in diameter if the deformation is entirely elastic. Assume a Young’s modulus of 30 × 106 psi and a Poisson's ratio of 0.27.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A closed right circular cylinder has radius 2 units and height 17 units A load of an unknown weight is put on top of the cylinder, causing the cylinder to shorten by 1.1 units. Find the new volume of cylinder due to this deformation in the height of the cylinder.
A 10.0 mm diameter cylindrical specimen of a bearing bronze material is pulled under uniaxial tension with a force of 1500 N. The diameter of the bar reduces by 0.67 mm. Compute the modulus of elasticity for this material given that it’s Poisson’s ratio,n, is 0.35.
Steel cylinder has 200 mm mean diameter with a wall 1 mm thick and 310 mm long.
Determine the circumferential and longitudinal stresses that occur on the cylinder if the maximum pressure difference allowed between the inside and outside must not exceed 100 MPa.
Determine the effects of three dimensional loading by determine volumetric strain and change in volume for the first steel cylinder.
Modulus of elasticity E= (210 GPa),
Poisson's ratio 0.30.
7
Chapter 3 Solutions
Materials for Civil and Construction Engineers (4th Edition)
Ch. 3 - What is the chemical composition of steel? What is...Ch. 3 - Why does the ironcarbon phase diagram go only to...Ch. 3 - Draw a simple ironcarbon phase diagram showing the...Ch. 3 - What is the typical maximum percent of carbon in...Ch. 3 - Calculate the amounts and compositions of phases...Ch. 3 - Briefly discuss four heat treatment methods to...Ch. 3 - Define alloy steels. Explain why alloys are added...Ch. 3 - Prob. 3.8QPCh. 3 - Specifically state the shape and size of the...Ch. 3 - What are the typical uses of structural steel?
Ch. 3 - What is the range of thicknesses of cold-formed...Ch. 3 - Why is coil steel used for cold-formed steel...Ch. 3 - If a steel with a 33 ksi yield strength is used...Ch. 3 - Why is reinforcing steel used in concrete? Discuss...Ch. 3 - What is high-performance steel? State two HPS...Ch. 3 - Name three mechanical tests used to measure...Ch. 3 - The following laboratory tests are performed on...Ch. 3 - Sketch the stress-strain behavior of steel, and...Ch. 3 - Three steel bars with a diameter of 25 mm and...Ch. 3 - Three steel bars with a diameter of 0.5 in. and...Ch. 3 - Draw a typical stressstrain relationship for steel...Ch. 3 - Getting measurements from Figure 3.18, determine...Ch. 3 - A steel specimen is tested in tension. The...Ch. 3 - A steel specimen is tested in tension. The...Ch. 3 - A No. 10 steel rebar is tested in tension. By...Ch. 3 - A mild steel specimen originally 300 mm long is...Ch. 3 - A tension stress of 70 ksi was applied on a 12-in....Ch. 3 - A tensile stress is applied along the long axis of...Ch. 3 - A cylindrical steel alloy rod with a 0.5 in....Ch. 3 - A round steel alloy bar with a diameter of 0.75...Ch. 3 - A 19-mm reinforcing steel bar and a gauge length...Ch. 3 - Testing a round steel alloy bar with a diameter of...Ch. 3 - During the tension test on a steel rod within the...Ch. 3 - A grade 36 round steel bar with a diameter of 0.5...Ch. 3 - A high-yield-strength alloy steel bar with a...Ch. 3 - Estimate the cross-sectional area of a 350S125-27...Ch. 3 - An ASTM A615 grade 60 number 10 rebar with a gauge...Ch. 3 - A 32-mm rebar with a gauge length of 200 mm was...Ch. 3 - A steel pipe having a length of 3 ft. an outside...Ch. 3 - A steel pipe having a length of 1 m, an outside...Ch. 3 - A drill rod with a diameter of 10 mm is made of...Ch. 3 - A drill rod with, a diameter of 1/2 in. is made of...Ch. 3 - Prob. 3.43QPCh. 3 - An engineering technician performed a tension test...Ch. 3 - A Charpy V Notch (CVN) test was performed on a...Ch. 3 - Prob. 3.46QPCh. 3 - Prob. 3.47QPCh. 3 - How can the flaws in steel and welds be detected?...Ch. 3 - Determine the welding zone classification of A36...Ch. 3 - Briefly define steel corrosion. What are the four...Ch. 3 - Discuss the main methods used to protect steel...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.arrow_forwardThe data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.arrow_forwardThe results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.arrow_forward
- A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.arrow_forwardAccording to Figure 5-20, is ii possible to completely separate one of the four materials from the other three? Explain your answer.arrow_forwardA 2-m long steel rod, 10-mm in diameter, is carrying a load of 20 kN. (a) what is the axial stress developed in the rod, in kN/m^2. Is the tensile or compressive? (b) compute the amount of elongation (in mm) in the steel rod caused by the applied load, (c) what will be the elongation (in mm) in the steel rod if the weight of the steel rod is included? Use density of the steel to be 7860 kg/m^3. Young's modulus of elasticity, E=200GPa. W=mg. Draw free body diagram of the steel rod.arrow_forward
- A tensile stress is applied along the long axis of a cylindrical steel rod with adiameter of 10 mm. If the deformation is entirely elastic, determine the magnitude of the load required to produce a 5 X 10-3 mm change in diameter. Assume a modulus of elasticity of 200 GPa and a Poisson’s ratio of 0.27.arrow_forwardA tensile stress is applied along the long axis of a cylindrical steel rod with a diameter of 10 mm. If the deformation is entirely elastic, determine the magnitude of the load required to produce a 5 * 10-3 mm change in diameter.Assume a modulus of elasticity of 200 GPa and a Poisson’s ratio of 0.27.arrow_forwardIf a steel column with cross-sectional area A = 1000 mm^2 modulus of elasticity E = 200 MPa and length of 10 m is subjected to 2 kN axial tension, compute for its axial deformationarrow_forward
- A compound bar consisting of bronze, aluminum, and steel segments is loaded axially as shown in the figure. Determine the maximum allowable value P if the change in length of the bar is limited to 2 mm and the working stresses prescribed in the table are not to be exceededarrow_forwardCalculate the plane stresses involved where two pieces of steel are welded together. Our sign convention defines forces causing the object to be in tension positive and forces causing the object to be in compression negative. As we can see from the picture our σx = −4.5MPa and σy = 10MPa. Steel has an average Young’s modulus of elasticity of E = 200 GPa and an average Poisson’s ratio of ν = .285 Because it is not defined we will assume that initially there is no shear stress, τxy = 0. Solve only for: Compression in the x-direction(deformation along the weld)=(-Blank 4)? x 10^-5arrow_forward
arrow_back_ios
arrow_forward_ios
Recommended textbooks for you
Steel Design (Activate Learning with these NEW ti...Civil EngineeringISBN:9781337094740Author:Segui, William T.Publisher:Cengage Learning
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Solid Waste EngineeringCivil EngineeringISBN:9781305635203Author:Worrell, William A.Publisher:Cengage Learning,
Principles of Foundation Engineering (MindTap Cou...Civil EngineeringISBN:9781337705028Author:Braja M. Das, Nagaratnam SivakuganPublisher:Cengage Learning
Steel Design (Activate Learning with these NEW ti...
Civil Engineering
ISBN:9781337094740
Author:Segui, William T.
Publisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
Solid Waste Engineering
Civil Engineering
ISBN:9781305635203
Author:Worrell, William A.
Publisher:Cengage Learning,
Principles of Foundation Engineering (MindTap Cou...
Civil Engineering
ISBN:9781337705028
Author:Braja M. Das, Nagaratnam Sivakugan
Publisher:Cengage Learning
The History of Iron and Steel; Author: Real Engineering;https://www.youtube.com/watch?v=7E__zqy6xcw;License: Standard Youtube License