Minority carriers (holes) are injected into a homogeneous n-type semiconductor sample at one point. An electric field of 50 V/em is applied across the sample, and the field moves these minority carriers a distance of 1 cm in 100 us. The diffusivity of the minority carriers [sm/ ] at 300 K i 5.3 Option 5 51.8 5.81 5.18

Minority carriers (holes) are injected into a homogeneous n-type semiconductor sample at one point. An electric field of 50 V/em is applied across the sample, and the field moves these minority carriers a distance of 1 cm in 100 us. The diffusivity of the minority carriers [sm/ ] at 300 K i 5.3 Option 5 51.8 5.81 5.18

Delmar's Standard Textbook Of Electricity

7th Edition

ISBN:9781337900348

Author:Stephen L. Herman

Publisher:Stephen L. Herman

Chapter30: Dc Motors

Section: Chapter Questions

Problem 6RQ: What is CEMF?

See similar textbooks

Similar questions

Boron gas is used to dope the silicon wafer to a dopant concentration of 10¹6 / cm³. After letting the sample cooldown to 300K (a) What is the new number of free electrons and holes in equilibrium? (b) What type of semiconductor do we have after the process?
Assume D = D0e^–Ea/kT is the diffusion coefficient of boron in silicon surface, whereD0 = 10.5 cm^2/s and Ea = 3.7 eV. The substrate is N-type silicon doped to 10^15 cm^3.N0 = 10^15 cm^2 of boron is introduced just below the silicon surface.(a) What is the junction depth after a 1-h drive-in at 1,100°C?(b) By how much will the junction depth change after 10^6 h (~100 years) of operation at100°C
Hall measurement is conducted on a silicon sample of unknown doping with W= 100cm, A = 2.5 × 10-3cm2, I = 2 mA and the magnetic field is 500 Gauss. If the Hall voltage of +150mV is measured, find the Hall coefficient, conductivity type, majority carrier concentration, resistivity and mobility of the semiconductor sample.
Estimate the amount of free electrons and holes in a N-doped Silicon wafer a) at room temperature with 1014 cm-3 doping level, and b) at 650K with 1015 cm-3 doping level
(a) Calculate the indium content of an InGaAs ternary compound semiconductor using a linear approximation, which would have a bandgap of 1.155 eV knowing that a bandgap (EG InAs) of InAs is 0.354 eV and a bandgap (EG GaAs) of GaAs is 1.424 eV. (b) Calculate the effective electron mass of the InGaAs ternary compound semiconductor using a linear approximation with an indium content from question (a). Use a relative electron effective mass of InAs of 0.031 and of GaAs of 0.0665.
An n-type semiconductor with direct band structure (Eg = 2.5 eV) is applied with a DC voltage shown below. (i) Schematically draw the band diagram for this semiconductor under this DC voltage. (ii) Calculate the longest wavelength in light absorption from this n-type semiconductor with applied DC voltage.
Calculate the drift current density in a semiconductor for a given electric field.Consider a germanium sample at T = 300°K with doping concentration of Nd = 0 and Na= 1016 cm-3. Assume complete ionization and electron and hole mobilities are 3900 cm2/V⋅sec and 1900 cm2/V⋅sec. The applied electric field is E = 50 V/cm
A silicon diode is in connected to a DC voltage source with Forward biased, the net currentflowing through the diode is (25mA) where the applied voltage across the terminals of thediode is (820mV). Determine diode temperature, if Is "dark saturation current", the diodeleakage current density in the absence of light is 3.4 × 10−10 A
3. at ??? = 10mA. Determine also the diode dynamic resistance at ??? = 10mA, and compare it with the theoretical value obtained from the equation
The linear electron and hole concentration profiles in a 4 um wide region of silicon material is shown in the figure below. The silicon material is subjected to electron injection from the left and hole injection from the right as shown in the figure. Assume that the cross-sectional area of the material ?=1 ??2, electron mobility ??=1312.75 ??2/? ?, and hole mobility ??=463.33 ??2/? ?. Find the total current (to one decimal place) flowing through the material. ?=300?, ?=1.6×10−19 ?, ?=8.62×10−5 ??/?, ?=1.38×10−23 ?/?, and 1 ??=1.6×10−19 ?. Explain how depletion and diffusion capacitances differ
what is the schemtic diagram of TP4056 and Li-ion battery when they connect to each other. The picture given below
A drift current density of 120A/cm2is established in n-type silicon with an applied electric field of 18V/cm. If the electron and hole mobilities are µn =1250 cm2/V-s and µp =450 cm2/V-s, respectively, determine the required doping concentration