Question
Chapter 5, Problem 5.61P
(a)
To determine
The carbon content at 0.05cm beneath the surface.
(b)
To determine
The carbon content at 0.05 beneath the surface.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. Determine the amount of pure iron or pure carbon we need to add to this 1000 gram alloy if we need to have 100% pearlite at 720C upon slow cooling from complete melt.
For alloy of two hypothetical metals A and B, there exist an a, A-rich phase and a
B, B-rich phase. For alloys of two different overall compositions at 25°C, the weight fractions of Wa and
WB are listed in the table. Determine the solubility limits for both a and B phases at 25°C.
Alloy Composition
Wa
WB
70wt% A-30wt% B
0.78
0.22
35wt% A-65wt% B
0.36
0.64
Determine the activation energy for vacancy formation in aluminum, if theequilibrium number of vacancies at 500 °C is 7.57 × 1023 m-3. Given that theatomic weight and density for aluminum are 26.98 g/mol and2.62 g/cm3, respectively.
Chapter 5 Solutions
The Science and Engineering of Materials (MindTap Course List)
Ch. 5 - What is the driving force for diffusion?Ch. 5 - Give three examples of materials processes that...Ch. 5 - In the carburization treatment of steels, what are...Ch. 5 - Prob. 5.4PCh. 5 - Prob. 5.5PCh. 5 - Prob. 5.6PCh. 5 - Prob. 5.7PCh. 5 - A certain mechanical component is heat treated...Ch. 5 - Prob. 5.9PCh. 5 - Prob. 5.10P
Ch. 5 - Prob. 5.11PCh. 5 - Prob. 5.12PCh. 5 - Prob. 5.13PCh. 5 - Prob. 5.14PCh. 5 - Prob. 5.15PCh. 5 - Prob. 5.16PCh. 5 - Compare the diffusion coefficients of carb on in...Ch. 5 - Prob. 5.18PCh. 5 - Activation energy is sometimes expressed as...Ch. 5 - Prob. 5.20PCh. 5 - The activation energy for the diffusion of copper...Ch. 5 - Prob. 5.22PCh. 5 - Prob. 5.23PCh. 5 - Prob. 5.24PCh. 5 - Prob. 5.25PCh. 5 - Write down Fick’s first law of diffusion. Clearly...Ch. 5 - Prob. 5.27PCh. 5 - Prob. 5.28PCh. 5 - Prob. 5.29PCh. 5 - Prob. 5.30PCh. 5 - A 1-mm-thick BCC iron foil is used to separate a...Ch. 5 - Prob. 5.32PCh. 5 - Prob. 5.33PCh. 5 - A 0.001 in. BCC iron foil is used to separate a...Ch. 5 - Prob. 5.35PCh. 5 - Prob. 5.36PCh. 5 - Prob. 5.37PCh. 5 - Prob. 5.38PCh. 5 - Prob. 5.39PCh. 5 - Prob. 5.40PCh. 5 - Prob. 5.41PCh. 5 - Prob. 5.42PCh. 5 - Prob. 5.43PCh. 5 - Prob. 5.44PCh. 5 - Prob. 5.45PCh. 5 - Prob. 5.46PCh. 5 - Prob. 5.47PCh. 5 - Prob. 5.48PCh. 5 - Pure zinc is to be diffused into copper by dipping...Ch. 5 - Nitriding is a process in which nitrogen is...Ch. 5 - Determine the carburizing time necessary to...Ch. 5 - Prob. 5.52PCh. 5 - Prob. 5.53PCh. 5 - Prob. 5.54PCh. 5 - Prob. 5.55PCh. 5 - Prob. 5.56PCh. 5 - Prob. 5.57PCh. 5 - Prob. 5.58PCh. 5 - Compare the rate at which oxygen ions diffuse in...Ch. 5 - Prob. 5.60PCh. 5 - Prob. 5.61PCh. 5 - Prob. 5.62PCh. 5 - Prob. 5.63PCh. 5 - Prob. 5.64PCh. 5 - Prob. 5.65PCh. 5 - A 0.80% C steel must operate at 950°C in an...Ch. 5 - Prob. 5.67PCh. 5 - Prob. 5.68PCh. 5 - Prob. 5.69PCh. 5 - Prob. 5.70PCh. 5 - Prob. 5.71PCh. 5 - Prob. 5.72PCh. 5 - Most metals and alloys can be processed using the...Ch. 5 - Prob. 5.74PCh. 5 - Prob. 5.75PCh. 5 - Prob. 5.76PCh. 5 - A ceramic part made from MgO is sintered...Ch. 5 - Prob. 5.78PCh. 5 - What are the advantages of using hot pressing and...Ch. 5 - Prob. 5.80PCh. 5 - Prob. 5.81DPCh. 5 - Design a spherical tank, with a will thickness of...Ch. 5 - Prob. 5.83DPCh. 5 - Prob. 5.84DPCh. 5 - Prob. 5.85DPCh. 5 - Prob. 5.86CPCh. 5 - Prob. 5.87CPCh. 5 - Prob. 5.88CPCh. 5 - Prob. 5.1KP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A 0.015M solution of hydrogen cyanate ,HOCN has a pH of 2.67arrow_forwardMetal A (Tm=860 oC) and metal B (Tm=620 oC) were fully dissolved in each other in the liquid state. The ultimate solubility of B in A is 12% at 460 oC which decreasing with decreasing temperature to 3% at room temperature while the maximum solubility of A in B is 7% at 460 oC still constant to room temperature. A and B form eutectic at 460 oC and 48 % of B. construct phase diagram for A-B alloying system, label all phases and temperatures, and answer the following: a) 28 wt % A alloy is slowly cooled from 720 oC at what temperature does the first solid phase is formed? What is the composition of this solid phase? For this alloy what is the mass fraction of the phases at, 600 oC, 300 oC ,and TR? c) What is the ?composition of the phases in (b)arrow_forward•You are case-hardening a tool made of BCC (α) iron in the presence of a carbonaceous material. A heat treatment at 600 oC for 100 minutes results in a carbon concentration of 0.75 wt% at a position 0.5mm below the surface. How long would it take to obtain the same concentration at the same position if the heat treatment were conducted at 900 oC? x12/D1t1= x22/D2t2 Arrhenius equation: D=D0e^(〖-Qd〗∕RT) Qd = Activation energy of diffusion D0 = Pre-exponential diffusion factor R = gas constant = 8.314 J/(mol*K) Use the Arrhenius equation to calculate D1 and D2. Calculate the time to satisfy the problem statement.arrow_forward
- A 50%Ni-50%Cu alloy is slowly cooled from 1400°C to 1200°C. Determine: At 1300°C, estimate the weight fractions of the solid and liquid.arrow_forwardFor a Fe-2.5 %C alloy , what is the temperature at which the first liquid forms on heating and also give the composition of the liquid at that temperaturearrow_forwardA 1020 steel contains 0.20% carbon is carburized by a source that maintains a surface carbon content 0f 2.0% C. It is desired to produce a 0.80 wt% C concentration 0.1 cm below the steel surface after a 4-hour treatment. At what temperature should the carburization be carried out? R = 8.314 J/mol•K; DO = 2.3x10-5 m2 /s; Qd=148,000 J/mol erf(z) erf(z) erf(z) 0.55 0.5633 1.3 0.9340 0.025 0.05 0.0282 0.60 0.6039 1.4 0.9523 0.0564 0.65 0.6420 1.5 0.9661 0.10 0.1125 0.70 0.6778 1.6 0.9763 0.15 0.1680 0.75 0.7112 1.7 0.9838 0.20 0.25 0.30 0.2227 0.80 0.7421 1.8 0.9891 0.2763 0.85 0.7707 1.9 0.9928 0.3286 0.90 0.7970 2.0 0.9953 0.35 0.3794 0.95 0.8209 2.2 0.9981 0.40 0.4284 1.0 0.8427 2.4 0.9993 0.45 0.4755 1.1 0.8802 2.6 0.9998 0.50 0.5205 1.2 0.9103 2.8 0.9999arrow_forward
- 1. For some hypothetical metal the equilibrium number of vacancies at 750°C is 2.8×1024?−3. If the density and atomic weight of this metal are 5.60 ? ??3⁄ and 65.6 ?/???, respectively, calculate the fraction of vacancies for this metal at 750°C. 2. Calculate the number of vacancies per cubic meter in iron at 850°C. The energy for vacancy formation is 1.08 eV/atom. The density and atomic weight for Fe are 7.65 g/cm3 and 55.85 g/mol, respectively. Answer both pleasearrow_forwardDuring freezing of a Cu-Zn alloy, we find that the composition is non-uniform. By heating the alloy to 600°C for 3 hours, diffusion of zinc helps to make the composition more uniform. What temperature would be required if we wished to perform this homogenization treatment in 30 minutes?arrow_forwardDetermine the carburizing time necessary to achieve a carbon concentration of 0.50 wt% at a position 3.1 mm into an iron-carbon alloy that initially contains 0.12 wt% C. The surface concentration is to be maintained at 1.2 wt% C, and the treatment is to be conducted at 1080°C. Assume that Do = 5.8 x 10-5 m²/s and Qd = 156 kJ/mol. The table Tabulation Error Function Values may be useful.arrow_forward
- For alloys of two hypothetical metals A and B, there exists an a, A-rich phase and a b, B-rich phase. From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine the composition of the phase boundary (or solubility limit) for the following: Alloy composition Fraction a Phase Fraction b Phase 60wt%A-40wt%B 0.60 0.40 30wt%A-70wt%B 0.12 0.88 a) a Phase = ___________ wt%A b) b Phase = ___________ wt%Aarrow_forwardGiven that a component is made of 0.1 wt.%C steel is carburized by introducing 1.0 wt.% carbon at its surface at 980ºC. Calculate the carbon content at 0.5 mm below the surface of this component after 1 hour.Do= 0.2 cm^2/s and Qd=40,000 cal/mol.arrow_forwardCalculate the concentration of monovacancies in gold at 1,000 K, knowingthat Hf = 1.4 × 10−19 J. If the gold is suddenly quenched to ambienttemperature, what will be the excess vacancy concentration?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Introduction to Diffusion in Solids; Author: Engineering and Design Solutions;https://www.youtube.com/watch?v=K_1QmKJvNjc;License: Standard youtube license